DuPont Performance Polymers Crastin® SK602 NC010 PBT

DuPont Performance Polymers Crastin® SK602 NC010 PBT 物性表: DuPont Performance Polymers Crastin® SK602 NC010 PBT物性表及特性介绍,DuPont Performance Polymers Crastin® SK602 NC010 PBT注塑参数详情,如需DuPont Performance Polymers Crastin® SK602 NC010 PBT下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.41
  • 吸水率 [%]: 0.17
  • 缺口冲击强度: 0.58
  • 弯曲模量 [MPa]: 2.009
  • 热变形温度 [℃]: 220.0
 
Physical PropertiesMetricEnglishComments
Specific Gravity 1.41 g/cc1.41 g/ccASTM D792
Density 1.41 g/cc0.0509 lb/in³ISO 1183
Filler Content 15 %15 %
Water Absorption  0.17 %
@Temperature 23.0 °C		0.17 %
@Temperature 73.4 °F		Equilibrium 50%RH; ISO 62, Similar to
 0.42 %
@Temperature 23.0 °C		0.42 %
@Temperature 73.4 °F		Saturation, immersed; ISO 62, Similar to
Viscosity  66000 cP
@Shear Rate 10000 1/s,
Temperature 260 °C		66000 cP
@Shear Rate 10000 1/s,
Temperature 500 °F		ISO 11443
 79000 cP
@Shear Rate 10000 1/s,
Temperature 250 °C		79000 cP
@Shear Rate 10000 1/s,
Temperature 482 °F		ISO 11443
 91000 cP
@Shear Rate 5000 1/s,
Temperature 260 °C		91000 cP
@Shear Rate 5000 1/s,
Temperature 500 °F		ISO 11443
 95000 cP
@Shear Rate 10000 1/s,
Temperature 240 °C		95000 cP
@Shear Rate 10000 1/s,
Temperature 464 °F		ISO 11443
 108000 cP
@Shear Rate 5000 1/s,
Temperature 250 °C		108000 cP
@Shear Rate 5000 1/s,
Temperature 482 °F		ISO 11443
 130000 cP
@Shear Rate 5000 1/s,
Temperature 240 °C		130000 cP
@Shear Rate 5000 1/s,
Temperature 464 °F		ISO 11443
 137000 cP
@Shear Rate 2000 1/s,
Temperature 260 °C		137000 cP
@Shear Rate 2000 1/s,
Temperature 500 °F		ISO 11443
 164000 cP
@Shear Rate 2000 1/s,
Temperature 250 °C		164000 cP
@Shear Rate 2000 1/s,
Temperature 482 °F		ISO 11443
 184000 cP
@Shear Rate 1000 1/s,
Temperature 260 °C		184000 cP
@Shear Rate 1000 1/s,
Temperature 500 °F		ISO 11443
 198000 cP
@Shear Rate 2000 1/s,
Temperature 240 °C		198000 cP
@Shear Rate 2000 1/s,
Temperature 464 °F		ISO 11443
 221000 cP
@Shear Rate 1000 1/s,
Temperature 250 °C		221000 cP
@Shear Rate 1000 1/s,
Temperature 482 °F		ISO 11443
 242000 cP
@Shear Rate 500 1/s,
Temperature 260 °C		242000 cP
@Shear Rate 500 1/s,
Temperature 500 °F		ISO 11443
 269000 cP
@Shear Rate 1000 1/s,
Temperature 240 °C		269000 cP
@Shear Rate 1000 1/s,
Temperature 464 °F		ISO 11443
 294000 cP
@Shear Rate 500 1/s,
Temperature 250 °C		294000 cP
@Shear Rate 500 1/s,
Temperature 482 °F		ISO 11443
 361000 cP
@Shear Rate 500 1/s,
Temperature 240 °C		361000 cP
@Shear Rate 500 1/s,
Temperature 464 °F		ISO 11443
 390000 cP
@Shear Rate 100 1/s,
Temperature 260 °C		390000 cP
@Shear Rate 100 1/s,
Temperature 500 °F		ISO 11443
 498000 cP
@Shear Rate 100 1/s,
Temperature 250 °C		498000 cP
@Shear Rate 100 1/s,
Temperature 482 °F		ISO 11443
 640000 cP
@Shear Rate 100 1/s,
Temperature 240 °C		640000 cP
@Shear Rate 100 1/s,
Temperature 464 °F		ISO 11443
Linear Mold Shrinkage 0.0060 cm/cm0.0060 in/inFlow
 0.012 cm/cm0.012 in/inTransverse
Linear Mold Shrinkage, Flow 0.0055 cm/cm0.0055 in/inParallel; Annealed; ISO 294-4
 0.0040 cm/cm
@Thickness 2.00 mm		0.0040 in/in
@Thickness 0.0787 in		Parallel; ISO 294-4
Linear Mold Shrinkage, Transverse 0.014 cm/cm0.014 in/inNormal; Annealed; ISO 294-4
 0.011 cm/cm
@Thickness 2.00 mm		0.011 in/in
@Thickness 0.0787 in		Normal; ISO 294-4
Melt Index of Compound 15 g/10 min
@Load 2.16 kg,
Temperature 250 °C		15 g/10 min
@Load 4.76 lb,
Temperature 482 °F		cm3/10 min; ISO 1133
 
Mechanical PropertiesMetricEnglishComments
Tensile Strength at Break  46.0 MPa
@Temperature 150 °C		6670 psi
@Temperature 302 °F		ISO 527
 54.0 MPa
@Temperature 120 °C		7830 psi
@Temperature 248 °F		ISO 527
 109 MPa
@Temperature 23.0 °C		15800 psi
@Temperature 73.4 °F		ISO 527
 145 MPa
@Temperature -40.0 °C		21000 psi
@Temperature -40.0 °F		ISO 527
Tensile Strength 100 MPa
@Temperature 23.0 °C		14500 psi
@Temperature 73.4 °F		ASTM D638
Tensile Stress  4.49 MPa
@Strain 0.260 %,
Temperature 150 °C		651 psi
@Strain 0.260 %,
Temperature 302 °F		ISO 11403-1/-2
 5.92 MPa
@Strain 0.260 %,
Temperature 120 °C		859 psi
@Strain 0.260 %,
Temperature 248 °F		ISO 11403-1/-2
 6.91 MPa
@Strain 0.260 %,
Temperature 90.0 °C		1000 psi
@Strain 0.260 %,
Temperature 194 °F		ISO 11403-1/-2
 7.07 MPa
@Strain 0.220 %,
Temperature 60.0 °C		1030 psi
@Strain 0.220 %,
Temperature 140 °F		ISO 11403-1/-2
 7.15 MPa
@Strain 0.120 %,
Temperature -20.0 °C		1040 psi
@Strain 0.120 %,
Temperature -4.00 °F		ISO 11403-1/-2
 7.28 MPa
@Strain 0.120 %,
Temperature 0.000 °C		1060 psi
@Strain 0.120 %,
Temperature 32.0 °F		ISO 11403-1/-2
