Bayer MaterialScience Makroblend® UT5207 PC/PBT Blend 物性表: Bayer MaterialScience Makroblend® UT5207 PC/PBT Blend物性表及特性介绍,Bayer MaterialScience Makroblend® UT5207 PC/PBT Blend注塑参数详情,如需Bayer MaterialScience Makroblend® UT5207 PC/PBT Blend下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.22
  • 缺口冲击强度: 45.0
  • 拉伸强度 [MPa]: 55.0
  • 弯曲模量 [MPa]: 2.00
  • 热变形温度 [℃]: 100.0
 
Physical PropertiesMetricEnglishComments
Density 1.22 g/cc0.0441 lb/in³ISO 1183-1
Linear Mold Shrinkage, Flow 0.0070 - 0.0090 cm/cm0.0070 - 0.0090 in/inb.o. ISO 2577
Linear Mold Shrinkage, Transverse 0.0070 - 0.0090 cm/cm0.0070 - 0.0090 in/inb.o. ISO 2577
 
Mechanical PropertiesMetricEnglishComments
Tensile Strength at Break 45.0 MPa6530 psi50 mm/min; ISO 527-1,-2
Tensile Strength, Yield 55.0 MPa7980 psi50 mm/min; ISO 527-1,-2
Elongation at Break >= 50 %>= 50 %Nominal, 50 mm/min; ISO 527-1,-2
Elongation at Yield 4.5 %4.5 %50 mm/min; ISO 527-1,-2
Tensile Modulus 2.00 GPa290 ksi1 mm/min; ISO 527-1,-2
Flexural Modulus 2.00 GPa290 ksi2 mm/min; ISO 178
Izod Impact, Notched (ISO)  45.0 kJ/m²
@Temperature -20.0 °C
21.4 ft-lb/in²
@Temperature -4.00 °F
ISO 180-A
 60.0 kJ/m²
@Temperature 23.0 °C
28.6 ft-lb/in²
@Temperature 73.4 °F
ISO 180-A
 
Electrical PropertiesMetricEnglishComments
Volume Resistivity 1.00e+16 ohm-cm1.00e+16 ohm-cmIEC 60093
Surface Resistance 1.00e+15 ohm1.00e+15 ohmIEC 60093
Dielectric Constant  3.1
@Frequency 1.00e+6 Hz
3.1
@Frequency 1.00e+6 Hz
IEC 60250
 3.2
@Frequency 100 Hz
3.2
@Frequency 100 Hz
IEC 60250
Dissipation Factor  0.0030
@Frequency 100 Hz
0.0030
@Frequency 100 Hz
IEC 60250
 0.015
@Frequency 1.00e+6 Hz
0.015
@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index 100 V100 VCTI M; Solution B; IEC 60112
 225 V225 VSolution A; IEC 60112
 
Thermal PropertiesMetricEnglishComments
CTE, linear, Parallel to Flow 90.0 µm/m-°C
@Temperature 23.0 - 55.0 °C
50.0 µin/in-°F
@Temperature 73.4 - 131 °F
ISO 11359-1,-2
CTE, linear, Transverse to Flow 90.0 µm/m-°C
@Temperature 23.0 - 55.0 °C
50.0 µin/in-°F
@Temperature 73.4 - 131 °F
ISO 11359-1,-2
Deflection Temperature at 0.46 MPa (66 psi) 100 °C212 °FISO 75-1,-2
Deflection Temperature at 1.8 MPa (264 psi) 75.0 °C167 °FISO 75-1,-2
Vicat Softening Point 122 °C
@Load 5.10 kg
252 °F
@Load 11.2 lb
120°C/h; ISO 306
Shrinkage 0.10 - 0.20 %0.10 - 0.20 %post-shrinkage; b.o. ISO 2577

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-37825.html

免责声明: 本文 Bayer MaterialScience Makroblend® UT5207 PC/PBT Blend 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4