- 拉伸强度 [MPa]: 3.372
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Volatiles | 1.0 - 4.0 % | 1.0 - 4.0 % | Prepreg | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 3.372 MPa @Temperature 93.0 °C | 489.1 psi @Temperature 199 °F | Sandwich Flatwise Tension, Dry | ||
| 5.192 MPa @Temperature 24.0 °C | 753.0 psi @Temperature 75.2 °F | Sandwich Flatwise Tension, Dry | |||
| 1269 MPa @Temperature -54.0 °C | 184100 psi @Temperature -65.2 °F | Dry | |||
| 1331 MPa @Temperature 24.0 °C | 193000 psi @Temperature 75.2 °F | Dry | |||
| 1427 MPa @Temperature 71.0 °C | 207000 psi @Temperature 160 °F | Dry | |||
| 1751 MPa @Temperature 93.0 °C | 254000 psi @Temperature 199 °F | Dry | |||
| Tensile Modulus | 120 GPa @Temperature 24.0 °C | 17400 ksi @Temperature 75.2 °F | Dry | ||
| 121.4 GPa @Temperature 71.0 °C | 17610 ksi @Temperature 160 °F | Dry | |||
| 123.4 GPa @Temperature -54.0 °C | 17900 ksi @Temperature -65.2 °F | Dry | |||
| 126.2 GPa @Temperature 93.0 °C | 18300 ksi @Temperature 199 °F | Dry | |||
| Compressive Yield Strength | 183 MPa @Temperature 24.0 °C | 26500 psi @Temperature 75.2 °F | Compression After Impact, Dry | ||
| 1234 MPa @Temperature 71.0 °C | 179000 psi @Temperature 160 °F | Wet | |||
| 1455 MPa @Temperature 93.0 °C | 211000 psi @Temperature 199 °F | Dry | |||
| 1538 MPa @Temperature 71.0 °C | 223100 psi @Temperature 160 °F | Dry | |||
| 1655 MPa @Temperature 24.0 °C | 240000 psi @Temperature 75.2 °F | Dry | |||
| 1786 MPa @Temperature -59.0 °C | 259000 psi @Temperature -74.2 °F | Dry | |||
| Compressive Modulus | 108.3 GPa @Temperature -59.0 °C | 15710 ksi @Temperature -74.2 °F | Dry | ||
| 113.8 GPa @Temperature 93.0 °C | 16510 ksi @Temperature 199 °F | Dry | |||
| 114.5 GPa @Temperature 24.0 °C | 16610 ksi @Temperature 75.2 °F | Dry | |||
| 115.1 GPa @Temperature 71.0 °C | 16690 ksi @Temperature 160 °F | Dry | |||
| Descriptive Properties | |||||
| Cured Thickness per Ply (cm) | 0.02-0.021 | Laminate | |||
| Dry Resin Content (%) | 36-40 | Prepreg | |||
| Fiber Volume (%) | 50-55 | Laminate | |||
| Flow (%) | 13-25 | ||||