- 密度 [g/cm3]: 1.73
- 缺口冲击强度: 0.69
- 弯曲强度 [MPa]: 123.0
- 弯曲模量 [MPa]: 14.7
- 热变形温度 [℃]: 215.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.73 g/cc | 0.0625 lb/in³ | |
| Linear Mold Shrinkage | 0.0010 cm/cm | 0.0010 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 123 MPa | 17800 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Flexural Strength | 203 MPa | 29400 psi | ASTM D790 |
| Flexural Modulus | 14.7 GPa | 2130 ksi | ASTM D790 |
| Izod Impact, Notched | 0.690 J/cm | 1.29 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.23 J/cm | 9.80 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 210 - 225 °C | 410 - 437 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C | 419 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 235 - 249 °C | 455 - 480 °F | Approximate middle barrel temperature range |