- 密度 [g/cm3]: 1.493
- 拉伸强度 [MPa]: 91.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.493 g/cc | 0.05394 lb/in³ | ISO 1183 | ||
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0050 cm/cm @Thickness 2.00 mm | 0.0030 - 0.0050 in/in @Thickness 0.0787 in | Parallel; ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0090 cm/cm @Thickness 2.00 mm | 0.0050 - 0.0090 in/in @Thickness 0.0787 in | Normal; ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 91.0 MPa @Temperature 23.0 °C | 13200 psi @Temperature 73.4 °F | ISO 527 | ||
| Elongation at Break | 2.8 % @Temperature 23.0 °C | 2.8 % @Temperature 73.4 °F | ISO 527 | ||
| Tensile Modulus | 5.70 GPa @Temperature 23.0 °C | 827 ksi @Temperature 73.4 °F | ISO 527 | ||
| Charpy Impact Unnotched | 2.15 J/cm² @Temperature -30.0 °C | 10.2 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eU | ||
| 2.31 J/cm² @Temperature 23.0 °C | 11.0 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 0.500 J/cm² @Temperature -30.0 °C | 2.38 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eA | ||
| 0.510 J/cm² @Temperature 23.0 °C | 2.43 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 195 °C | 383 °F | ISO 75-1/-2 | ||
| UL RTI, Electrical | 130 °C @Thickness 0.710 mm | 266 °F @Thickness 0.0280 in | UL 746B | ||
| 130 °C @Thickness 1.50 mm | 266 °F @Thickness 0.0591 in | UL 746B | |||
| 130 °C @Thickness 3.00 mm | 266 °F @Thickness 0.118 in | UL 746B | |||
| UL RTI, Mechanical with Impact | 110 °C @Thickness 0.710 mm | 230 °F @Thickness 0.0280 in | UL 746B | ||
| 110 °C @Thickness 1.50 mm | 230 °F @Thickness 0.0591 in | UL 746B | |||
| 120 °C @Thickness 3.00 mm | 248 °F @Thickness 0.118 in | UL 746B | |||
| UL RTI, Mechanical without Impact | 130 °C @Thickness 0.710 mm | 266 °F @Thickness 0.0280 in | UL 746B | ||
| 130 °C @Thickness 1.50 mm | 266 °F @Thickness 0.0591 in | UL 746B | |||
| 130 °C @Thickness 3.00 mm | 266 °F @Thickness 0.118 in | UL 746B | |||
| Flammability, UL94 | V-0 @Thickness 0.710 mm | V-0 @Thickness 0.0280 in | UL94 | ||
| V-0 @Thickness 1.50 mm | V-0 @Thickness 0.0591 in | UL94 | |||
| V-0 @Thickness 3.00 mm | V-0 @Thickness 0.118 in | UL94 | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 223 °C | 433 °F | 10°C/min; ISO 11357-1/-3 | ||
| 250 °C | 482 °F | Optimum; Injection Molding | |||
| 240 - 260 °C | 464 - 500 °F | Injection Molding | |||
| Mold Temperature | 60.0 °C | 140 °F | optimum; Injection Molding | ||
| 10.0 - 110 °C | 50.0 - 230 °F | Injection Molding | |||
| Drying Temperature | 100 - 140 °C | 212 - 284 °F | Injection Molding | ||
| Dry Time | 2.00 - 6.00 hour | 2.00 - 6.00 hour | Injection Molding | ||
| Moisture Content | <= 0.040 % | <= 0.040 % | Injection Molding | ||
| Descriptive Properties | |||||
| Forms | Pellets | ||||
| Generic | PBT | ||||
| Material Status | Current | ||||
| Part Marking Code | >PBT-GF15FR(17)< | ISO 11469 | |||
| Processing Method | Injection Molding | ||||
| Product Category | Extrusion Resins | ||||
| Glass Reinforced Resins | |||||
| Resin Identification | PBT-GF15FR(17) | ISO 1043 | |||
| RoHS Compliance | Contact Manufacturer | ||||