DuPont Performance Polymers Crastin® SK601 NC010 PBT 物性表: DuPont Performance Polymers Crastin® SK601 NC010 PBT物性表及特性介绍,DuPont Performance Polymers Crastin® SK601 NC010 PBT注塑参数详情,如需DuPont Performance Polymers Crastin® SK601 NC010 PBT下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.37
  • 吸水率 [%]: 0.2
  • 缺口冲击强度: 4.5
  • 热变形温度 [℃]: 215.0
 
Physical PropertiesMetricEnglishComments
Density 1.37 g/cc0.0495 lb/in³ISO 1183
Filler Content 10 %10 %
Water Absorption  0.20 %
@Temperature 23.0 °C		0.20 %
@Temperature 73.4 °F		Equilibrium 50%RH; ISO 62, Similar to
 0.40 %
@Temperature 23.0 °C		0.40 %
@Temperature 73.4 °F		Saturation, immersed; ISO 62, Similar to
Linear Mold Shrinkage, Flow 0.0080 cm/cm0.0080 in/inParallel; Annealed; ISO 294-4
 0.0070 cm/cm
@Thickness 2.00 mm		0.0070 in/in
@Thickness 0.0787 in		Parallel; ISO 294-4
Linear Mold Shrinkage, Transverse 0.0145 cm/cm0.0145 in/inNormal; Annealed; ISO 294-4
 0.012 cm/cm
@Thickness 2.00 mm		0.012 in/in
@Thickness 0.0787 in		Normal; ISO 294-4
Melt Index of Compound 15 g/10 min
@Load 2.16 kg,
Temperature 250 °C		15 g/10 min
@Load 4.76 lb,
Temperature 482 °F		cm3/10 min; ISO 1133
 
Mechanical PropertiesMetricEnglishComments
Tensile Strength at Break 90.0 MPa
@Temperature 23.0 °C		13100 psi
@Temperature 73.4 °F		ISO 527
Tensile Stress  3.06 MPa
@Strain 0.250 %,
Temperature 160 °C		444 psi
@Strain 0.250 %,
Temperature 320 °F		ISO 527
 3.75 MPa
@Strain 0.250 %,
Temperature 120 °C		544 psi
@Strain 0.250 %,
Temperature 248 °F		ISO 527
 4.15 MPa
@Strain 0.250 %,
Temperature 100 °C		602 psi
@Strain 0.250 %,
Temperature 212 °F		ISO 527
 4.50 MPa
@Strain 0.250 %,
Temperature 80.0 °C		653 psi
@Strain 0.250 %,
Temperature 176 °F		ISO 527
 5.50 MPa
@Strain 0.250 %,
Temperature 60.0 °C		798 psi
@Strain 0.250 %,
Temperature 140 °F		ISO 527
 5.85 MPa
@Strain 0.500 %,
Temperature 160 °C		848 psi
@Strain 0.500 %,
Temperature 320 °F		ISO 527
 7.29 MPa
@Strain 0.500 %,
Temperature 120 °C		1060 psi
@Strain 0.500 %,
Temperature 248 °F		ISO 527
 8.16 MPa
@Strain 0.500 %,
Temperature 100 °C		1180 psi
@Strain 0.500 %,
Temperature 212 °F		ISO 527
 8.55 MPa
@Strain 0.250 %,
Temperature 40.0 °C		1240 psi
@Strain 0.250 %,
Temperature 104 °F		ISO 527
 8.76 MPa
@Strain 0.500 %,
Temperature 80.0 °C		1270 psi
@Strain 0.500 %,
Temperature 176 °F		ISO 527
 10.7 MPa
@Strain 1.00 %,
Temperature 160 °C		1550 psi
@Strain 1.00 %,
Temperature 320 °F		ISO 527
 10.9 MPa
@Strain 0.500 %,
Temperature 60.0 °C		1580 psi
@Strain 0.500 %,
Temperature 140 °F		ISO 527
 11.1 MPa
@Strain 0.250 %,
Temperature 23.0 °C		1610 psi
@Strain 0.250 %,
Temperature 73.4 °F		ISO 527
 12.1 MPa
@Strain 0.250 %,
Temperature 0.000 °C		1750 psi
@Strain 0.250 %,
Temperature 32.0 °F		ISO 527
