- 熔体流动速率 [g/10min]: 24.0
- 缺口冲击强度: 8.0
- 弯曲模量 [MPa]: 7.00
- 热变形温度 [℃]: 212.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.54 g/cc | 1.54 g/cc | ASTM D792 |
| Moisture Absorption at Equilibrium | 0.18 % | 0.18 % | 50% RH; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm | 0.0040 in/in | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.011 cm/cm | 0.011 in/in | ASTM D955 |
| Melt Flow | 24 g/10 min @Load 2.16 kg, Temperature 250 °C | 24 g/10 min @Load 4.76 lb, Temperature 482 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 106 MPa | 15400 psi | ASTM D638 |
| Tensile Modulus | 9.30 GPa | 1350 ksi | ASTM D638 |
| Flexural Strength | 160 MPa | 23200 psi | ASTM D790 |
| Flexural Modulus | 7.00 GPa | 1020 ksi | ASTM D790 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² | 3.81 ft-lb/in² | ASTM D256 |
| Izod Impact, Unnotched (ISO) | 50.0 kJ/m² | 23.8 ft-lb/in² | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.20e+16 ohm-cm | 1.20e+16 ohm-cm | ASTM D257 |
| Dielectric Strength | 20.0 kV/mm | 508 kV/in | ASTM D149 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 212 °C | 414 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 203 °C | 397 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 0.800 mm | V-0 @Thickness 0.0315 in | |
| V-0 @Thickness 1.60 mm | V-0 @Thickness 0.0630 in | ||