- 拉伸强度 [MPa]: 741.0
- 断裂伸长率 [%]: 518
- 弯曲模量 [MPa]: 37.0
| Mechanical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Tensile Strength, Yield | 741 MPa @Temperature 23.0 °C | 107000 psi @Temperature 73.4 °F | 0°, Conditioning: 23°C; ASTM D3039 | ||
| Tensile Modulus | 54.0 GPa @Temperature 23.0 °C | 7830 ksi @Temperature 73.4 °F | 0°, Conditioning: 23°C; ASTM D3039 | ||
| Flexural Yield Strength | 518 MPa @Temperature 90.0 °C | 75100 psi @Temperature 194 °F | 0°, Conditioning: 23°C; ASTM D790 | ||
| 921 MPa @Temperature 23.0 °C | 134000 psi @Temperature 73.4 °F | 0°, Conditioning: 23°C; ASTM D790 | |||
| Flexural Modulus | 37.0 GPa @Temperature 90.0 °C | 5370 ksi @Temperature 194 °F | 0°, Conditioning: 23°C; ASTM D790 | ||
| 41.0 GPa @Temperature 23.0 °C | 5950 ksi @Temperature 73.4 °F | 0°, Conditioning: 23°C; ASTM D790 | |||
| Compressive Yield Strength | 350 MPa @Temperature 90.0 °C | 50800 psi @Temperature 194 °F | 0°, Conditioning: 23°C; ASTM D965 | ||
| 610 MPa @Temperature 23.0 °C | 88500 psi @Temperature 73.4 °F | 0°, Conditioning: 23°C; ASTM D965 | |||
| Shear Strength | 29.0 MPa @Temperature 60.0 °C | 4210 psi @Temperature 140 °F | 0°, Interlaminar, Conditioning: 60°C-90% RH; ASTM D2344 | ||
| 36.0 MPa @Temperature 90.0 °C | 5220 psi @Temperature 194 °F | 0°, Interlaminar, Conditioning: 23°C; ASTM D2344 | |||
| 69.0 MPa @Temperature 23.0 °C | 10000 psi @Temperature 73.4 °F | 0°, Interlaminar, Conditioning: 23°C; ASTM D2344 | |||
| Processing Properties | Metric | English | Comments | ||
| Shelf Life | 12.0 Month @Temperature -18.0 °C | 12.0 Month @Temperature -0.400 °F | |||
| Descriptive Properties | |||||
| Dry Resin Content (%) | 42 | ||||
| Fiber Volume (%) | 49.5 | ||||