- 密度 [g/cm3]: 1.22
- 缺口冲击强度: 45.0
- 拉伸强度 [MPa]: 55.0
- 弯曲模量 [MPa]: 2.00
- 热变形温度 [℃]: 100.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.22 g/cc | 0.0441 lb/in³ | ISO 1183-1 |
| Linear Mold Shrinkage, Flow | 0.0070 - 0.0090 cm/cm | 0.0070 - 0.0090 in/in | b.o. ISO 2577 |
| Linear Mold Shrinkage, Transverse | 0.0070 - 0.0090 cm/cm | 0.0070 - 0.0090 in/in | b.o. ISO 2577 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 45.0 MPa | 6530 psi | 50 mm/min; ISO 527-1,-2 |
| Tensile Strength, Yield | 55.0 MPa | 7980 psi | 50 mm/min; ISO 527-1,-2 |
| Elongation at Break | >= 50 % | >= 50 % | Nominal, 50 mm/min; ISO 527-1,-2 |
| Elongation at Yield | 4.5 % | 4.5 % | 50 mm/min; ISO 527-1,-2 |
| Tensile Modulus | 2.00 GPa | 290 ksi | 1 mm/min; ISO 527-1,-2 |
| Flexural Modulus | 2.00 GPa | 290 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 45.0 kJ/m² @Temperature -20.0 °C | 21.4 ft-lb/in² @Temperature -4.00 °F | ISO 180-A |
| 60.0 kJ/m² @Temperature 23.0 °C | 28.6 ft-lb/in² @Temperature 73.4 °F | ISO 180-A | |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | IEC 60093 |
| Dielectric Constant | 3.1 @Frequency 1.00e+6 Hz | 3.1 @Frequency 1.00e+6 Hz | IEC 60250 |
| 3.2 @Frequency 100 Hz | 3.2 @Frequency 100 Hz | IEC 60250 | |
| Dissipation Factor | 0.0030 @Frequency 100 Hz | 0.0030 @Frequency 100 Hz | IEC 60250 |
| 0.015 @Frequency 1.00e+6 Hz | 0.015 @Frequency 1.00e+6 Hz | IEC 60250 | |
| Comparative Tracking Index | 100 V | 100 V | CTI M; Solution B; IEC 60112 |
| 225 V | 225 V | Solution A; IEC 60112 | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 90.0 µm/m-°C @Temperature 23.0 - 55.0 °C | 50.0 µin/in-°F @Temperature 73.4 - 131 °F | ISO 11359-1,-2 |
| CTE, linear, Transverse to Flow | 90.0 µm/m-°C @Temperature 23.0 - 55.0 °C | 50.0 µin/in-°F @Temperature 73.4 - 131 °F | ISO 11359-1,-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | ISO 75-1,-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | ISO 75-1,-2 |
| Vicat Softening Point | 122 °C @Load 5.10 kg | 252 °F @Load 11.2 lb | 120°C/h; ISO 306 |
| Shrinkage | 0.10 - 0.20 % | 0.10 - 0.20 % | post-shrinkage; b.o. ISO 2577 |