 7.42 MPa
@Strain 0.180 %,
Temperature 40.0 °C		1080 psi
@Strain 0.180 %,
Temperature 104 °F		ISO 11403-1/-2
 8.32 MPa
@Strain 0.140 %,
Temperature 23.0 °C		1210 psi
@Strain 0.140 %,
Temperature 73.4 °F		ISO 11403-1/-2
 9.33 MPa
@Strain 0.500 %,
Temperature 150 °C		1350 psi
@Strain 0.500 %,
Temperature 302 °F		ISO 11403-1/-2
 11.05 MPa
@Strain 0.480 %,
Temperature 120 °C		1603 psi
@Strain 0.480 %,
Temperature 248 °F		ISO 11403-1/-2
 13.09 MPa
@Strain 0.490 %,
Temperature 90.0 °C		1899 psi
@Strain 0.490 %,
Temperature 194 °F		ISO 11403-1/-2
 13.69 MPa
@Strain 0.750 %,
Temperature 150 °C		1986 psi
@Strain 0.750 %,
Temperature 302 °F		ISO 11403-1/-2
 13.76 MPa
@Strain 0.220 %,
Temperature -20.0 °C		1996 psi
@Strain 0.220 %,
Temperature -4.00 °F		ISO 11403-1/-2
 14.44 MPa
@Strain 0.230 %,
Temperature 0.000 °C		2094 psi
@Strain 0.230 %,
Temperature 32.0 °F		ISO 11403-1/-2
 14.57 MPa
@Strain 0.450 %,
Temperature 60.0 °C		2113 psi
@Strain 0.450 %,
Temperature 140 °F		ISO 11403-1/-2
 15.93 MPa
@Strain 0.260 %,
Temperature 23.0 °C		2310 psi
@Strain 0.260 %,
Temperature 73.4 °F		ISO 11403-1/-2
 16.2 MPa
@Strain 0.730 %,
Temperature 120 °C		2350 psi
@Strain 0.730 %,
Temperature 248 °F		ISO 11403-1/-2
 16.27 MPa
@Strain 0.370 %,
Temperature 40.0 °C		2360 psi
@Strain 0.370 %,
Temperature 104 °F		ISO 11403-1/-2
 17.16 MPa
@Strain 0.980 %,
Temperature 150 °C		2489 psi
@Strain 0.980 %,
Temperature 302 °F		ISO 11403-1/-2
 18.73 MPa
@Strain 0.720 %,
Temperature 90.0 °C		2717 psi
@Strain 0.720 %,
Temperature 194 °F		ISO 11403-1/-2
 20.48 MPa
@Strain 1.22 %,
Temperature 150 °C		2970 psi
@Strain 1.22 %,
Temperature 302 °F		ISO 11403-1/-2
 20.67 MPa
@Strain 0.970 %,
Temperature 120 °C		2998 psi
@Strain 0.970 %,
Temperature 248 °F		ISO 11403-1/-2
 20.81 MPa
@Strain 0.330 %,
Temperature -20.0 °C		3018 psi
@Strain 0.330 %,
Temperature -4.00 °F		ISO 11403-1/-2
 20.85 MPa
@Strain 0.660 %,
Temperature 60.0 °C		3024 psi
@Strain 0.660 %,
Temperature 140 °F		ISO 11403-1/-2
 21.59 MPa
@Strain 0.350 %,
Temperature 0.000 °C		3131 psi
@Strain 0.350 %,
Temperature 32.0 °F		ISO 11403-1/-2
 23.39 MPa
@Strain 1.47 %,
Temperature 150 °C		3392 psi
@Strain 1.47 %,
Temperature 302 °F		ISO 11403-1/-2
 23.54 MPa
@Strain 0.390 %,
Temperature 23.0 °C		3414 psi
@Strain 0.390 %,
Temperature 73.4 °F		ISO 11403-1/-2
 23.75 MPa
@Strain 0.540 %,
Temperature 40.0 °C		3445 psi
@Strain 0.540 %,
Temperature 104 °F		ISO 11403-1/-2
 23.77 MPa
@Strain 0.950 %,
Temperature 90.0 °C		3448 psi
@Strain 0.950 %,
Temperature 194 °F		ISO 11403-1/-2
 24.47 MPa
@Strain 1.20 %,
Temperature 120 °C		3549 psi
@Strain 1.20 %,
Temperature 248 °F		ISO 11403-1/-2
 25.93 MPa
@Strain 1.72 %,
Temperature 150 °C		3761 psi
@Strain 1.72 %,
Temperature 302 °F		ISO 11403-1/-2
 26.57 MPa
@Strain 0.870 %,
Temperature 60.0 °C		3854 psi
@Strain 0.870 %,
Temperature 140 °F		ISO 11403-1/-2
 27.54 MPa
@Strain 1.14 %,
Temperature 90.0 °C		3994 psi
@Strain 1.14 %,
Temperature 194 °F		ISO 11403-1/-2
 27.87 MPa
@Strain 0.440 %,
Temperature -20.0 °C		4042 psi
@Strain 0.440 %,
Temperature -4.00 °F		ISO 11403-1/-2
 28.13 MPa
@Strain 1.45 %,
Temperature 120 °C		4080 psi
@Strain 1.45 %,
Temperature 248 °F		ISO 11403-1/-2
 28.21 MPa
@Strain 1.96 %,
Temperature 150 °C		4092 psi
@Strain 1.96 %,
Temperature 302 °F		ISO 11403-1/-2
 29.35 MPa
@Strain 0.470 %,
Temperature 0.000 °C		4257 psi
@Strain 0.470 %,
Temperature 32.0 °F		ISO 11403-1/-2
 30.16 MPa
@Strain 2.21 %,
Temperature 150 °C		4374 psi
@Strain 2.21 %,
Temperature 302 °F		ISO 11403-1/-2
 30.95 MPa
@Strain 0.510 %,
Temperature 23.0 °C		4489 psi
@Strain 0.510 %,
Temperature 73.4 °F		ISO 11403-1/-2
 31.41 MPa
@Strain 1.69 %,
Temperature 120 °C		4556 psi
@Strain 1.69 %,
Temperature 248 °F		ISO 11403-1/-2
 31.52 MPa
@Strain 0.730 %,
Temperature 40.0 °C		4572 psi
@Strain 0.730 %,
Temperature 104 °F		ISO 11403-1/-2
 31.81 MPa
@Strain 1.37 %,
Temperature 90.0 °C		4614 psi
@Strain 1.37 %,
Temperature 194 °F		ISO 11403-1/-2
 31.82 MPa
@Strain 1.08 %,
Temperature 60.0 °C		4615 psi
@Strain 1.08 %,
Temperature 140 °F		ISO 11403-1/-2
 31.93 MPa
@Strain 2.46 %,
Temperature 150 °C		4631 psi
@Strain 2.46 %,
Temperature 302 °F		ISO 11403-1/-2
 33.34 MPa
@Strain 2.69 %,
Temperature 150 °C		4836 psi
@Strain 2.69 %,
Temperature 302 °F		ISO 11403-1/-2
 34.07 MPa
@Strain 1.92 %,
Temperature 120 °C		4941 psi
@Strain 1.92 %,
Temperature 248 °F		ISO 11403-1/-2
 34.3 MPa
@Strain 0.540 %,
Temperature -20.0 °C		4970 psi
@Strain 0.540 %,
Temperature -4.00 °F		ISO 11403-1/-2
 34.71 MPa
@Strain 2.93 %,
