- 密度 [g/cm3]: 0.0521
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.0521 g/cc | 0.00188 lb/in³ | DIN 53420, ISO 845, ASTM D 1622 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 1.90 MPa | 276 psi | DIN 53455, ISO 527-2, ASTM D 638 |
| Elongation at Break | 4.0 % | 4.0 % | DIN 53455, ISO 527-2, ASTM D 638 |
| Modulus of Elasticity | 0.0700 GPa | 10.2 ksi | ISO 527-2, ASTM D 638 |
| Flexural Strength | 1.60 MPa | 232 psi | DIN 53423, ISO 1209, ASTM D 790 |
| Compressive Strength | 0.900 MPa | 131 psi | DIN 53421, ISO 844, ASTM D 1621 |
| Shear Modulus | 0.0190 GPa | 2.76 ksi | DIN 53294, ASTM C 273 |
| Shear Strength | 0.800 MPa | 116 psi | DIN 53294, ASTM C 273 |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 180 °C | 356 °F | Heat Distortion Resistance; DIN 53424 |