- 拉伸强度 [MPa]: 1572.0
- 断裂伸长率 [%]: 1372
- 弯曲模量 [MPa]: 100
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 1572 MPa | 228000 psi | Room temperature |
| 1779 MPa @Temperature 71.0 °C | 258000 psi @Temperature 160 °F | 1/2 hr | |
| Tensile Modulus | 90.3 GPa | 13100 ksi | Room temperature |
| 93.8 GPa @Temperature 71.0 °C | 13600 ksi @Temperature 160 °F | 1/2 hr | |
| Flexural Yield Strength | 1372 MPa | 199000 psi | Room temperature |
| 1172 MPa @Temperature 71.0 °C | 170000 psi @Temperature 160 °F | 1/2 hr | |
| Flexural Modulus | 100 GPa | 14500 ksi | Room temperature |
| 97.9 GPa @Temperature 71.0 °C | 14200 ksi @Temperature 160 °F | 1/2 hr | |
| Compressive Yield Strength | 1248 MPa | 181000 psi | Room temperature |
| 1103 MPa @Temperature 71.0 °C | 160000 psi @Temperature 160 °F | 1/2 hr | |
| Compressive Modulus | 92.4 GPa | 13400 ksi | Room temperature |
| 90.3 GPa @Temperature 71.0 °C | 13100 ksi @Temperature 160 °F | 1/2 hr | |
| Shear Strength | 86.9 MPa | 12600 psi | Short Beam, Room temperature |
| 72.4 MPa @Temperature 71.0 °C | 10500 psi @Temperature 160 °F | Short Beam, 1/2 hr | |