Temperature 150 °C		5034 psi
@Strain 2.93 %,
Temperature 302 °F		ISO 11403-1/-2
 35.66 MPa
@Strain 1.61 %,
Temperature 90.0 °C		5172 psi
@Strain 1.61 %,
Temperature 194 °F		ISO 11403-1/-2
 35.9 MPa
@Strain 3.18 %,
Temperature 150 °C		5210 psi
@Strain 3.18 %,
Temperature 302 °F		ISO 11403-1/-2
 36.29 MPa
@Strain 0.590 %,
Temperature 0.000 °C		5263 psi
@Strain 0.590 %,
Temperature 32.0 °F		ISO 11403-1/-2
 36.62 MPa
@Strain 2.17 %,
Temperature 120 °C		5311 psi
@Strain 2.17 %,
Temperature 248 °F		ISO 11403-1/-2
 36.95 MPa
@Strain 3.43 %,
Temperature 150 °C		5359 psi
@Strain 3.43 %,
Temperature 302 °F		ISO 11403-1/-2
 37.09 MPa
@Strain 0.620 %,
Temperature 23.0 °C		5379 psi
@Strain 0.620 %,
Temperature 73.4 °F		ISO 11403-1/-2
 37.15 MPa
@Strain 1.31 %,
Temperature 60.0 °C		5388 psi
@Strain 1.31 %,
Temperature 140 °F		ISO 11403-1/-2
 37.88 MPa
@Strain 3.67 %,
Temperature 150 °C		5494 psi
@Strain 3.67 %,
Temperature 302 °F		ISO 11403-1/-2
 37.95 MPa
@Strain 0.900 %,
Temperature 40.0 °C		5504 psi
@Strain 0.900 %,
Temperature 104 °F		ISO 11403-1/-2
 38.68 MPa
@Strain 3.92 %,
Temperature 150 °C		5610 psi
@Strain 3.92 %,
Temperature 302 °F		ISO 11403-1/-2
 38.83 MPa
@Strain 2.41 %,
Temperature 120 °C		5632 psi
@Strain 2.41 %,
Temperature 248 °F		ISO 11403-1/-2
 39.16 MPa
@Strain 1.84 %,
Temperature 90.0 °C		5680 psi
@Strain 1.84 %,
Temperature 194 °F		ISO 11403-1/-2
 39.44 MPa
@Strain 4.17 %,
Temperature 150 °C		5720 psi
@Strain 4.17 %,
Temperature 302 °F		ISO 11403-1/-2
 40.02 MPa
@Strain 4.39 %,
Temperature 150 °C		5804 psi
@Strain 4.39 %,
Temperature 302 °F		ISO 11403-1/-2
 40.58 MPa
@Strain 4.64 %,
Temperature 150 °C		5886 psi
@Strain 4.64 %,
Temperature 302 °F		ISO 11403-1/-2
 40.74 MPa
@Strain 2.66 %,
Temperature 120 °C		5909 psi
@Strain 2.66 %,
Temperature 248 °F		ISO 11403-1/-2
 41.09 MPa
@Strain 4.89 %,
Temperature 150 °C		5960 psi
@Strain 4.89 %,
Temperature 302 °F		ISO 11403-1/-2
 41.11 MPa
@Strain 0.650 %,
Temperature -20.0 °C		5963 psi
@Strain 0.650 %,
Temperature -4.00 °F		ISO 11403-1/-2
 41.52 MPa
@Strain 5.13 %,
Temperature 150 °C		6022 psi
@Strain 5.13 %,
Temperature 302 °F		ISO 11403-1/-2
 41.68 MPa
@Strain 1.53 %,
Temperature 60.0 °C		6045 psi
@Strain 1.53 %,
Temperature 140 °F		ISO 11403-1/-2
 41.91 MPa
@Strain 5.38 %,
Temperature 150 °C		6079 psi
@Strain 5.38 %,
Temperature 302 °F		ISO 11403-1/-2
 42.22 MPa
@Strain 5.63 %,
Temperature 150 °C		6124 psi
@Strain 5.63 %,
Temperature 302 °F		ISO 11403-1/-2
 42.28 MPa
@Strain 2.88 %,
Temperature 120 °C		6132 psi
@Strain 2.88 %,
Temperature 248 °F		ISO 11403-1/-2
 42.28 MPa
@Strain 2.07 %,
Temperature 90.0 °C		6132 psi
@Strain 2.07 %,
Temperature 194 °F		ISO 11403-1/-2
 42.3 MPa
@Strain 5.87 %,
Temperature 150 °C		6140 psi
@Strain 5.87 %,
Temperature 302 °F		ISO 11403-1/-2
 42.5 MPa
@Strain 6.10 %,
Temperature 150 °C		6160 psi
@Strain 6.10 %,
Temperature 302 °F		ISO 11403-1/-2
 43.12 MPa
@Strain 0.700 %,
Temperature 0.000 °C		6254 psi
@Strain 0.700 %,
Temperature 32.0 °F		ISO 11403-1/-2
 43.68 MPa
@Strain 3.13 %,
Temperature 120 °C		6335 psi
@Strain 3.13 %,
Temperature 248 °F		ISO 11403-1/-2
 44.0 MPa
@Strain 0.750 %,
Temperature 23.0 °C		6380 psi
@Strain 0.750 %,
Temperature 73.4 °F		ISO 11403-1/-2
 44.62 MPa
@Strain 1.09 %,
Temperature 40.0 °C		6472 psi
@Strain 1.09 %,
Temperature 104 °F		ISO 11403-1/-2
 44.87 MPa
@Strain 3.38 %,
Temperature 120 °C		6508 psi
@Strain 3.38 %,
Temperature 248 °F		ISO 11403-1/-2
 45.07 MPa
@Strain 2.30 %,
Temperature 90.0 °C		6537 psi
@Strain 2.30 %,
Temperature 194 °F		ISO 11403-1/-2
 45.8 MPa
@Strain 3.60 %,
Temperature 120 °C		6640 psi
@Strain 3.60 %,
Temperature 248 °F		ISO 11403-1/-2
 45.81 MPa
@Strain 1.74 %,
Temperature 60.0 °C		6644 psi
@Strain 1.74 %,
Temperature 140 °F		ISO 11403-1/-2
 46.73 MPa
@Strain 3.85 %,
Temperature 120 °C		6778 psi
@Strain 3.85 %,
Temperature 248 °F		ISO 11403-1/-2
 47.45 MPa
@Strain 2.54 %,
Temperature 90.0 °C		6882 psi
@Strain 2.54 %,
Temperature 194 °F		ISO 11403-1/-2
 47.51 MPa
@Strain 4.10 %,
Temperature 120 °C		6891 psi
@Strain 4.10 %,
Temperature 248 °F		ISO 11403-1/-2
 47.82 MPa
@Strain 0.760 %,
Temperature -20.0 °C		6936 psi
@Strain 0.760 %,
Temperature -4.00 °F		ISO 11403-1/-2
 48.09 MPa
@Strain 4.32 %,
Temperature 120 °C		6975 psi
@Strain 4.32 %,
Temperature 248 °F		ISO 11403-1/-2
 48.64 MPa
@Strain 4.57 %,
Temperature 120 °C		7055 psi
@Strain 4.57 %,
Temperature 248 °F		ISO 11403-1/-2
 49.11 MPa
@Strain 4.81 %,
Temperature 120 °C		7123 psi
@Strain 4.81 %,
Temperature 248 °F		ISO 11403-1/-2
