- 熔体流动速率 [g/10min]: 37.26
- 密度 [g/cm3]: 1.62
- 吸水率 [%]: 0.3
- 热变形温度 [℃]: 220.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.62 g/cc | 0.0585 lb/in³ | ISO 1183 | ||
| Water Absorption | 0.30 % | 0.30 % | Sim. to ISO 62 | ||
| Moisture Absorption at Equilibrium | 0.15 % | 0.15 % | Humidity Absorption; Sim. to ISO 62 | ||
| Melt Flow | 37.26 g/10 min @Load 2.16 kg, Temperature 250 °C | 37.26 g/10 min @Load 4.76 lb, Temperature 482 °F | Calculated from Volume Flow Rate of 23 cm3/10min.; ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 120 MPa | 17400 psi | ISO 527-1/-2 | ||
| Elongation at Break | 3.0 % | 3.0 % | ISO 527-1/-2 | ||
| Tensile Modulus | 7.50 GPa | 1090 ksi | ISO 527-1/-2 | ||
| Charpy Impact Unnotched | 4.50 J/cm² @Temperature -30.0 °C | 21.4 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eU | ||
| 4.50 J/cm² @Temperature 23.0 °C | 21.4 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 0.700 J/cm² @Temperature -30.0 °C | 3.33 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eA | ||
| 0.700 J/cm² @Temperature 23.0 °C | 3.33 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 | ||
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | IEC 60093 | ||
| Dielectric Constant | 3.5 @Frequency 1e+6 Hz | 3.5 @Frequency 1e+6 Hz | IEC 60250 | ||
| 3.7 @Frequency 100 Hz | 3.7 @Frequency 100 Hz | IEC 60250 | |||
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | IEC 60243-1 | ||
| Dissipation Factor | 0.0020 @Frequency 100 Hz | 0.0020 @Frequency 100 Hz | IEC 60250 | ||
| 0.018 @Frequency 1e+6 Hz | 0.018 @Frequency 1e+6 Hz | IEC 60250 | |||
| Comparative Tracking Index | 400 V | 400 V | IEC 60112 | ||
| 400 - 599 V | 400 - 599 V | PLC 1; UL 746A | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 50.0 µm/m-°C @Temperature 20.0 °C | 27.8 µin/in-°F @Temperature 68.0 °F | ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 80.0 µm/m-°C @Temperature 20.0 °C | 44.4 µin/in-°F @Temperature 68.0 °F | ISO 11359-1/-2 | ||
| Melting Point | 225 °C | 437 °F | 10°C/min; ISO 11357-1/-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | ISO 75-1/-2 | ||
| UL RTI, Electrical | 140 °C @Thickness 1.50 mm | 284 °F @Thickness 0.0591 in | UL746B | ||
| 140 °C @Thickness 0.750 mm | 284 °F @Thickness 0.0295 in | UL746B | |||
| UL RTI, Mechanical with Impact | 130 °C @Thickness 0.750 mm | 266 °F @Thickness 0.0295 in | UL746B | ||
| 130 °C @Thickness 1.50 mm | 266 °F @Thickness 0.0591 in | UL746B | |||
| UL RTI, Mechanical without Impact | 130 °C @Thickness 1.50 mm | 266 °F @Thickness 0.0591 in | UL746B | ||
| 130 °C @Thickness 0.750 mm | 266 °F @Thickness 0.0295 in | UL746B | |||
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | IEC 60695-11-10 | ||
| HB @Thickness 0.750 mm | HB @Thickness 0.0295 in | IEC 60695-11-10 | |||
| Oxygen Index | 20 % | 20 % | ISO 4589-1/-2 | ||
| Descriptive Properties | |||||
| Injection Molding | Yes | ||||
| Release Agent | Yes | ||||
| With Fillers | Yes | ||||