- 拉伸强度 [MPa]: 11.7
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.50 g/cc | 1.50 g/cc | |
| Mooney Viscosity | 23 @Temperature 121 °C | 23 @Temperature 250 °F | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 68 | 68 | |
| Tensile Strength, Yield | 11.7 MPa | 1700 psi | |
| Elongation at Yield | 650 % | 650 % | |
| 100% Modulus | 0.00224 GPa | 0.325 ksi | |
| 300% Modulus | 0.00345 GPa | 0.500 ksi | |
| Tear Strength | 25.8 kN/m | 147 pli | Graves |
| Compression Set | 47 % | 47 % | Method B |
| Processing Properties | Metric | English | Comments |
| Cure Time | 90.0 min @Temperature 142 °C | 1.50 hour @Temperature 287 °F | |