 49.48 MPa
@Strain 5.04 %,
Temperature 120 °C		7176 psi
@Strain 5.04 %,
Temperature 248 °F		ISO 11403-1/-2
 49.48 MPa
@Strain 2.77 %,
Temperature 90.0 °C		7176 psi
@Strain 2.77 %,
Temperature 194 °F		ISO 11403-1/-2
 49.58 MPa
@Strain 1.95 %,
Temperature 60.0 °C		7191 psi
@Strain 1.95 %,
Temperature 140 °F		ISO 11403-1/-2
 49.71 MPa
@Strain 0.820 %,
Temperature 0.000 °C		7210 psi
@Strain 0.820 %,
Temperature 32.0 °F		ISO 11403-1/-2
 49.82 MPa
@Strain 5.29 %,
Temperature 120 °C		7226 psi
@Strain 5.29 %,
Temperature 248 °F		ISO 11403-1/-2
 50.09 MPa
@Strain 5.53 %,
Temperature 120 °C		7265 psi
@Strain 5.53 %,
Temperature 248 °F		ISO 11403-1/-2
 50.12 MPa
@Strain 1.26 %,
Temperature 40.0 °C		7269 psi
@Strain 1.26 %,
Temperature 104 °F		ISO 11403-1/-2
 50.26 MPa
@Strain 5.76 %,
Temperature 120 °C		7290 psi
@Strain 5.76 %,
Temperature 248 °F		ISO 11403-1/-2
 50.3 MPa
@Strain 6.00 %,
Temperature 120 °C		7300 psi
@Strain 6.00 %,
Temperature 248 °F		ISO 11403-1/-2
 50.69 MPa
@Strain 0.870 %,
Temperature 23.0 °C		7352 psi
@Strain 0.870 %,
Temperature 73.4 °F		ISO 11403-1/-2
 51.14 MPa
@Strain 3.00 %,
Temperature 90.0 °C		7417 psi
@Strain 3.00 %,
Temperature 194 °F		ISO 11403-1/-2
 52.51 MPa
@Strain 3.24 %,
Temperature 90.0 °C		7616 psi
@Strain 3.24 %,
Temperature 194 °F		ISO 11403-1/-2
 53.26 MPa
@Strain 2.18 %,
Temperature 60.0 °C		7725 psi
@Strain 2.18 %,
Temperature 140 °F		ISO 11403-1/-2
 53.42 MPa
@Strain 3.42 %,
Temperature 90.0 °C		7748 psi
@Strain 3.42 %,
Temperature 194 °F		ISO 11403-1/-2
 53.74 MPa
@Strain 0.870 %,
Temperature -20.0 °C		7794 psi
@Strain 0.870 %,
Temperature -4.00 °F		ISO 11403-1/-2
 54.36 MPa
@Strain 3.65 %,
Temperature 90.0 °C		7884 psi
@Strain 3.65 %,
Temperature 194 °F		ISO 11403-1/-2
 55.13 MPa
@Strain 3.89 %,
Temperature 90.0 °C		7996 psi
@Strain 3.89 %,
Temperature 194 °F		ISO 11403-1/-2
 55.67 MPa
@Strain 1.45 %,
Temperature 40.0 °C		8074 psi
@Strain 1.45 %,
Temperature 104 °F		ISO 11403-1/-2
 55.8 MPa
@Strain 4.12 %,
Temperature 90.0 °C		8090 psi
@Strain 4.12 %,
Temperature 194 °F		ISO 11403-1/-2
 56.11 MPa
@Strain 0.930 %,
Temperature 0.000 °C		8138 psi
@Strain 0.930 %,
Temperature 32.0 °F		ISO 11403-1/-2
 56.31 MPa
@Strain 2.39 %,
Temperature 60.0 °C		8167 psi
@Strain 2.39 %,
Temperature 140 °F		ISO 11403-1/-2
 56.33 MPa
@Strain 4.35 %,
Temperature 90.0 °C		8170 psi
@Strain 4.35 %,
Temperature 194 °F		ISO 11403-1/-2
 56.75 MPa
@Strain 4.59 %,
Temperature 90.0 °C		8231 psi
@Strain 4.59 %,
Temperature 194 °F		ISO 11403-1/-2
 57.1 MPa
@Strain 4.82 %,
Temperature 90.0 °C		8280 psi
@Strain 4.82 %,
Temperature 194 °F		ISO 11403-1/-2
 57.15 MPa
@Strain 1.00 %,
Temperature 23.0 °C		8289 psi
@Strain 1.00 %,
Temperature 73.4 °F		ISO 11403-1/-2
 57.37 MPa
@Strain 5.05 %,
Temperature 90.0 °C		8321 psi
@Strain 5.05 %,
Temperature 194 °F		ISO 11403-1/-2
 57.52 MPa
@Strain 5.28 %,
Temperature 90.0 °C		8343 psi
@Strain 5.28 %,
Temperature 194 °F		ISO 11403-1/-2
 57.58 MPa
@Strain 5.50 %,
Temperature 90.0 °C		8351 psi
@Strain 5.50 %,
Temperature 194 °F		ISO 11403-1/-2
 57.6 MPa
@Strain 5.70 %,
Temperature 90.0 °C		8350 psi
@Strain 5.70 %,
Temperature 194 °F		ISO 11403-1/-2
 58.92 MPa
@Strain 2.60 %,
Temperature 60.0 °C		8546 psi
@Strain 2.60 %,
Temperature 140 °F		ISO 11403-1/-2
 60.2 MPa
@Strain 0.980 %,
Temperature -20.0 °C		8730 psi
@Strain 0.980 %,
Temperature -4.00 °F		ISO 11403-1/-2
 60.22 MPa
@Strain 1.62 %,
Temperature 40.0 °C		8734 psi
@Strain 1.62 %,
Temperature 104 °F		ISO 11403-1/-2
 61.15 MPa
@Strain 2.81 %,
Temperature 60.0 °C		8869 psi
@Strain 2.81 %,
Temperature 140 °F		ISO 11403-1/-2
 62.27 MPa
@Strain 1.05 %,
Temperature 0.000 °C		9032 psi
@Strain 1.05 %,
Temperature 32.0 °F		ISO 11403-1/-2
 63.07 MPa
@Strain 3.04 %,
Temperature 60.0 °C		9148 psi
@Strain 3.04 %,
Temperature 140 °F		ISO 11403-1/-2
 63.25 MPa
@Strain 1.13 %,
Temperature 23.0 °C		9174 psi
@Strain 1.13 %,
Temperature 73.4 °F		ISO 11403-1/-2
 64.44 MPa
@Strain 3.25 %,
Temperature 60.0 °C		9346 psi
@Strain 3.25 %,
Temperature 140 °F		ISO 11403-1/-2
 64.75 MPa
@Strain 1.81 %,
Temperature 40.0 °C		9391 psi
@Strain 1.81 %,
Temperature 104 °F		ISO 11403-1/-2
 65.5 MPa
@Strain 3.46 %,
Temperature 60.0 °C		9500 psi
@Strain 3.46 %,
Temperature 140 °F		ISO 11403-1/-2
 66.29 MPa
@Strain 3.68 %,
Temperature 60.0 °C		9615 psi
@Strain 3.68 %,
Temperature 140 °F		ISO 11403-1/-2
 66.44 MPa
@Strain 1.09 %,
Temperature -20.0 °C		9636 psi
@Strain 1.09 %,
Temperature -4.00 °F		ISO 11403-1/-2
 66.98 MPa
@Strain 3.91 %,
Temperature 60.0 °C		9715 psi
@Strain 3.91 %,
