- 熔体流动速率 [g/10min]: 23.9
- 密度 [g/cm3]: 1.47
- 吸水率 [%]: 0.4
- 热变形温度 [℃]: 210.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.47 g/cc | 0.0531 lb/in³ | ISO 1183 | ||
| Water Absorption | 0.40 % | 0.40 % | DIN 53495/1L | ||
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | 23°C/50% R.H. | ||
| Viscosity Test | 105 cm³/g | 105 cm³/g | Viscosity number; ISO 1628 | ||
| Linear Mold Shrinkage, Flow | 0.0010 cm/cm | 0.0010 in/in | Sheet | ||
| 0.0029 cm/cm | 0.0029 in/in | 60x60x2mm; ISO 294 | |||
| Linear Mold Shrinkage, Transverse | 0.0075 cm/cm | 0.0075 in/in | 60x60x2mm; ISO 294 | ||
| 0.0075 cm/cm | 0.0075 in/in | Sheet | |||
| Melt Flow | 23.9 g/10 min @Load 2.16 kg, Temperature 275 °C | 23.9 g/10 min @Load 4.76 lb, Temperature 527 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Ball Indentation Hardness | 164 MPa | 23800 psi | ISO 2039-1 | ||
| Tensile Strength at Break | 125 MPa | 18100 psi | 5mm/min; ISO 527-2 | ||
| Tensile Strength | 65.0 MPa @Temperature 100 °C | 9430 psi @Temperature 212 °F | ISO 527 | ||
| 120 MPa @Temperature 50.0 °C | 17400 psi @Temperature 122 °F | ISO 527 | |||
| 150 MPa @Temperature 23.0 °C | 21800 psi @Temperature 73.4 °F | ISO 527 | |||
| 195 MPa @Temperature -40.0 °C | 28300 psi @Temperature -40.0 °F | ISO 527 | |||
| Elongation at Break | 2.2 % | 2.2 % | 5mm/min; ISO 527-2 | ||
| Modulus of Elasticity | 9.70 GPa | 1410 ksi | ISO 527-2 | ||
| Flexural Strength | 183 MPa | 26500 psi | ISO 178 | ||
| Charpy Impact Unnotched | 5.90 J/cm² | 28.1 ft-lb/in² | ISO 179/1eU | ||
| Charpy Impact, Notched | 0.900 J/cm² | 4.28 ft-lb/in² | ISO 179/1eA | ||
| Dart Drop, Total Energy | <= 5.00 J | <= 3.69 ft-lb | ISO 6603-1 | ||
| Tensile Creep Modulus, 1000 hours | 6700 MPa | 972000 psi | ISO 899-1 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 3.00e+15 ohm-cm | 3.00e+15 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | IEC 60093 | ||
| Dielectric Constant | 3.7 @Frequency 1.00e+6 Hz | 3.7 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| 3.8 @Frequency 100 Hz | 3.8 @Frequency 100 Hz | IEC 60250 | |||
| Dielectric Strength | 95.0 kV/mm | 2410 kV/in | IEC 243/1 | ||
| Dissipation Factor | 0.0030 @Frequency 100 Hz | 0.0030 @Frequency 100 Hz | IEC 60250 | ||
| 0.018 @Frequency 1.00e+6 Hz | 0.018 @Frequency 1.00e+6 Hz | IEC 60250 | |||
| Comparative Tracking Index | 125 V | 125 V | Test solution B; IEC 60112 | ||
| 500 V | 500 V | Test solution A; IEC 60112 | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 3.00 µm/m-°C @Temperature 23.0 - 80.0 °C | 1.67 µin/in-°F @Temperature 73.4 - 176 °F | DIN 53752 | ||
| Specific Heat Capacity | 1.50 J/g-°C | 0.359 BTU/lb-°F | IEC 1006 | ||
| Thermal Conductivity | 0.290 W/m-K | 2.01 BTU-in/hr-ft²-°F | DIN 52612 | ||
| Melting Point | 220 - 225 °C | 428 - 437 °F | |||
| Maximum Service Temperature, Air | 110 °C | 230 °F | at 50% loss of tensile strength after 20000h; IEC 216-1 | ||
| 140 °C | 284 °F | at 50% loss of tensile strength after 5000h; IEC 216-1 | |||
| 170 °C | 338 °F | ||||
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | ISO 75-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 175 °C | 347 °F | ISO 75-2 | ||
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |||
| HB @Thickness 0.800 mm | HB @Thickness 0.0315 in | ||||
| Flame Spread Index | <= 100 | <= 100 | [mm/min]; DIN 75200 | ||
| Glow Wire Test | 760 °C @Thickness 3.00 mm | 1400 °F @Thickness 0.118 in | IEC 695 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 250 - 275 °C | 482 - 527 °F | Injection molding | ||
| 270 °C | 518 °F | for shrinkage test | |||
| Mold Temperature | 60.0 - 100 °C | 140 - 212 °F | |||
| 80.0 °C | 176 °F | for shrinkage test | |||
| Descriptive Properties | |||||
| Color | Natural | ||||
| Commercial Status | Active America | ||||
| Form | Pellets | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||
| Processing | Injection Molding | ||||
| Special characteristic | Heat stabilized or stable to heat | ||||
| Light stabilized or stable to light | |||||
| Lubricant | |||||
| U.V. stabilized or stable to weather | |||||