 13.2 MPa
@Strain 0.250 %,
Temperature -20.0 °C		1910 psi
@Strain 0.250 %,
Temperature -4.00 °F		ISO 527
 13.7 MPa
@Strain 1.00 %,
Temperature 120 °C		1990 psi
@Strain 1.00 %,
Temperature 248 °F		ISO 527
 13.7 MPa
@Strain 0.250 %,
Temperature -40.0 °C		1990 psi
@Strain 0.250 %,
Temperature -40.0 °F		ISO 527
 14.5 MPa
@Strain 1.50 %,
Temperature 160 °C		2100 psi
@Strain 1.50 %,
Temperature 320 °F		ISO 527
 15.6 MPa
@Strain 1.00 %,
Temperature 100 °C		2260 psi
@Strain 1.00 %,
Temperature 212 °F		ISO 527
 16.6 MPa
@Strain 1.00 %,
Temperature 80.0 °C		2410 psi
@Strain 1.00 %,
Temperature 176 °F		ISO 527
 16.9 MPa
@Strain 0.500 %,
Temperature 40.0 °C		2450 psi
@Strain 0.500 %,
Temperature 104 °F		ISO 527
 17.6 MPa
@Strain 2.00 %,
Temperature 160 °C		2550 psi
@Strain 2.00 %,
Temperature 320 °F		ISO 527
 19.0 MPa
@Strain 1.50 %,
Temperature 120 °C		2760 psi
@Strain 1.50 %,
Temperature 248 °F		ISO 527
 19.9 MPa
@Strain 2.50 %,
Temperature 160 °C		2890 psi
@Strain 2.50 %,
Temperature 320 °F		ISO 527
 21.2 MPa
@Strain 1.00 %,
Temperature 60.0 °C		3070 psi
@Strain 1.00 %,
Temperature 140 °F		ISO 527
 21.6 MPa
@Strain 3.00 %,
Temperature 160 °C		3130 psi
@Strain 3.00 %,
Temperature 320 °F		ISO 527
 21.9 MPa
@Strain 0.500 %,
Temperature 23.0 °C		3180 psi
@Strain 0.500 %,
Temperature 73.4 °F		ISO 527
 22.0 MPa
@Strain 1.50 %,
Temperature 100 °C		3190 psi
@Strain 1.50 %,
Temperature 212 °F		ISO 527
 22.9 MPa
@Strain 3.50 %,
Temperature 160 °C		3320 psi
@Strain 3.50 %,
Temperature 320 °F		Break; ISO 527
 23.4 MPa
@Strain 2.00 %,
Temperature 120 °C		3390 psi
@Strain 2.00 %,
Temperature 248 °F		ISO 527
 23.5 MPa
@Strain 1.50 %,
Temperature 80.0 °C		3410 psi
@Strain 1.50 %,
Temperature 176 °F		ISO 527
 24.2 MPa
@Strain 0.500 %,
Temperature 0.000 °C		3510 psi
@Strain 0.500 %,
Temperature 32.0 °F		ISO 527
 26.2 MPa
@Strain 0.500 %,
Temperature -20.0 °C		3800 psi
@Strain 0.500 %,
Temperature -4.00 °F		ISO 527
 26.8 MPa
@Strain 2.50 %,
Temperature 120 °C		3890 psi
@Strain 2.50 %,
Temperature 248 °F		ISO 527
 27.1 MPa
@Strain 0.500 %,
Temperature -40.0 °C		3930 psi
@Strain 0.500 %,
Temperature -40.0 °F		ISO 527
 27.3 MPa
@Strain 2.00 %,
Temperature 100 °C		3960 psi
@Strain 2.00 %,
Temperature 212 °F		ISO 527
 29.4 MPa
@Strain 3.00 %,
Temperature 120 °C		4260 psi
@Strain 3.00 %,
Temperature 248 °F		ISO 527
 29.6 MPa
@Strain 2.00 %,
Temperature 80.0 °C		4290 psi
@Strain 2.00 %,
Temperature 176 °F		ISO 527
 30.2 MPa
@Strain 1.50 %,
Temperature 60.0 °C		4380 psi
@Strain 1.50 %,
Temperature 140 °F		ISO 527
 31.3 MPa
@Strain 3.50 %,
Temperature 120 °C		4540 psi
@Strain 3.50 %,
Temperature 248 °F		Break; ISO 527
 31.4 MPa
@Strain 2.50 %,
Temperature 100 °C		4550 psi
@Strain 2.50 %,
Temperature 212 °F		ISO 527