Temperature 140 °F		ISO 11403-1/-2
 67.4 MPa
@Strain 4.12 %,
Temperature 60.0 °C		9780 psi
@Strain 4.12 %,
Temperature 140 °F		ISO 11403-1/-2
 67.72 MPa
@Strain 4.33 %,
Temperature 60.0 °C		9822 psi
@Strain 4.33 %,
Temperature 140 °F		ISO 11403-1/-2
 67.95 MPa
@Strain 4.54 %,
Temperature 60.0 °C		9855 psi
@Strain 4.54 %,
Temperature 140 °F		ISO 11403-1/-2
 68.1 MPa
@Strain 4.77 %,
Temperature 60.0 °C		9880 psi
@Strain 4.77 %,
Temperature 140 °F		ISO 11403-1/-2
 68.14 MPa
@Strain 4.98 %,
Temperature 60.0 °C		9883 psi
@Strain 4.98 %,
Temperature 140 °F		ISO 11403-1/-2
 68.18 MPa
@Strain 5.10 %,
Temperature 60.0 °C		9889 psi
@Strain 5.10 %,
Temperature 140 °F		ISO 11403-1/-2
 68.2 MPa
@Strain 5.40 %,
Temperature 60.0 °C		9890 psi
@Strain 5.40 %,
Temperature 140 °F		ISO 11403-1/-2
 68.31 MPa
@Strain 1.16 %,
Temperature 0.000 °C		9908 psi
@Strain 1.16 %,
Temperature 32.0 °F		ISO 11403-1/-2
 68.37 MPa
@Strain 1.98 %,
Temperature 40.0 °C		9916 psi
@Strain 1.98 %,
Temperature 104 °F		ISO 11403-1/-2
 69.15 MPa
@Strain 1.25 %,
Temperature 23.0 °C		10030 psi
@Strain 1.25 %,
Temperature 73.4 °F		ISO 11403-1/-2
 71.86 MPa
@Strain 1.19 %,
Temperature -20.0 °C		10420 psi
@Strain 1.19 %,
Temperature -4.00 °F		ISO 11403-1/-2
 71.96 MPa
@Strain 2.17 %,
Temperature 40.0 °C		10440 psi
@Strain 2.17 %,
Temperature 104 °F		ISO 11403-1/-2
 74.56 MPa
@Strain 1.29 %,
Temperature 0.000 °C		10810 psi
@Strain 1.29 %,
Temperature 32.0 °F		ISO 11403-1/-2
 74.58 MPa
@Strain 1.38 %,
Temperature 23.0 °C		10820 psi
@Strain 1.38 %,
Temperature 73.4 °F		ISO 11403-1/-2
 74.75 MPa
@Strain 2.34 %,
Temperature 40.0 °C		10840 psi
@Strain 2.34 %,
Temperature 104 °F		ISO 11403-1/-2
 77.46 MPa
@Strain 2.53 %,
Temperature 40.0 °C		11230 psi
@Strain 2.53 %,
Temperature 104 °F		ISO 11403-1/-2
 77.73 MPa
@Strain 1.30 %,
Temperature -20.0 °C		11270 psi
@Strain 1.30 %,
Temperature -4.00 °F		ISO 11403-1/-2
 79.59 MPa
@Strain 2.70 %,
Temperature 40.0 °C		11540 psi
@Strain 2.70 %,
Temperature 104 °F		ISO 11403-1/-2
 79.78 MPa
@Strain 1.50 %,
Temperature 23.0 °C		11570 psi
@Strain 1.50 %,
Temperature 73.4 °F		ISO 11403-1/-2
 80.09 MPa
@Strain 1.40 %,
Temperature 0.000 °C		11620 psi
@Strain 1.40 %,
Temperature 32.0 °F		ISO 11403-1/-2
 81.45 MPa
@Strain 2.89 %,
Temperature 40.0 °C		11810 psi
@Strain 2.89 %,
Temperature 104 °F		ISO 11403-1/-2
 82.74 MPa
@Strain 3.06 %,
Temperature 40.0 °C		12000 psi
@Strain 3.06 %,
Temperature 104 °F		ISO 11403-1/-2
 83.47 MPa
@Strain 1.41 %,
Temperature -20.0 °C		12110 psi
@Strain 1.41 %,
Temperature -4.00 °F		ISO 11403-1/-2
 83.74 MPa
@Strain 3.25 %,
Temperature 40.0 °C		12150 psi
@Strain 3.25 %,
Temperature 104 °F		ISO 11403-1/-2
 84.29 MPa
@Strain 3.42 %,
Temperature 40.0 °C		12230 psi
@Strain 3.42 %,
Temperature 104 °F		ISO 11403-1/-2
 84.59 MPa
@Strain 3.97 %,
Temperature 40.0 °C		12270 psi
@Strain 3.97 %,
Temperature 104 °F		ISO 11403-1/-2
 84.6 MPa
@Strain 4.14 %,
Temperature 40.0 °C		12300 psi
@Strain 4.14 %,
Temperature 104 °F		ISO 11403-1/-2
 84.61 MPa
@Strain 3.61 %,
Temperature 40.0 °C		12270 psi
@Strain 3.61 %,
Temperature 104 °F		ISO 11403-1/-2
 84.61 MPa
@Strain 1.63 %,
Temperature 23.0 °C		12270 psi
@Strain 1.63 %,
Temperature 73.4 °F		ISO 11403-1/-2
 84.63 MPa
@Strain 4.33 %,
Temperature 40.0 °C		12270 psi
@Strain 4.33 %,
Temperature 104 °F		ISO 11403-1/-2
 84.68 MPa
@Strain 3.78 %,
Temperature 40.0 °C		12280 psi
@Strain 3.78 %,
Temperature 104 °F		ISO 11403-1/-2
 84.7 MPa
@Strain 4.50 %,
Temperature 40.0 °C		12300 psi
@Strain 4.50 %,
Temperature 104 °F		ISO 11403-1/-2
 85.44 MPa
@Strain 1.51 %,
Temperature 0.000 °C		12390 psi
@Strain 1.51 %,
Temperature 32.0 °F		ISO 11403-1/-2
 88.42 MPa
@Strain 1.74 %,
Temperature 23.0 °C		12820 psi
@Strain 1.74 %,
Temperature 73.4 °F		ISO 11403-1/-2
 88.5 MPa
@Strain 1.51 %,
Temperature -20.0 °C		12800 psi
@Strain 1.51 %,
Temperature -4.00 °F		ISO 11403-1/-2
 90.5 MPa
@Strain 1.63 %,
Temperature 0.000 °C		13100 psi
@Strain 1.63 %,
Temperature 32.0 °F		ISO 11403-1/-2
 92.49 MPa
@Strain 1.86 %,
Temperature 23.0 °C		13410 psi
@Strain 1.86 %,
Temperature 73.4 °F		ISO 11403-1/-2
 93.74 MPa
@Strain 1.63 %,
Temperature -20.0 °C		13600 psi
@Strain 1.63 %,
Temperature -4.00 °F		ISO 11403-1/-2
 95.27 MPa
@Strain 1.74 %,
Temperature 0.000 °C		13820 psi
@Strain 1.74 %,
Temperature 32.0 °F		ISO 11403-1/-2
 96.01 MPa
@Strain 1.99 %,
Temperature 23.0 °C		13930 psi
@Strain 1.99 %,
Temperature 73.4 °F		ISO 11403-1/-2
 98.83 MPa
@Strain 1.74 %,
Temperature -20.0 °C		14330 psi
@Strain 1.74 %,
Temperature -4.00 °F		ISO 11403-1/-2
