- 吸水率 [%]: 0.4
- 热变形温度 [℃]: 220.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Bulk Density | 0.600 - 0.900 g/cc | 0.0217 - 0.0325 lb/in³ | |||
| Water Absorption | 0.40 % | 0.40 % | ISO 62 | ||
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | ISO 62 | ||
| Viscosity Measurement | 95 | 95 | [cm3/g]; ISO 307 | ||
| Linear Mold Shrinkage, Flow | 0.0013 cm/cm | 0.0013 in/in | plate with film gate 150x150x3mm3 | ||
| 0.0032 cm/cm | 0.0032 in/in | ISO 2577 | |||
| Linear Mold Shrinkage, Transverse | 0.00889 cm/cm | 0.00889 in/in | plate with film gate 150x150x3mm3 | ||
| 0.0097 cm/cm | 0.0097 in/in | ISO 2577 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 120 MPa | 17400 psi | ISO 527-1/-2 | ||
| Elongation at Break | 2.2 % | 2.2 % | ISO 527-1/-2 | ||
| Tensile Modulus | 9.50 GPa | 1380 ksi | ISO 527-1/-2 | ||
| Charpy Impact Unnotched | 4.00 J/cm² @Temperature -30.0 °C | 19.0 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eU | ||
| 5.00 J/cm² @Temperature 23.0 °C | 23.8 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 0.780 J/cm² @Temperature 23.0 °C | 3.71 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 2.00e+15 ohm-cm | 2.00e+15 ohm-cm | IEC 60093 | ||
| Dielectric Constant | 3.7 @Frequency 1.00e+6 Hz | 3.7 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| 3.9 @Frequency 100 Hz | 3.9 @Frequency 100 Hz | IEC 60250 | |||
| Dissipation Factor | 0.0046 @Frequency 100 Hz | 0.0046 @Frequency 100 Hz | IEC 60250 | ||
| 0.0202 @Frequency 1.00e+6 Hz | 0.0202 @Frequency 1.00e+6 Hz | IEC 60250 | |||
| Comparative Tracking Index | 425 V | 425 V | Test Solution A; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 223 °C | 433 °F | ISO 11357-1/-2 | ||
| Maximum Service Temperature, Air | 170 °C | 338 °F | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | ISO 75-1/-2 | ||
| Decomposition Temperature | >= 300 °C | >= 572 °F | |||
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 250 - 275 °C | 482 - 527 °F | Injection molding/Extrusion | ||
| Mold Temperature | 60.0 - 100 °C | 140 - 212 °F | Injection molding | ||
| Descriptive Properties | |||||
| Commercial Status | Europe | ||||
| Ignition Temperature | >400°C | ASTM D1929 | |||