- 密度 [g/cm3]: 1.53
- 弯曲强度 [MPa]: 130.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.53 g/cc | 0.0553 lb/in³ | ISO 1183 | ||
| Moisture Absorption at Equilibrium | 0.12 % | 0.12 % | 23°C/50% R.H.; ISO 62 | ||
| Viscosity Test | 105 cm³/g | 105 cm³/g | Viscosity number | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Ultimate | 130 MPa | 18900 psi | 5mm/min; ISO 527 | ||
| Elongation at Break | 3.0 % | 3.0 % | 5mm/min; ISO 527 | ||
| Tensile Modulus | 8.98 GPa | 1300 ksi | 1mm/min; ISO 527 | ||
| Charpy Impact, Notched | 0.730 J/cm² | 3.47 ft-lb/in² | ISO 179 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 223 °C | 433 °F | 10 K/min | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 203 °C | 397 °F | ISO 75 | ||
| Descriptive Properties | |||||
| Form | Pellets | ||||
| Special characteristic | Heat stabilized or stable to heat | ||||