 99.15 MPa
@Strain 2.12 %,
Temperature 23.0 °C		14380 psi
@Strain 2.12 %,
Temperature 73.4 °F		ISO 11403-1/-2
 99.71 MPa
@Strain 1.86 %,
Temperature 0.000 °C		14460 psi
@Strain 1.86 %,
Temperature 32.0 °F		ISO 11403-1/-2
 101.95 MPa
@Strain 2.24 %,
Temperature 23.0 °C		14787 psi
@Strain 2.24 %,
Temperature 73.4 °F		ISO 11403-1/-2
 103.25 MPa
@Strain 1.84 %,
Temperature -20.0 °C		14975 psi
@Strain 1.84 %,
Temperature -4.00 °F		ISO 11403-1/-2
 104.24 MPa
@Strain 1.98 %,
Temperature 0.000 °C		15119 psi
@Strain 1.98 %,
Temperature 32.0 °F		ISO 11403-1/-2
 104.34 MPa
@Strain 2.37 %,
Temperature 23.0 °C		15133 psi
@Strain 2.37 %,
Temperature 73.4 °F		ISO 11403-1/-2
 106.4 MPa
@Strain 2.49 %,
Temperature 23.0 °C		15430 psi
@Strain 2.49 %,
Temperature 73.4 °F		ISO 11403-1/-2
 107.83 MPa
@Strain 1.95 %,
Temperature -20.0 °C		15639 psi
@Strain 1.95 %,
Temperature -4.00 °F		ISO 11403-1/-2
 108.07 MPa
@Strain 2.10 %,
Temperature 0.000 °C		15674 psi
@Strain 2.10 %,
Temperature 32.0 °F		ISO 11403-1/-2
 108.45 MPa
@Strain 2.62 %,
Temperature 23.0 °C		15729 psi
@Strain 2.62 %,
Temperature 73.4 °F		ISO 11403-1/-2
 109.72 MPa
@Strain 2.75 %,
Temperature 23.0 °C		15914 psi
@Strain 2.75 %,
Temperature 73.4 °F		ISO 11403-1/-2
 110.44 MPa
@Strain 2.85 %,
Temperature 23.0 °C		16018 psi
@Strain 2.85 %,
Temperature 73.4 °F		ISO 11403-1/-2
 110.85 MPa
@Strain 2.98 %,
Temperature 23.0 °C		16077 psi
@Strain 2.98 %,
Temperature 73.4 °F		ISO 11403-1/-2
 110.9 MPa
@Strain 3.10 %,
Temperature 23.0 °C		16080 psi
@Strain 3.10 %,
Temperature 73.4 °F		ISO 11403-1/-2
 111.8 MPa
@Strain 2.21 %,
Temperature 0.000 °C		16220 psi
@Strain 2.21 %,
Temperature 32.0 °F		ISO 11403-1/-2
 112.17 MPa
@Strain 2.06 %,
Temperature -20.0 °C		16269 psi
@Strain 2.06 %,
Temperature -4.00 °F		ISO 11403-1/-2
 114.97 MPa
@Strain 2.33 %,
Temperature 0.000 °C		16675 psi
@Strain 2.33 %,
Temperature 32.0 °F		ISO 11403-1/-2
 116.38 MPa
@Strain 2.16 %,
Temperature -20.0 °C		16880 psi
@Strain 2.16 %,
Temperature -4.00 °F		ISO 11403-1/-2
 118.07 MPa
@Strain 2.44 %,
Temperature 0.000 °C		17125 psi
@Strain 2.44 %,
Temperature 32.0 °F		ISO 11403-1/-2
 120.63 MPa
@Strain 2.27 %,
Temperature -20.0 °C		17496 psi
@Strain 2.27 %,
Temperature -4.00 °F		ISO 11403-1/-2
 120.8 MPa
@Strain 2.55 %,
Temperature 0.000 °C		17520 psi
@Strain 2.55 %,
Temperature 32.0 °F		ISO 11403-1/-2
 123.16 MPa
@Strain 2.67 %,
Temperature 0.000 °C		17863 psi
@Strain 2.67 %,
Temperature 32.0 °F		ISO 11403-1/-2
 124.61 MPa
@Strain 2.38 %,
Temperature -20.0 °C		18073 psi
@Strain 2.38 %,
Temperature -4.00 °F		ISO 11403-1/-2
 125.33 MPa
@Strain 2.79 %,
Temperature 0.000 °C		18178 psi
@Strain 2.79 %,
Temperature 32.0 °F		ISO 11403-1/-2
 127.29 MPa
@Strain 2.91 %,
Temperature 0.000 °C		18462 psi
@Strain 2.91 %,
Temperature 32.0 °F		ISO 11403-1/-2
 127.58 MPa
@Strain 2.49 %,
Temperature -20.0 °C		18504 psi
@Strain 2.49 %,
Temperature -4.00 °F		ISO 11403-1/-2
 130.3 MPa
@Strain 2.59 %,
Temperature -20.0 °C		18900 psi
@Strain 2.59 %,
Temperature -4.00 °F		ISO 11403-1/-2
 133.4 MPa
@Strain 2.70 %,
Temperature -20.0 °C		19350 psi
@Strain 2.70 %,
Temperature -4.00 °F		ISO 11403-1/-2
Elongation at Break  2.8 %
@Temperature -40.0 °C		2.8 %
@Temperature -40.0 °F		ISO 527
 3.5 %
@Temperature 23.0 °C		3.5 %
@Temperature 73.4 °F		ISO 527
 3.6 %
@Temperature 23.0 °C		3.6 %
@Temperature 73.4 °F		ASTM D638
 7.8 %
@Temperature 150 °C		7.8 %
@Temperature 302 °F		ISO 527
 7.9 %
@Temperature 120 °C		7.9 %
@Temperature 248 °F		ISO 527
Tensile Modulus  2.50 GPa
@Temperature 120 °C		363 ksi
@Temperature 248 °F		ISO 527
 5.80 GPa
@Temperature 23.0 °C		841 ksi
@Temperature 73.4 °F		ISO 527
 6.00 GPa
@Temperature 23.0 °C		870 ksi
@Temperature 73.4 °F		ASTM D638
 6.60 GPa
@Temperature -40.0 °C		957 ksi
@Temperature -40.0 °F		ISO 527
Flexural Strength  52.0 MPa
@Temperature 150 °C		7540 psi
@Temperature 302 °F		ISO 178
 62.0 MPa
@Temperature 120 °C		8990 psi
@Temperature 248 °F		ISO 178
 160 MPa
@Temperature 23.0 °C		23200 psi
@Temperature 73.4 °F		ASTM D790
 160 MPa
@Temperature 23.0 °C		23200 psi
@Temperature 73.4 °F		ISO 178
Flexural Modulus  2.009 GPa
@Temperature 150 °C		291.4 ksi
@Temperature 302 °F		ISO 178
 2.30 GPa
@Temperature 120 °C		334 ksi
@Temperature 248 °F		ISO 178
 5.20 GPa
@Temperature 23.0 °C		754 ksi
@Temperature 73.4 °F		ISO 178
 5.976 GPa
@Temperature 23.0 °C		866.7 ksi
@Temperature 73.4 °F		ASTM D790
Shear Modulus  0.250 GPa
@Temperature 200 °C		36.3 ksi
@Temperature 392 °F		ISO 6721
 0.274 GPa
@Temperature 190 °C		39.7 ksi
