- 拉伸强度 [MPa]: 26.79
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 75 | 75 | |
| Tensile Strength, Yield | 26.79 MPa | 3886 psi | |
| Elongation at Yield | 531 % | 531 % | |
| 100% Modulus | 0.00471 GPa | 0.683 ksi | |
| 200% Modulus | 0.009942 GPa | 1.442 ksi | |
| 300% Modulus | 0.0153 GPa | 2.22 ksi | |
| Tear Strength | 60.8 kN/m | 347 pli | |
| Taber Abrasion, mg/1000 Cycles | 5.0 @Load 1.00 kg | 5.0 @Load 2.20 lb | H-18 wheel |
| Compression Set | 46.8 % @Temperature 70.0 °C, Time 79200 sec | 46.8 % @Temperature 158 °F, Time 22.0 hour | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 10.0 min @Temperature 155 °C | 0.167 hour @Temperature 311 °F | |