- 密度 [g/cm3]: 1.53
- 缺口冲击强度: 0.84
- 拉伸强度 [MPa]: 119.0
- 断裂伸长率 [%]: 190
- 弯曲模量 [MPa]: 7.60
- 热变形温度 [℃]: 216.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.53 g/cc | 0.0553 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0050 cm/cm | 0.0030 - 0.0050 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0040 - 0.0060 cm/cm | 0.0040 - 0.0060 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 119 MPa | 17300 psi | ASTM D638 |
| Flexural Yield Strength | 190 MPa | 27600 psi | ASTM D790 |
| Flexural Modulus | 7.60 GPa | 1100 ksi | ASTM D790 |
| Izod Impact, Notched | 0.840 J/cm | 1.57 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 227 °C | 441 °F | ASTM D3418 |
| Deflection Temperature at 0.46 MPa (66 psi) | 216 °C | 421 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 152 °C | 306 °F | ASTM D648 |