@Temperature 374 °F		ISO 6721
 0.295 GPa
@Temperature 180 °C		42.8 ksi
@Temperature 356 °F		ISO 6721
 0.311 GPa
@Temperature 170 °C		45.1 ksi
@Temperature 338 °F		ISO 6721
 0.328 GPa
@Temperature 160 °C		47.6 ksi
@Temperature 320 °F		ISO 6721
 0.343 GPa
@Temperature 150 °C		49.7 ksi
@Temperature 302 °F		ISO 6721
 0.359 GPa
@Temperature 140 °C		52.1 ksi
@Temperature 284 °F		ISO 6721
 0.376 GPa
@Temperature 130 °C		54.5 ksi
@Temperature 266 °F		ISO 6721
 0.393 GPa
@Temperature 120 °C		57.0 ksi
@Temperature 248 °F		ISO 6721
 0.412 GPa
@Temperature 110 °C		59.8 ksi
@Temperature 230 °F		ISO 6721
 0.433 GPa
@Temperature 100 °C		62.8 ksi
@Temperature 212 °F		ISO 6721
 0.460 GPa
@Temperature 90.0 °C		66.7 ksi
@Temperature 194 °F		ISO 6721
 0.501 GPa
@Temperature 80.0 °C		72.7 ksi
@Temperature 176 °F		ISO 6721
 0.568 GPa
@Temperature 70.0 °C		82.4 ksi
@Temperature 158 °F		ISO 6721
 0.679 GPa
@Temperature 60.0 °C		98.5 ksi
@Temperature 140 °F		ISO 6721
 0.993 GPa
@Temperature 50.0 °C		144 ksi
@Temperature 122 °F		ISO 6721
 1.28 GPa
@Temperature 40.0 °C		186 ksi
@Temperature 104 °F		ISO 6721
 1.36 GPa
@Temperature 30.0 °C		197 ksi
@Temperature 86.0 °F		ISO 6721
 1.42 GPa
@Temperature 20.0 °C		206 ksi
@Temperature 68.0 °F		ISO 6721
 1.47 GPa
@Temperature 10.0 °C		213 ksi
@Temperature 50.0 °F		ISO 6721
 1.52 GPa
@Temperature 0.000 °C		220 ksi
@Temperature 32.0 °F		ISO 6721
 1.54 GPa
@Temperature -10.0 °C		223 ksi
@Temperature 14.0 °F		ISO 6721
 1.56 GPa
@Temperature -20.0 °C		226 ksi
@Temperature -4.00 °F		ISO 6721
 1.61 GPa
@Temperature -40.0 °C		234 ksi
@Temperature -40.0 °F		ISO 6721
 1.61 GPa
@Temperature -30.0 °C		234 ksi
@Temperature -22.0 °F		ISO 6721
 1.62 GPa
@Temperature -50.0 °C		235 ksi
@Temperature -58.0 °F		ISO 6721
Izod Impact, Notched  0.580 J/cm
@Temperature -40.0 °C		1.09 ft-lb/in
@Temperature -40.0 °F		ASTM D256
 0.690 J/cm
@Temperature 23.0 °C		1.29 ft-lb/in
@Temperature 73.4 °F		ASTM D256
Izod Impact, Unnotched  6.45 J/cm
@Temperature -40.0 °C		12.1 ft-lb/in
@Temperature -40.0 °F		ASTM D4812
 7.04 J/cm
@Temperature 23.0 °C		13.2 ft-lb/in
@Temperature 73.4 °F		ASTM D4812
Izod Impact, Notched (ISO)  6.00 kJ/m²
@Temperature -40.0 °C		2.86 ft-lb/in²
@Temperature -40.0 °F		ISO 180/1A
 6.00 kJ/m²
@Temperature -30.0 °C		2.86 ft-lb/in²
@Temperature -22.0 °F		ISO 180/1A
 6.50 kJ/m²
@Temperature 23.0 °C		3.09 ft-lb/in²
@Temperature 73.4 °F		ISO 180/1A
Izod Impact, Unnotched (ISO)  30.0 kJ/m²
@Temperature -40.0 °C		14.3 ft-lb/in²
@Temperature -40.0 °F		ISO 180/1U
 50.0 kJ/m²
@Temperature -30.0 °C		23.8 ft-lb/in²
@Temperature -22.0 °F		ISO 180/1U
 50.0 kJ/m²
@Temperature 23.0 °C		23.8 ft-lb/in²
@Temperature 73.4 °F		ISO 180/1U
Charpy Impact Unnotched  4.00 J/cm²
@Temperature -40.0 °C		19.0 ft-lb/in²
@Temperature -40.0 °F		ISO 179/1eU
 4.50 J/cm²
@Temperature -30.0 °C		21.4 ft-lb/in²
@Temperature -22.0 °F		ISO 179/1eU
 4.50 J/cm²
@Temperature 23.0 °C		21.4 ft-lb/in²
@Temperature 73.4 °F		ISO 179/1eU
Charpy Impact, Notched  0.700 J/cm²
@Temperature -40.0 °C		3.33 ft-lb/in²
@Temperature -40.0 °F		ISO 179/1eA
 0.700 J/cm²
@Temperature -30.0 °C		3.33 ft-lb/in²
@Temperature -22.0 °F		ISO 179/1eA
 0.700 J/cm²
@Temperature 23.0 °C		3.33 ft-lb/in²
@Temperature 73.4 °F		ISO 179/1eA
Tensile Creep Modulus, 1 hour 5300 MPa
@Temperature 23.0 °C		769000 psi
@Temperature 73.4 °F		ISO 899
Tensile Creep Modulus, 1000 hours 4300 MPa
@Temperature 23.0 °C		624000 psi
@Temperature 73.4 °F		ISO 899
 
Electrical PropertiesMetricEnglishComments
Volume Resistivity  >= 1.00e+15 ohm-cm
@Temperature 23.0 °C		>= 1.00e+15 ohm-cm
@Temperature 73.4 °F		IEC 60093
 1.00e+16 ohm-cm
@Temperature 23.0 °C		1.00e+16 ohm-cm
@Temperature 73.4 °F		ASTM D257
Surface Resistance  1.00e+15 ohm
@Temperature 23.0 °C		1.00e+15 ohm
@Temperature 73.4 °F		ASTM D257
 1.00e+15 ohm
@Temperature 23.0 °C		1.00e+15 ohm
@Temperature 73.4 °F		IEC 60093
Dielectric Constant  3.5
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		3.5
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		ASTM D150
 3.5
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		3.5
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		IEC 60250
 3.7
@Frequency 1000 Hz,
Temperature 23.0 °C		3.7
@Frequency 1000 Hz,
Temperature 73.4 °F		ASTM D150
 4.1
@Frequency 100 Hz,
Temperature 23.0 °C		4.1
@Frequency 100 Hz,
Temperature 73.4 °F		IEC 60250
Dielectric Strength  17.0 kV/mm
@Thickness 3.20 mm,
Temperature 23.0 °C		432 kV/in
@Thickness 0.126 in,
Temperature 73.4 °F		Short Time; ASTM D149
 23.0 kV/mm
@Thickness 1.60 mm,
