- 熔体流动速率 [g/10min]: 41.7
- 密度 [g/cm3]: 1.39
- 吸水率 [%]: 0.4
- 拉伸强度 [MPa]: 100.0
- 热变形温度 [℃]: 210.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.39 g/cc | 0.0502 lb/in³ | ISO 1183 | ||
| Water Absorption | 0.40 % | 0.40 % | Saturation; DIN 53495/1L | ||
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | 23°C; 50% RH | ||
| Viscosity Measurement | 104 | 104 | [ml/g]; Viscosity number; ISO 1628 | ||
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm | 0.0020 in/in | Sheet | ||
| 0.0046 cm/cm | 0.0046 in/in | 60x60x2 mm; ISO 294 | |||
| Linear Mold Shrinkage, Transverse | 0.0091 cm/cm | 0.0091 in/in | 60x60x2 mm; ISO 294 | ||
| 0.010 cm/cm | 0.010 in/in | Sheet | |||
| Melt Flow | 41.7 g/10 min @Load 2.16 kg, Temperature 275 °C | 41.7 g/10 min @Load 4.76 lb, Temperature 527 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 100 MPa | 14500 psi | 50 mm/min; ISO 527-2 | ||
| Elongation at Yield | 2.6 % | 2.6 % | 50 mm/min; ISO 527-2 | ||
| Modulus of Elasticity | 6.80 GPa | 986 ksi | ISO 527-2 | ||
| Charpy Impact Unnotched | 4.90 J/cm² | 23.3 ft-lb/in² | ISO 179/1eU | ||
| Charpy Impact, Notched | 0.660 J/cm² | 3.14 ft-lb/in² | ISO 179/1eA | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 220 - 225 °C | 428 - 437 °F | DSC; ISO 11357-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | ISO 75-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | ISO 75-2 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 260 - 280 °C | 500 - 536 °F | Injection-molding | ||
| 270 °C | 518 °F | for shrinkage test | |||
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |||
| 80.0 °C | 176 °F | for shrinkage test | |||
| Descriptive Properties | |||||
| Color | Natural and Black | ||||
| Commercial Status | Europe | ||||
| Primary Processing Technique | Injection Molding | ||||