 32.5 MPa
@Strain 1.00 %,
Temperature 40.0 °C		4710 psi
@Strain 1.00 %,
Temperature 104 °F		ISO 527
 34.4 MPa
@Strain 3.00 %,
Temperature 100 °C		4990 psi
@Strain 3.00 %,
Temperature 212 °F		ISO 527
 35.0 MPa
@Strain 2.50 %,
Temperature 80.0 °C		5080 psi
@Strain 2.50 %,
Temperature 176 °F		ISO 527
 36.5 MPa
@Strain 3.50 %,
Temperature 100 °C		5290 psi
@Strain 3.50 %,
Temperature 212 °F		Break; ISO 527
 37.7 MPa
@Strain 2.00 %,
Temperature 60.0 °C		5470 psi
@Strain 2.00 %,
Temperature 140 °F		ISO 527
 39.6 MPa
@Strain 3.00 %,
Temperature 80.0 °C		5740 psi
@Strain 3.00 %,
Temperature 176 °F		ISO 527
 41.8 MPa
@Strain 1.00 %,
Temperature 23.0 °C		6060 psi
@Strain 1.00 %,
Temperature 73.4 °F		ISO 527
 43.6 MPa
@Strain 2.50 %,
Temperature 60.0 °C		6320 psi
@Strain 2.50 %,
Temperature 140 °F		ISO 527
 43.7 MPa
@Strain 3.50 %,
Temperature 80.0 °C		6340 psi
@Strain 3.50 %,
Temperature 176 °F		Break; ISO 527
 45.5 MPa
@Strain 1.50 %,
Temperature 40.0 °C		6600 psi
@Strain 1.50 %,
Temperature 104 °F		ISO 527
 47.9 MPa
@Strain 1.00 %,
Temperature 0.000 °C		6950 psi
@Strain 1.00 %,
Temperature 32.0 °F		ISO 527
 48.0 MPa
@Strain 3.00 %,
Temperature 60.0 °C		6960 psi
@Strain 3.00 %,
Temperature 140 °F		ISO 527
 50.9 MPa
@Strain 1.00 %,
Temperature -20.0 °C		7380 psi
@Strain 1.00 %,
Temperature -4.00 °F		ISO 527
 51.0 MPa
@Strain 3.50 %,
Temperature 60.0 °C		7400 psi
@Strain 3.50 %,
Temperature 140 °F		Break; ISO 527
 52.5 MPa
@Strain 1.00 %,
Temperature -40.0 °C		7610 psi
@Strain 1.00 %,
Temperature -40.0 °F		ISO 527
 55.5 MPa
@Strain 2.00 %,
Temperature 40.0 °C		8050 psi
@Strain 2.00 %,
Temperature 104 °F		ISO 527
 59.5 MPa
@Strain 1.50 %,
Temperature 23.0 °C		8630 psi
@Strain 1.50 %,
Temperature 73.4 °F		ISO 527
 62.6 MPa
@Strain 2.50 %,
Temperature 40.0 °C		9080 psi
@Strain 2.50 %,
Temperature 104 °F		ISO 527
 67.0 MPa
@Strain 3.00 %,
Temperature 40.0 °C		9720 psi
@Strain 3.00 %,
Temperature 104 °F		ISO 527
 69.2 MPa
@Strain 1.50 %,
Temperature 0.000 °C		10000 psi
@Strain 1.50 %,
Temperature 32.0 °F		ISO 527
 69.3 MPa
@Strain 3.50 %,
Temperature 40.0 °C		10100 psi
@Strain 3.50 %,
Temperature 104 °F		Break; ISO 527
 72.9 MPa
@Strain 1.50 %,
Temperature -20.0 °C		10600 psi
@Strain 1.50 %,
Temperature -4.00 °F		ISO 527
 74.0 MPa
@Strain 2.00 %,
Temperature 23.0 °C		10700 psi
@Strain 2.00 %,
Temperature 73.4 °F		ISO 527
 75.0 MPa
@Strain 1.50 %,
Temperature -40.0 °C		10900 psi
@Strain 1.50 %,
Temperature -40.0 °F		ISO 527
 84.4 MPa
@Strain 2.50 %,
Temperature 23.0 °C		12200 psi
@Strain 2.50 %,
Temperature 73.4 °F		ISO 527
 87.1 MPa
@Strain 2.00 %,
Temperature 0.000 °C		12600 psi
@Strain 2.00 %,
Temperature 32.0 °F		ISO 527
 90.2 MPa
@Strain 3.00 %,
Temperature 23.0 °C		13100 psi
