- 缺口冲击强度: 0.641
- 拉伸强度 [MPa]: 121.0
- 断裂伸长率 [%]: 165
- 弯曲模量 [MPa]: 8.96
- 热变形温度 [℃]: 213.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.66 g/cc | 1.66 g/cc | ASTM D792 |
| Filler Content | 30 % | 30 % | ASTM D2584 |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0050 cm/cm | 0.0030 - 0.0050 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 121 MPa | 17500 psi | ASTM D648 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Elongation at Yield | 3.0 % | 3.0 % | ASTM D638 |
| Flexural Yield Strength | 165 MPa | 24000 psi | ASTM D790 |
| Flexural Modulus | 8.96 GPa | 1300 ksi | ASTM D790 |
| Izod Impact, Notched | 0.641 J/cm @Temperature 22.8 °C | 1.20 ft-lb/in @Temperature 73.0 °F | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 213 °C | 415 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 199 °C | 390 °F | ASTM D648 |
| Flammability, UL94 | V-0 | V-0 | 1/32, 1/16, 1/8, 1/4 |
| Processing Properties | Metric | English | Comments |
| Rear Barrel Temperature | 221 - 249 °C | 430 - 480 °F | |
| Middle Barrel Temperature | 227 - 254 °C | 440 - 490 °F | |
| Front Barrel Temperature | 232 - 260 °C | 450 - 500 °F | |
| Nozzle Temperature | 238 - 266 °C | 460 - 510 °F | |
| Melt Temperature | 232 - 260 °C | 450 - 500 °F | |
| Mold Temperature | 82.2 - 121 °C | 180 - 250 °F | |
| Dry Time | <= 4 hour | <= 4 hour | to ensure moisture content is less than 0.02% |
| Injection Pressure | 4.96 - 8.27 MPa | 720 - 1200 psi | Secondary |
| 8.27 - 13.8 MPa | 1200 - 2000 psi | Initial | |
| Back Pressure | 0.345 MPa | 50.0 psi | |
| Shot Size | 30 - 80 % | 30 - 80 % | |
| Screw Speed | 25 - 100 rpm | 25 - 100 rpm | |