- 密度 [g/cm3]: 0.97
- 拉伸强度 [MPa]: 34.5
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.970 g/cc | 0.0350 lb/in³ | ASTM D1475 | ||
| Solids Content | 37.5 % | 37.5 % | by volume; ASTM D2369 Modified | ||
| 43.7 % | 43.7 % | by weight; ASTM D2369 Modified | |||
| Volatile Organic Compounds (VOC) Content | 546 g/l | 546 g/l | ASTM D3960 | ||
| Brookfield Viscosity | 450 cP | 450 cP | ASTM D2196, LVT, Spindle #2 @ 30rpm | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 34.5 MPa | 5000 psi | Coatings catalyzed 2% with 9995, baked 15 minutes @ 107ºC, post cured 2 weeks @ 25ºC and 50% relative humidity. Free films tested on an Instron tester | ||
| Elongation at Yield | 400 % | 400 % | Coatings catalyzed 2% with 9995, baked 15 minutes @ 107ºC, post cured 2 weeks @ 25ºC and 50% relative humidity. Free films tested on an Instron tester | ||
| Thermal Properties | Metric | English | Comments | ||
| Flash Point | 23.0 °C | 73.4 °F | ASTM D3278, Seta Flash, Closed Cup | ||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 1.00 - 4.00 min @Temperature 149 - 191 °C | 0.0167 - 0.0667 hour @Temperature 300 - 376 °F | |||
| 2.00 - 5.00 min @Temperature 121 - 149 °C | 0.0333 - 0.0833 hour @Temperature 250 - 300 °F | ||||
| 10.0 - 30.0 min @Temperature 93.0 - 121 °C | 0.167 - 0.500 hour @Temperature 199 - 250 °F | ||||
| Descriptive Properties | |||||
| Appearance | Black | ||||
| Theoretical Coverage (ft²/gallon/mil) | 600 | ||||