@Strain 3.00 %,
Temperature 73.4 °F		ISO 527
 91.0 MPa
@Strain 3.70 %,
Temperature 23.0 °C		13200 psi
@Strain 3.70 %,
Temperature 73.4 °F		Break; ISO 527
 91.0 MPa
@Strain 2.00 %,
Temperature -20.0 °C		13200 psi
@Strain 2.00 %,
Temperature -4.00 °F		ISO 527
 93.9 MPa
@Strain 2.00 %,
Temperature -40.0 °C		13600 psi
@Strain 2.00 %,
Temperature -40.0 °F		ISO 527
 103 MPa
@Strain 2.60 %,
Temperature 0.000 °C		14900 psi
@Strain 2.60 %,
Temperature 32.0 °F		Break; ISO 527
 107 MPa
@Strain 2.60 %,
Temperature -20.0 °C		15500 psi
@Strain 2.60 %,
Temperature -4.00 °F		Break; ISO 527
 112 MPa
@Strain 2.60 %,
Temperature -40.0 °C		16200 psi
@Strain 2.60 %,
Temperature -40.0 °F		Break; ISO 527
Elongation at Break 4.7 %
@Temperature 23.0 °C		4.7 %
@Temperature 73.4 °F		ISO 527
Tensile Modulus 4.50 GPa
@Temperature 23.0 °C		653 ksi
@Temperature 73.4 °F		ISO 527
Flexural Strength 140 MPa
@Temperature 23.0 °C		20300 psi
@Temperature 73.4 °F		ISO 178
Shear Modulus  0.219 GPa
@Temperature 200 °C		31.8 ksi
@Temperature 392 °F		ISO 6721
 0.241 GPa
@Temperature 190 °C		35.0 ksi
@Temperature 374 °F		ISO 6721
 0.260 GPa
@Temperature 180 °C		37.7 ksi
@Temperature 356 °F		ISO 6721
 0.274 GPa
@Temperature 170 °C		39.7 ksi
@Temperature 338 °F		ISO 6721
 0.288 GPa
@Temperature 160 °C		41.8 ksi
@Temperature 320 °F		ISO 6721
 0.307 GPa
@Temperature 150 °C		44.5 ksi
@Temperature 302 °F		ISO 6721
 0.317 GPa
@Temperature 140 °C		46.0 ksi
@Temperature 284 °F		ISO 6721
 0.333 GPa
@Temperature 130 °C		48.3 ksi
@Temperature 266 °F		ISO 6721
 0.340 GPa
@Temperature 120 °C		49.3 ksi
@Temperature 248 °F		ISO 6721
 0.360 GPa
@Temperature 110 °C		52.2 ksi
@Temperature 230 °F		ISO 6721
 0.379 GPa
@Temperature 100 °C		55.0 ksi
@Temperature 212 °F		ISO 6721
 0.405 GPa
@Temperature 90.0 °C		58.7 ksi
@Temperature 194 °F		ISO 6721
 0.446 GPa
@Temperature 80.0 °C		64.7 ksi
@Temperature 176 °F		ISO 6721
 0.513 GPa
@Temperature 70.0 °C		74.4 ksi
@Temperature 158 °F		ISO 6721
 0.626 GPa
@Temperature 60.0 °C		90.8 ksi
@Temperature 140 °F		ISO 6721
 0.929 GPa
@Temperature 50.0 °C		135 ksi
@Temperature 122 °F		ISO 6721
 1.12 GPa
@Temperature 40.0 °C		162 ksi
@Temperature 104 °F		ISO 6721
 1.20 GPa
@Temperature 30.0 °C		174 ksi
@Temperature 86.0 °F		ISO 6721
 1.24 GPa
@Temperature 20.0 °C		180 ksi
@Temperature 68.0 °F		ISO 6721
 1.27 GPa
@Temperature 10.0 °C		184 ksi
@Temperature 50.0 °F		ISO 6721
 1.30 GPa
@Temperature 0.000 °C		189 ksi
@Temperature 32.0 °F		ISO 6721
 1.32 GPa
@Temperature -10.0 °C		191 ksi
@Temperature 14.0 °F		ISO 6721
 1.35 GPa
@Temperature -20.0 °C		196 ksi
@Temperature -4.00 °F		ISO 6721
 1.38 GPa
@Temperature -30.0 °C		200 ksi
@Temperature -22.0 °F		ISO 6721
 1.46 GPa
@Temperature -40.0 °C		212 ksi
