- 拉伸强度 [MPa]: 22.28
| Mechanical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Hardness, Shore A | 58 | 58 | |||
| 70 | 70 | heat aged 70 hours @ 100ºC | |||
| Tensile Strength, Yield | 22.28 MPa | 3232 psi | |||
| Elongation at Yield | 560 % | 560 % | |||
| 100% Modulus | 0.00243 GPa | 0.353 ksi | |||
| 200% Modulus | 0.00645 GPa | 0.936 ksi | |||
| 300% Modulus | 0.01104 GPa | 1.601 ksi | |||
| Tear Strength | 51.0 kN/m | 291 pli | Die C | ||
| Compression Set | 50 % @Temperature 70.0 °C, Time 79200 sec | 50 % @Temperature 158 °F, Time 22.0 hour | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 11.0 min @Temperature 155 °C | 0.183 hour @Temperature 311 °F | |||
| Descriptive Properties | |||||
| Weight Loss (%) | 1.6 | heat aged 70 hours @ 100ºC | |||