Rogers Corporation Poron® 4701-50 Thin as Cast Urethane Foam, Firm, Thin as Cast物性表参数

Rogers Corporation Poron® 4701-50 Thin as Cast Urethane Foam, Firm, Thin as Cast

Rogers Corporation Poron® 4701-50 Thin as Cast Urethane Foam, Firm, Thin as Cast 物性表: Rogers Corporation Poron® 4701-50 Thin as Cast Urethane Foam, Firm, Thin as Cast物性表及特性介绍,Rogers Corporation Poron® 4701-50 Thin as Cast Urethane Foam, Firm, Thin as Cast注塑参数详情,如需Rogers Corporation Poron® 4701-50 Thin as Cast Urethane Foam, Firm, Thin as Cast下载, 可到相关下载区下载

密度 [g/cm3]: 0.481
吸水率 [%]: 5.0
脆化温度 [℃]: -40.0

Physical Properties	Metric	English	Comments

Density	0.481 g/cc	0.0174 lb/in³	ASTM D3574-95 Test A
Water Absorption	5.0 %	5.0 %	Immersion; ASTM D570-95
Moisture Absorption at Equilibrium	2.0 %	2.0 %	High Humidity; AMS 3568-95
Thickness	432 - 508 microns	17.0 - 20.0 mil	Range of Thicknesses Available
Outgassing - Total Mass Loss	0.060 % @Temperature 125 °C, Time 86400 sec	0.060 % @Temperature 257 °F, Time 24.0 hour	CVCM; at 7000 Pa; ASTM E595-93
	0.43 % @Temperature 125 °C, Time 86400 sec	0.43 % @Temperature 257 °F, Time 24.0 hour	WVR; at 7000 Pa; ASTM E595-93
	0.90 % @Temperature 125 °C, Time 86400 sec	0.90 % @Temperature 257 °F, Time 24.0 hour	TML; at 7000 Pa; ASTM E595-93

Mechanical Properties	Metric	English	Comments
Hardness, Shore O	55	55	ASTM D2240-97
Tensile Strength	>= 1.10 MPa	>= 160 psi	ASTM D3574-75 Test E
	1.64 MPa	238 psi	Typical; ASTM D3574-75 Test E
Elongation at Break	>= 90 %	>= 90 %	ASTM D3574-75 Test E
	118 %	118 %	Typical; ASTM D3574-75 Test E
Compressive Yield Strength	0.0345 - 0.310 MPa @Strain 25.0 %	5.00 - 45.0 psi @Strain 25.0 %	Range, 0.2"/min. strain rate
	0.221 MPa @Strain 25.0 %	32.0 psi @Strain 25.0 %	Typical value, 0.2"/min. strain rate
Tear Strength	>= 1.60 kN/m	>= 9.13 pli	ASTM D264-91 Die C
	4.40 kN/m	25.1 pli	Typical; ASTM D264-91 Die C
Compression Set	5.0 % @Temperature 23.0 °C	5.0 % @Temperature 73.4 °F	ASTM D1667-90 Test D
	5.0 % @Temperature 121 °C	5.0 % @Temperature 250 °F	autoclaved 5 hrs; ASTM D3574-95 J/Test D
	10 % @Temperature 70.0 °C	10 % @Temperature 158 °F	ASTM D3574-95 Test D

Electrical Properties	Metric	English	Comments
Volume Resistivity	2.00e+12 ohm-cm	2.00e+12 ohm-cm	ASTM D257-99
Dielectric Constant	1.63 @Time 86400 sec	1.63 @Time 24.0 hour	50% RH; ASTM D150
Dielectric Strength	1.97 kV/mm	50.0 kV/in	ASTM D149-97a
Dissipation Factor	0.050	0.050	ASTM D150-98

Thermal Properties	Metric	English	Comments
CTE, linear	230 - 310 µm/m-°C	128 - 172 µin/in-°F
Maximum Service Temperature, Air	90.0 °C	194 °F	Constant use; SAE J-2236
	121 °C	250 °F	Intermittent use; ASTM D746-98
Brittleness Temperature	-40.0 °C	-40.0 °F	ASTM D746-98

Descriptive Properties
Flammability Test	pass		MVSS 302; 0.045 in.

关键词:
供应
聚氨酯TS
Firm
Rogers Corporation Poron® 4701-50 Thin as Cast Urethane Foam
Thin as Cast

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-37523.html

免责声明: 本文 Rogers Corporation Poron® 4701-50 Thin as Cast Urethane Foam, Firm, Thin as Cast 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络