@Temperature -40.0 °F		ISO 6721
 1.49 GPa
@Temperature -50.0 °C		216 ksi
@Temperature -58.0 °F		ISO 6721
Izod Impact, Notched (ISO)  4.50 kJ/m²
@Temperature 23.0 °C		2.14 ft-lb/in²
@Temperature 73.4 °F		ISO 180/1A
 5.00 kJ/m²
@Temperature -30.0 °C		2.38 ft-lb/in²
@Temperature -22.0 °F		ISO 180/1A
Izod Impact, Unnotched (ISO)  26.0 kJ/m²
@Temperature -30.0 °C		12.4 ft-lb/in²
@Temperature -22.0 °F		ISO 180/1U
 27.0 kJ/m²
@Temperature 23.0 °C		12.8 ft-lb/in²
@Temperature 73.4 °F		ISO 180/1U
Charpy Impact Unnotched  3.50 J/cm²
@Temperature 23.0 °C		16.7 ft-lb/in²
@Temperature 73.4 °F		ISO 179/1eU
 4.00 J/cm²
@Temperature -30.0 °C		19.0 ft-lb/in²
@Temperature -22.0 °F		ISO 179/1eU
Charpy Impact, Notched  0.600 J/cm²
@Temperature -30.0 °C		2.86 ft-lb/in²
@Temperature -22.0 °F		ISO 179/1eA
 0.600 J/cm²
@Temperature 23.0 °C		2.86 ft-lb/in²
@Temperature 73.4 °F		ISO 179/1eA
Tensile Creep Modulus, 1 hour 4000 MPa
@Temperature 23.0 °C		580000 psi
@Temperature 73.4 °F		ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 23.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 73.4 °F		1h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 60.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 140 °F		10h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 60.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 140 °F		1h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 23.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 73.4 °F		10h; Isochronous; ISO 899
 5.00 MPa
@Strain 0.267 %,
Temperature 60.0 °C		725 psi
@Strain 0.267 %,
Temperature 140 °F		1h; Isochronous; ISO 899
 5.00 MPa
@Strain 0.275 %,
Temperature 60.0 °C		725 psi
@Strain 0.275 %,
Temperature 140 °F		10h; Isochronous; ISO 899
 10.0 MPa
@Strain 0.551 %,
Temperature 60.0 °C		1450 psi
@Strain 0.551 %,
Temperature 140 °F		10h; Isochronous; ISO 899
 10.0 MPa
@Strain 0.250 %,
Temperature 23.0 °C		1450 psi
@Strain 0.250 %,
Temperature 73.4 °F		1h; Isochronous; ISO 899
 10.0 MPa
@Strain 0.530 %,
Temperature 60.0 °C		1450 psi
@Strain 0.530 %,
Temperature 140 °F		1h; Isochronous; ISO 899
 10.0 MPa
@Strain 0.270 %,
Temperature 23.0 °C		1450 psi
@Strain 0.270 %,
Temperature 73.4 °F		10h; Isochronous; ISO 899
 15.0 MPa
@Strain 0.798 %,
Temperature 60.0 °C		2180 psi
@Strain 0.798 %,
Temperature 140 °F		1h; Isochronous; ISO 899
 15.0 MPa
@Strain 0.834 %,
Temperature 60.0 °C		2180 psi
@Strain 0.834 %,
Temperature 140 °F		10h; Isochronous; ISO 899
 20.0 MPa
@Strain 1.14 %,
Temperature 60.0 °C		2900 psi
@Strain 1.14 %,
Temperature 140 °F		10h; Isochronous; ISO 899
 20.0 MPa
@Strain 0.498 %,
Temperature 23.0 °C		2900 psi
@Strain 0.498 %,
Temperature 73.4 °F		1h; Isochronous; ISO 899
 20.0 MPa
@Strain 1.08 %,
Temperature 60.0 °C		2900 psi
