- 拉伸强度 [MPa]: 579.0
| Mechanical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Tensile Strength, Yield | 579 MPa @Temperature 177 °C | 84000 psi @Temperature 351 °F | |||
| 610 MPa @Temperature 24.0 °C | 88500 psi @Temperature 75.2 °F | ||||
| Tensile Modulus | 60.5 GPa @Temperature 177 °C | 8770 ksi @Temperature 351 °F | |||
| 63.7 GPa @Temperature 24.0 °C | 9240 ksi @Temperature 75.2 °F | ||||
| Compressive Yield Strength | 585 MPa @Temperature 71.0 °C | 84800 psi @Temperature 160 °F | |||
| 666 MPa @Temperature 24.0 °C | 96600 psi @Temperature 75.2 °F | ||||
| Shear Strength | 47.0 MPa @Temperature 177 °C | 6820 psi @Temperature 351 °F | Short Beam | ||
| 48.0 MPa @Temperature 132 °C | 6960 psi @Temperature 270 °F | Short Beam | |||
| 65.0 MPa @Temperature -54.0 °C | 9430 psi @Temperature -65.2 °F | Short Beam | |||
| 72.0 MPa @Temperature 24.0 °C | 10400 psi @Temperature 75.2 °F | Short Beam | |||
| Descriptive Properties | |||||
| Cured Thickness per Ply (cm) | 0.034 | Laminate | |||
| Dry Resin Content (%) | 35-39 | Prepreg | |||
| Fiber Volume (%) | 62 | Laminate | |||
| Flow (%) | 9-22 | ||||