- 密度 [g/cm3]: 1.62
- 缺口冲击强度: 0.8
- 断裂伸长率 [%]: 166
- 弯曲强度 [MPa]: 114.0
- 弯曲模量 [MPa]: 8.30
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.62 g/cc | 0.0585 lb/in³ | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 114 MPa | 16500 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Flexural Yield Strength | 166 MPa | 24100 psi | ASTM D790 |
| Flexural Modulus | 8.30 GPa | 1200 ksi | ASTM D790 |
| Izod Impact, Notched | 0.800 J/cm | 1.50 ft-lb/in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Dielectric Strength | 18.0 kV/mm | 457 kV/in | ASTM D149 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 207 °C | 405 °F | ASTM D789 |
| Deflection Temperature at 1.8 MPa (264 psi) | 221 °C | 430 °F | ASTM D648 |
| Flammability, UL94 | V-0 | V-0 | 1/16 in. |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 254 °C | 489 °F | |