@Strain 1.08 %,
Temperature 140 °F		1h; Isochronous; ISO 899
 20.0 MPa
@Strain 0.544 %,
Temperature 23.0 °C		2900 psi
@Strain 0.544 %,
Temperature 73.4 °F		10h; Isochronous; ISO 899
 25.0 MPa
@Strain 1.39 %,
Temperature 60.0 °C		3630 psi
@Strain 1.39 %,
Temperature 140 °F		1h; Isochronous; ISO 899
 25.0 MPa
@Strain 1.47 %,
Temperature 60.0 °C		3630 psi
@Strain 1.47 %,
Temperature 140 °F		10h; Isochronous; ISO 899
 30.0 MPa
@Strain 1.86 %,
Temperature 60.0 °C		4350 psi
@Strain 1.86 %,
Temperature 140 °F		10h; Isochronous; ISO 899
 30.0 MPa
@Strain 0.756 %,
Temperature 23.0 °C		4350 psi
@Strain 0.756 %,
Temperature 73.4 °F		1h; Isochronous; ISO 899
 30.0 MPa
@Strain 1.76 %,
Temperature 60.0 °C		4350 psi
@Strain 1.76 %,
Temperature 140 °F		1h; Isochronous; ISO 899
 30.0 MPa
@Strain 0.835 %,
Temperature 23.0 °C		4350 psi
@Strain 0.835 %,
Temperature 73.4 °F		10h; Isochronous; ISO 899
 35.0 MPa
@Strain 2.24 %,
Temperature 60.0 °C		5080 psi
@Strain 2.24 %,
Temperature 140 °F		1h; Break; Isochronous; ISO 899
 35.0 MPa
@Strain 2.37 %,
Temperature 60.0 °C		5080 psi
@Strain 2.37 %,
Temperature 140 °F		10h; Break; Isochronous; ISO 899
 40.0 MPa
@Strain 1.04 %,
Temperature 23.0 °C		5800 psi
@Strain 1.04 %,
Temperature 73.4 °F		1h; Isochronous; ISO 899
 40.0 MPa
@Strain 1.17 %,
Temperature 23.0 °C		5800 psi
@Strain 1.17 %,
Temperature 73.4 °F		10h; Isochronous; ISO 899
 50.0 MPa
@Strain 1.59 %,
Temperature 23.0 °C		7250 psi
@Strain 1.59 %,
Temperature 73.4 °F		10h; Isochronous; ISO 899
 50.0 MPa
@Strain 1.40 %,
Temperature 23.0 °C		7250 psi
@Strain 1.40 %,
Temperature 73.4 °F		1h; Isochronous; ISO 899
 60.0 MPa
@Strain 2.00 %,
Temperature 23.0 °C		8700 psi
@Strain 2.00 %,
Temperature 73.4 °F		1h; Break; Isochronous; ISO 899
 60.0 MPa
@Strain 2.35 %,
Temperature 23.0 °C		8700 psi
@Strain 2.35 %,
Temperature 73.4 °F		10h; Break; Isochronous; ISO 899
Tensile Creep Modulus, 1000 hours 2500 MPa
@Temperature 23.0 °C		363000 psi
@Temperature 73.4 °F		ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 23.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 73.4 °F		1000h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 60.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 140 °F		100h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 23.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 73.4 °F		100h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 60.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 140 °F		1000h; Isochronous; ISO 899
 5.00 MPa
@Strain 0.310 %,
Temperature 60.0 °C		725 psi
@Strain 0.310 %,
Temperature 140 °F		1000h; Isochronous; ISO 899
 5.00 MPa
@Strain 0.294 %,
Temperature 60.0 °C		725 psi
@Strain 0.294 %,
Temperature 140 °F		100h; Isochronous; ISO 899
