- 密度 [g/cm3]: 0.032
Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 0.0320 g/cc | 0.00116 lb/in³ | DIN 53420, ISO 845, ASTM D 1622 |
Mechanical Properties | Metric | English | Comments |
Tensile Strength at Break | 1.00 MPa | 145 psi | DIN 53455, ISO 527-2, ASTM D 638 |
Elongation at Break | 3.5 % | 3.5 % | DIN 53455, ISO 527-2, ASTM D 638 |
Modulus of Elasticity | 0.0360 GPa | 5.22 ksi | ISO 527-2, ASTM D 638 |
Compressive Strength | 0.400 MPa | 58.0 psi | DIN 53421, ISO 844, ASTM D 1621 |
Shear Modulus | 0.0130 GPa | 1.89 ksi | DIN 53294, ASTM C 273 |
Shear Strength | 0.400 MPa | 58.0 psi | DIN 53294, ASTM C 273 |
Thermal Properties | Metric | English | Comments |
Maximum Service Temperature, Air | 180 °C | 356 °F | Heat Distortion Resistance; DIN 53424 |