- 熔体流动速率 [g/10min]: 67.47
- 密度 [g/cm3]: 1.73
- 吸水率 [%]: 0.4
- 拉伸强度 [MPa]: 165.0
- 热变形温度 [℃]: 221.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Bulk Density | 0.600 - 0.900 g/cc | 0.0217 - 0.0325 lb/in³ | |||
| Density | 1.73 g/cc | 0.0625 lb/in³ | ISO 1183 | ||
| Water Absorption | 0.40 % | 0.40 % | ISO 62 | ||
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | ISO 62 | ||
| Viscosity Measurement | 90 | 90 | [cm3/g]; ISO 307 | ||
| Linear Mold Shrinkage, Flow | 0.0010 cm/cm | 0.0010 in/in | plate with film gate 150x150x3mm3 | ||
| 0.0024 cm/cm | 0.0024 in/in | ISO 2577 | |||
| Linear Mold Shrinkage, Transverse | 0.0075 cm/cm | 0.0075 in/in | plate with film gate 150x150x3mm3 | ||
| 0.0077 cm/cm | 0.0077 in/in | ISO 2577 | |||
| Melt Flow | 67.47 g/10 min @Load 10.0 kg, Temperature 275 °C | 67.47 g/10 min @Load 22.0 lb, Temperature 527 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 165 MPa | 23900 psi | 50 mm/min; ISO 527-1/-2 | ||
| Elongation at Break | 1.5 % | 1.5 % | ISO 527-1/-2 | ||
| Tensile Modulus | 18.7 GPa | 2710 ksi | ISO 527-1/-2 | ||
| Charpy Impact Unnotched | 5.20 J/cm² @Temperature 23.0 °C | 24.7 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eU | ||
| 5.80 J/cm² @Temperature -30.0 °C | 27.6 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 1.00 J/cm² @Temperature 23.0 °C | 4.76 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | IEC 60093 | ||
| Dielectric Constant | 4.5 @Frequency 1.00e+6 Hz | 4.5 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| 4.7 @Frequency 100 Hz | 4.7 @Frequency 100 Hz | IEC 60250 | |||
| Dissipation Factor | 0.0020 @Frequency 100 Hz | 0.0020 @Frequency 100 Hz | IEC 60250 | ||
| 0.015 @Frequency 1.00e+6 Hz | 0.015 @Frequency 1.00e+6 Hz | IEC 60250 | |||
| Comparative Tracking Index | 225 V | 225 V | Test Solution A; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 0.200 - 0.300 µm/m-°C @Temperature 23.0 - 80.0 °C | 0.111 - 0.167 µin/in-°F @Temperature 73.4 - 176 °F | ISO 11359-1/-2 | ||
| Melting Point | 235 °C | 455 °F | ISO 11357-1/-2 | ||
| Maximum Service Temperature, Air | 140 °C | 284 °F | at 50% loss of tensile strength after 20,000hr | ||
| 160 °C | 320 °F | at 50% loss of tensile strength after 5,000hr | |||
| 210 °C | 410 °F | ||||
| Deflection Temperature at 0.46 MPa (66 psi) | 221 °C | 430 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | ISO 75-1/-2 | ||
| Decomposition Temperature | >= 290 °C | >= 554 °F | |||
| Flammability, UL94 | HB @Thickness >=0.400 mm | HB @Thickness >=0.0157 in | |||
| HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | ||||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 80.0 °C | 176 °F | Hopper Throat | ||
| Zone 1 | 260 °C | 500 °F | Feed zone | ||
| Zone 2 | 265 °C | 509 °F | Compression | ||
| Zone 3 | 270 °C | 518 °F | Metering-zone | ||
| Zone 4 | 270 °C | 518 °F | Nozzle | ||
| Melt Temperature | 250 - 280 °C | 482 - 536 °F | Injection molding/Extrusion | ||
| 270 °C | 518 °F | Optimal | |||
| Mold Temperature | 60.0 - 100 °C | 140 - 212 °F | Injection molding | ||
| 80.0 °C | 176 °F | Optimal | |||
| Drying Temperature | 80.0 - 120 °C | 176 - 248 °F | |||
| Dry Time | 4 hour | 4 hour | |||
| Moisture Content | <= 0.040 % | <= 0.040 % | |||
| Descriptive Properties | |||||
| Color | BK 15029 | ||||
| Commercial Status | Europe | ||||
| Ignition Temperature | 350°C | ASTM D1929 | |||
| Peripheral Screw Speed | < 0.25 m/s | ||||