 10.0 MPa
@Strain 0.581 %,
Temperature 60.0 °C		1450 psi
@Strain 0.581 %,
Temperature 140 °F		100h; Isochronous; ISO 899
 10.0 MPa
@Strain 0.611 %,
Temperature 60.0 °C		1450 psi
@Strain 0.611 %,
Temperature 140 °F		1000h; Isochronous; ISO 899
 10.0 MPa
@Strain 0.298 %,
Temperature 23.0 °C		1450 psi
@Strain 0.298 %,
Temperature 73.4 °F		100h; Isochronous; ISO 899
 10.0 MPa
@Strain 0.398 %,
Temperature 23.0 °C		1450 psi
@Strain 0.398 %,
Temperature 73.4 °F		1000h; Isochronous; ISO 899
 15.0 MPa
@Strain 0.915 %,
Temperature 60.0 °C		2180 psi
@Strain 0.915 %,
Temperature 140 °F		1000h; Isochronous; ISO 899
 15.0 MPa
@Strain 0.871 %,
Temperature 60.0 °C		2180 psi
@Strain 0.871 %,
Temperature 140 °F		100h; Isochronous; ISO 899
 20.0 MPa
@Strain 1.18 %,
Temperature 60.0 °C		2900 psi
@Strain 1.18 %,
Temperature 140 °F		100h; Isochronous; ISO 899
 20.0 MPa
@Strain 1.24 %,
Temperature 60.0 °C		2900 psi
@Strain 1.24 %,
Temperature 140 °F		1000h; Isochronous; ISO 899
 20.0 MPa
@Strain 0.615 %,
Temperature 23.0 °C		2900 psi
@Strain 0.615 %,
Temperature 73.4 °F		100h; Isochronous; ISO 899
 20.0 MPa
@Strain 0.807 %,
Temperature 23.0 °C		2900 psi
@Strain 0.807 %,
Temperature 73.4 °F		1000h; Isochronous; ISO 899
 25.0 MPa
@Strain 1.59 %,
Temperature 60.0 °C		3630 psi
@Strain 1.59 %,
Temperature 140 °F		1000h; Isochronous; ISO 899
 25.0 MPa
@Strain 1.52 %,
Temperature 60.0 °C		3630 psi
@Strain 1.52 %,
Temperature 140 °F		100h; Isochronous; ISO 899
 30.0 MPa
@Strain 1.93 %,
Temperature 60.0 °C		4350 psi
@Strain 1.93 %,
Temperature 140 °F		100h; Isochronous; ISO 899
 30.0 MPa
@Strain 2.03 %,
Temperature 60.0 °C		4350 psi
@Strain 2.03 %,
Temperature 140 °F		1000h; Isochronous; ISO 899
 30.0 MPa
@Strain 0.966 %,
Temperature 23.0 °C		4350 psi
@Strain 0.966 %,
Temperature 73.4 °F		100h; Isochronous; ISO 899
 30.0 MPa
@Strain 1.25 %,
Temperature 23.0 °C		4350 psi
@Strain 1.25 %,
Temperature 73.4 °F		1000h; Isochronous; ISO 899
 35.0 MPa
@Strain 2.67 %,
Temperature 60.0 °C		5080 psi
@Strain 2.67 %,
Temperature 140 °F		1000h; Break; Isochronous; ISO 899
 35.0 MPa
@Strain 2.52 %,
Temperature 60.0 °C		5080 psi
@Strain 2.52 %,
Temperature 140 °F		100h; Break; Isochronous; ISO 899
 40.0 MPa
@Strain 1.38 %,
Temperature 23.0 °C		5800 psi
@Strain 1.38 %,
Temperature 73.4 °F		100h; Isochronous; ISO 899
 40.0 MPa
@Strain 1.75 %,
Temperature 23.0 °C		5800 psi
@Strain 1.75 %,
Temperature 73.4 °F		1000h; Isochronous; ISO 899
 50.0 MPa
@Strain 1.90 %,
Temperature 23.0 °C		7250 psi
@Strain 1.90 %,
Temperature 73.4 °F		100h; Isochronous; ISO 899
 50.0 MPa
@Strain 2.39 %,
Temperature 23.0 °C		7250 psi
@Strain 2.39 %,
Temperature 73.4 °F		1000h; Isochronous; ISO 899
 60.0 MPa
@Strain 3.46 %,
