- 拉伸强度 [MPa]: 31.0
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 69 | 69 | |
| Tensile Strength, Yield | 31.0 MPa | 4490 psi | |
| Elongation at Yield | 520 % | 520 % | |
| 100% Modulus | 0.00393 GPa | 0.570 ksi | |
| 200% Modulus | 0.00903 GPa | 1.31 ksi | |
| 300% Modulus | 0.0158 GPa | 2.29 ksi | |
| Tear Strength | 63.0 kN/m | 359 pli | Die C |
| Compression Set | 30 % @Temperature 70.0 °C, Time 79200 sec | 30 % @Temperature 158 °F, Time 22.0 hour | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 3.80 min @Temperature 155 °C | 0.0633 hour @Temperature 311 °F | ts2 |
| 9.60 min @Temperature 155 °C | 0.160 hour @Temperature 311 °F | TC90 | |