Rogers Corporation Poron® ThinStik™ 92-12020 Self-Adhesive Urethane Foam

Rogers Corporation Poron® ThinStik™ 92-12020 Self-Adhesive Urethane Foam 物性表: Rogers Corporation Poron® ThinStik™ 92-12020 Self-Adhesive Urethane Foam物性表及特性介绍,Rogers Corporation Poron® ThinStik™ 92-12020 Self-Adhesive Urethane Foam注塑参数详情,如需Rogers Corporation Poron® ThinStik™ 92-12020 Self-Adhesive Urethane Foam下载, 可到相关下载区下载
  • 密度 [g/cm3]: 0.192
 
Physical PropertiesMetricEnglishComments
Density 0.192 g/cc0.00694 lb/in³ASTM D3574-95 Test A
 
Mechanical PropertiesMetricEnglishComments
Film Elongation at Break, MD 78 %78 %ASTM D882
 74 %
@Temperature 66.0 °C,
Time 346000 sec		74 %
@Temperature 151 °F,
Time 96.0 hour		80% RH; ASTM D882
Film Elongation at Break, TD 32 %32 %ASTM D882
 66 %
@Temperature 66.0 °C,
Time 346000 sec		66 %
@Temperature 151 °F,
Time 96.0 hour		80% RH; ASTM D882
Compressive Yield Strength 0.0112 MPa
@Strain 25.0 %		1.63 psi
@Strain 25.0 %		0.2"/min. strain rate
Tear Strength  0.310 kN/m
@Time 1190 sec		1.77 pli
@Time 0.330 hour		Peel Adhesion, 180° Peel, to Polypropylene; ASTM D1000
 0.320 kN/m
@Time 1190 sec		1.83 pli
@Time 0.330 hour		Peel Adhesion, 180° Peel, to Stainless Steel; ASTM D1000
 0.320 kN/m
@Time 259000 sec		1.83 pli
@Time 72.0 hour		Peel Adhesion, 180° Peel, to Polypropylene; ASTM D1000
 0.330 kN/m
@Time 1190 sec		1.88 pli
@Time 0.330 hour		Peel Adhesion, 180° Peel, to ABS; ASTM D1000
 0.330 kN/m
@Time 1190 sec		1.88 pli
@Time 0.330 hour		Peel Adhesion, 180° Peel, to Acrylic; ASTM D1000
 0.340 kN/m
@Time 1190 sec		1.94 pli
@Time 0.330 hour		Peel Adhesion, 180° Peel, to Polycarbonate; ASTM D1000
 0.360 kN/m
@Time 259000 sec		2.05 pli
@Time 72.0 hour		Peel Adhesion, 180° Peel, to Stainless Steel; ASTM D1000
 0.390 kN/m
@Time 259000 sec		2.23 pli
@Time 72.0 hour		Peel Adhesion, 180° Peel, to ABS; ASTM D1000
 0.390 kN/m
@Time 259000 sec		2.23 pli
@Time 72.0 hour		Peel Adhesion, 180° Peel, to Acrylic; ASTM D1000
 0.404 kN/m
@Time 259000 sec		2.31 pli
@Time 72.0 hour		Peel Adhesion, 180° Peel, to Polycarbonate; ASTM D1000
Compression Set  <= 5.0 %
@Temperature 23.0 °C		<= 5.0 %
@Temperature 73.4 °F		ASTM D3574-95 Test D
 <= 10 %
@Temperature 70.0 °C		<= 10 %
@Temperature 158 °F		ASTM D3574-95 Test D
Seal Strength 9.40 g/25 mm9.40 g/inRelease Adhesion, 180° Peel; ASTM D1000
 10.6 g/25 mm
@Temperature 66.0 °C,
Time 346000 sec		10.6 g/in
@Temperature 151 °F,
Time 96.0 hour		Release Adhesion, 180° Peel, 80% RH; ASTM D1000
 
Descriptive Properties
Tack411 gASTM D2979 (1 second dwell), 96 hours at 66°C/80% RH
 424 gASTM D2979 (1 second dwell)
Tensile, CMD (lb) per ASTM D882580% RH; 66°C; 96 hr
 9.1
Tensile, MD (lb) per ASTM D88211.480% RH; 66°C; 96 hr
 12

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-37519.html

免责声明: 本文 Rogers Corporation Poron® ThinStik™ 92-12020 Self-Adhesive Urethane Foam 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他物性信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4