- 拉伸强度 [MPa]: 139.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.35 - 1.45 g/cc @Thickness 1.57 mm | 1.35 - 1.45 g/cc @Thickness 0.0620 in | ASTM D792 | ||
| Moisture Absorption at Equilibrium | 0.72 % @Thickness 1.57 mm | 0.72 % @Thickness 0.0620 in | ASTM D229 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 85 - 105 @Thickness 1.57 mm | 85 - 105 @Thickness 0.0620 in | ASTM D785 | ||
| Tensile Strength, Yield | 139 MPa @Thickness 1.57 mm | 20100 psi @Thickness 0.0620 in | CW; ASTM D638 | ||
| 165 MPa @Thickness 1.57 mm | 23900 psi @Thickness 0.0620 in | LW; ASTM D638 | |||
| Modulus of Elasticity | 10.3 GPa @Thickness 1.57 mm | 1500 ksi @Thickness 0.0620 in | CW; ASTM D229 | ||
| 12.4 GPa @Thickness 1.57 mm | 1800 ksi @Thickness 0.0620 in | LW; ASTM D229 | |||
| Flexural Strength | 308 MPa @Thickness 1.57 mm | 44600 psi @Thickness 0.0620 in | CW; ASTM D790 | ||
| 356 MPa @Thickness 1.57 mm | 51600 psi @Thickness 0.0620 in | LW; ASTM D790 | |||
| Compressive Strength | 286 MPa @Thickness 12.7 mm | 41500 psi @Thickness 0.500 in | ASTM D695 | ||
| Shear Strength | 96.5 MPa @Thickness 15.7 mm | 14000 psi @Thickness 0.620 in | ASTM D732 | ||
| Izod Impact, Unnotched | 1.17 J/cm @Thickness 12.7 mm | 2.20 ft-lb/in @Thickness 0.500 in | CW, Cond E-48/50; ASTM D256 | ||
| 1.76 J/cm @Thickness 12.7 mm | 3.30 ft-lb/in @Thickness 0.500 in | LW, Cond E-48/50; ASTM D256 | |||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Constant | 5.2 @Thickness 1.57 mm | 5.2 @Thickness 0.0620 in | Permittivity, Cond D-24/23; ASTM D150 | ||
| Dielectric Strength | 21.7 kV/mm @Thickness 1.57 mm | 550 kV/in @Thickness 0.0620 in | Cond D-48/50; ASTM D229 S.T. | ||
| 23.6 kV/mm @Thickness 1.57 mm | 600 kV/in @Thickness 0.0620 in | Cond A; ASTM D229 S.T. | |||
| Dielectric Breakdown | 7000 V @Thickness 1.57 mm | 7000 V @Thickness 0.0620 in | Cond D-48/50; ASTM D229 S/S | ||
| 53000 V @Thickness 1.57 mm | 53000 V @Thickness 0.0620 in | Cond A; ASTM D229 S/S | |||
| Dissipation Factor | 0.037 @Thickness 1.57 mm | 0.037 @Thickness 0.0620 in | Cond D-24/23; ASTM D150 | ||
| Arc Resistance | 120 sec @Thickness 3.17 mm | 120 sec @Thickness 0.125 in | ASTM D495 | ||
| Comparative Tracking Index | 200 V @Thickness 3.17 mm | 200 V @Thickness 0.125 in | ASTM D3638 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 15.0 µm/m-°C @Thickness 1.57 mm, Temperature 20.0 °C | 8.33 µin/in-°F @Thickness 0.0620 in, Temperature 68.0 °F | x-axis; IPC-TM 650-2.4.24 | ||
| CTE, linear, Transverse to Flow | 13.0 µm/m-°C @Thickness 1.57 mm, Temperature 20.0 °C | 7.22 µin/in-°F @Thickness 0.0620 in, Temperature 68.0 °F | x-axis; IPC-TM 650-2.4.24 | ||
| Maximum Service Temperature, Air | 125 °C | 257 °F | |||
| Flammability, UL94 | HB @Thickness 1.57 mm | HB @Thickness 0.0620 in | |||
| Descriptive Properties | |||||
| Bond Strength | 1500 lb | 0.5", ASTM D229 | |||
| Color | Natural, Black | ||||