Temperature 23.0 °C		584 kV/in
@Thickness 0.0630 in,
Temperature 73.4 °F		Short Time; ASTM D149
 27.0 kV/mm
@Thickness 1.00 mm,
Temperature 23.0 °C		686 kV/in
@Thickness 0.0394 in,
Temperature 73.4 °F		IEC 60243-1
 17.0 kV/mm
@Thickness 2.00 mm,
Time 20.0 sec		432 kV/in
@Thickness 0.0787 in,
Time 0.00556 hour		IEC 60243-1
Dissipation Factor  0.0020
@Frequency 100 Hz,
Temperature 23.0 °C		0.0020
@Frequency 100 Hz,
Temperature 73.4 °F		IEC 60250
 0.0080
@Frequency 1000 Hz,
Temperature 23.0 °C		0.0080
@Frequency 1000 Hz,
Temperature 73.4 °F		ASTM D150
 0.020
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		0.020
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		ASTM D150
 0.020
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		0.020
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		IEC 60250
Comparative Tracking Index  250 V
@Temperature 23.0 °C		250 V
@Temperature 73.4 °F		UL 746A
 350 V
@Temperature 23.0 °C		350 V
@Temperature 73.4 °F		IEC 60112
 
Thermal PropertiesMetricEnglishComments
CTE, linear, Parallel to Flow  500 µm/m-°C
@Temperature 23.0 - 55.0 °C		278 µin/in-°F
@Temperature 73.4 - 131 °F		ASTM E 831
 500 µm/m-°C
@Temperature 23.0 - 55.0 °C		278 µin/in-°F
@Temperature 73.4 - 131 °F		ISO 11359-1/-2
CTE, linear, Transverse to Flow  110 µm/m-°C
@Temperature 23.0 - 55.0 °C		61.1 µin/in-°F
@Temperature 73.4 - 131 °F		ASTM E 831
 110 µm/m-°C
@Temperature 23.0 - 55.0 °C		61.1 µin/in-°F
@Temperature 73.4 - 131 °F		ISO 11359-1/-2
Melting Point 225 °C437 °FASTM D3418
Deflection Temperature at 0.46 MPa (66 psi) 220 °C428 °FISO 75-1/-2
 220 °C428 °FASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 195 °C383 °FASTM D648
 200 °C392 °FISO 75-1/-2
Deflection Temperature at 5.0 MPa 150 °C302 °F4x100x100mm plaque; ISO 75-1/-2
Deflection Temperature at 8.0 MPa 83.0 °C181 °FISO 75-1/-2
UL RTI, Electrical  130 °C
@Thickness 6.00 mm		266 °F
@Thickness 0.236 in		UL 746B
 130 °C
@Thickness 1.50 mm		266 °F
@Thickness 0.0591 in		UL 746B
 130 °C
@Thickness 0.750 mm		266 °F
@Thickness 0.0295 in		UL 746B
 130 °C
@Thickness 3.00 mm		266 °F
@Thickness 0.118 in		UL 746B
UL RTI, Mechanical with Impact  115 °C
@Thickness 1.50 mm		239 °F
@Thickness 0.0591 in		UL 746B
 115 °C
@Thickness 0.750 mm		239 °F
@Thickness 0.0295 in		UL 746B
 115 °C
@Thickness 3.00 mm		239 °F
@Thickness 0.118 in		UL 746B
 115 °C
@Thickness 6.00 mm		239 °F
@Thickness 0.236 in		UL 746B
UL RTI, Mechanical without Impact  120 °C
@Thickness 3.00 mm		248 °F
@Thickness 0.118 in		UL 746B
 120 °C
@Thickness 1.50 mm		248 °F
@Thickness 0.0591 in		UL 746B
 120 °C
@Thickness 0.750 mm		248 °F
@Thickness 0.0295 in		UL 746B
 120 °C
@Thickness 6.00 mm		248 °F
@Thickness 0.236 in		UL 746B
Flammability, UL94  HB
@Thickness 6.00 mm		HB
@Thickness 0.236 in		IEC 60695-11-10
 HB
@Thickness 1.50 mm		HB
@Thickness 0.0591 in		IEC 60695-11-10
 HB
@Thickness 3.00 mm		HB
@Thickness 0.118 in		IEC 60695-11-10
 HB
@Thickness 1.50 mm		HB
@Thickness 0.0591 in		UL94
 HB
@Thickness 3.00 mm		HB
@Thickness 0.118 in		UL94
 HB
@Thickness 6.00 mm		HB
@Thickness 0.236 in		UL94
Oxygen Index 19 %19 %ASTM D2863
 19 %19 %ISO 4589-1/-2
Glow Wire Test 750 °C
@Thickness 3.00 mm		1380 °F
@Thickness 0.118 in		IEC 60695-2-12
 
Processing PropertiesMetricEnglishComments
Melt Temperature 225 °C437 °F10°C/min; ISO 11357-1/-3
 250 °C482 °FOptimum
 240 - 260 °C464 - 500 °F
Mold Temperature 80.0 °C176 °Foptimum
 30.0 - 130 °C86.0 - 266 °F
Drying Temperature 110 - 130 °C230 - 266 °F
Dry Time 2.00 - 4.00 hour2.00 - 4.00 hour
Moisture Content <= 0.040 %<= 0.040 %
 
Descriptive Properties
AdditiveLubricant
AppearanceNatural Color
Drying RecommendedYes
FeaturesChemical Resistance, Good
 Dimensional Stability, Good
 Lubricated
 Moisture Absorption, Low
 Processability, Good
 Stiffness, Good
 Strength, Good
FillerGlass fiber reinforcement
FormsPellets
GenericPBT
Material StatusCurrent
Part Marking Code>PBT-GF15<ISO 11469
Polymer FamilyPolyester
Polymer TypePBT
Processing MethodInjection Molding
Product CategoryGlass Reinforced Resins
Region Available - GlobalYes
Resin IdentificationPBT-GF15ISO 1043
RoHS ComplianceContact Manufacturer
Ultrasonic WeldableYes
UsesAutomotive Applications
 General Purpose
 Industrial Applications
 Parts, Engineering
 Parts, Machine/Mechanical
 Structural Parts

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-38088.html

免责声明: 本文 DuPont Performance Polymers Crastin® SK602 NC010 PBT 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他物性信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4