- 缺口冲击强度: 4.3
- 拉伸强度 [MPa]: 66.0
- 断裂伸长率 [%]: 97.5
- 弯曲模量 [MPa]: 2.70
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Viscosity | 100 - 400 cP @Temperature 45.0 °C | 100 - 400 cP @Temperature 113 °F | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 66.0 MPa | 9570 psi | Plain Cast Resin; ASTM D638 |
| Elongation at Break | 3.50 - 4.50 % | 3.50 - 4.50 % | Plain Cast Resin; ASTM D638 |
| Modulus of Elasticity | 3.20 GPa | 464 ksi | Plain Cast Resin; ASTM D638 |
| Flexural Yield Strength | 97.5 MPa | 14100 psi | Plain Cast Resin; ASTM D790 |
| Flexural Modulus | 2.70 GPa | 392 ksi | Plain Cast Resin; ASTM D790 |
| Izod Impact, Notched | 4.30 J/cm | 8.06 ft-lb/in | Plain Cast Resin; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 °C | 129 °F | Plain Cast Resin; ASTM D648 |
| Glass Transition Temp, Tg | 83.0 °C | 181 °F | Plain Cast Resin; ASTM D3418 |
| Processing Properties | Metric | English | Comments |
| Pot Life | 15.0 - 20.0 min @Temperature 23.0 °C | 15.0 - 20.0 min @Temperature 73.4 °F | |