- 吸水率 [%]: 0.04
- 缺口冲击强度: 0.854
- 弯曲强度 [MPa]: 140.0
- 弯曲模量 [MPa]: 8.55
- 硬度: 118.0
- 热变形温度 [℃]: 216.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.54 g/cc | 1.54 g/cc | ASTM D792 |
| Water Absorption | 0.040 % | 0.040 % | 24 hr immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0050 - 0.0080 cm/cm | 0.0050 - 0.0080 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 84 | 84 | ASTM D785 |
| Hardness, Rockwell R | 118 | 118 | ASTM D785 |
| Tensile Strength, Ultimate | 140 MPa | 20300 psi | ASTM D638 |
| Flexural Strength | 195 MPa | 28300 psi | ASTM D790 |
| Flexural Modulus | 8.55 GPa | 1240 ksi | ASTM D790 |
| Compressive Yield Strength | 124 MPa | 18000 psi | ASTM D695 |
| Izod Impact, Notched | 0.854 J/cm @Thickness 3.17 mm | 1.60 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 210 - 227 °C | 410 - 440 °F | ASTM D789 |
| Deflection Temperature at 0.46 MPa (66 psi) | 216 °C | 420 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 198 °C | 388 °F | ASTM D648 |
| Flammability, UL94 | HB | HB | |