Temperature 23.0 °C		8700 psi
@Strain 3.46 %,
Temperature 73.4 °F		1000h; Break; Isochronous; ISO 899
 60.0 MPa
@Strain 2.75 %,
Temperature 23.0 °C		8700 psi
@Strain 2.75 %,
Temperature 73.4 °F		100h; Break; Isochronous; ISO 899
 
Electrical PropertiesMetricEnglishComments
Volume Resistivity >= 1.00e+15 ohm-cm
@Temperature 23.0 °C		>= 1.00e+15 ohm-cm
@Temperature 73.4 °F		IEC 60093
Surface Resistance >= 1.00e+14 ohm
@Temperature 23.0 °C		>= 1.00e+14 ohm
@Temperature 73.4 °F		IEC 60093
Dielectric Constant  3.5
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		3.5
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		IEC 60250
 3.9
@Frequency 100 Hz,
Temperature 23.0 °C		3.9
@Frequency 100 Hz,
Temperature 73.4 °F		IEC 60250
 3.9
@Frequency 50.0 Hz,
Temperature 23.0 °C		3.9
@Frequency 50.0 Hz,
Temperature 73.4 °F		IEC 60250
Dielectric Strength 30.0 kV/mm
@Thickness 1.00 mm,
Temperature 23.0 °C		762 kV/in
@Thickness 0.0394 in,
Temperature 73.4 °F		IEC 60243-1
 17.0 kV/mm
@Thickness 2.00 mm,
Time 20.0 sec		432 kV/in
@Thickness 0.0787 in,
Time 0.00556 hour		IEC 60243-1
Dissipation Factor  0.0020
@Frequency 100 Hz,
Temperature 23.0 °C		0.0020
@Frequency 100 Hz,
Temperature 73.4 °F		IEC 60250
 0.0020
@Frequency 50.0 Hz,
Temperature 23.0 °C		0.0020
@Frequency 50.0 Hz,
Temperature 73.4 °F		IEC 60250
 0.020
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C		0.020
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F		IEC 60250
Comparative Tracking Index  250 V
@Temperature 23.0 °C		250 V
@Temperature 73.4 °F		UL 746A
 300 V
@Temperature 23.0 °C		300 V
@Temperature 73.4 °F		IEC 60112
 
Thermal PropertiesMetricEnglishComments
CTE, linear, Parallel to Flow  500 µm/m-°C
@Temperature 23.0 - 55.0 °C		278 µin/in-°F
@Temperature 73.4 - 131 °F		ASTM E 831
 500 µm/m-°C
@Temperature 23.0 - 55.0 °C		278 µin/in-°F
@Temperature 73.4 - 131 °F		ISO 11359-1/-2
CTE, linear, Transverse to Flow  120 µm/m-°C
@Temperature 23.0 - 55.0 °C		66.7 µin/in-°F
@Temperature 73.4 - 131 °F		ASTM E 831
 120 µm/m-°C
@Temperature 23.0 - 55.0 °C		66.7 µin/in-°F
@Temperature 73.4 - 131 °F		ISO 11359-1/-2
Deflection Temperature at 0.46 MPa (66 psi) 215 °C419 °FISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 175 °C347 °FISO 75-1/-2
Deflection Temperature at 5.0 MPa 112 °C234 °F4x100x100mm plaque; ISO 75-1/-2
Deflection Temperature at 8.0 MPa 54.0 °C129 °FISO 75-1/-2
UL RTI, Electrical  130 °C
@Thickness 3.00 mm		266 °F
@Thickness 0.118 in		UL 746B
 130 °C
@Thickness 0.750 mm		266 °F
@Thickness 0.0295 in		UL 746B
 130 °C
@Thickness 1.50 mm		266 °F
@Thickness 0.0591 in		UL 746B
 130 °C
@Thickness 6.00 mm		266 °F
@Thickness 0.236 in		UL 746B
UL RTI, Mechanical with Impact  115 °C
@Thickness 6.00 mm		239 °F
@Thickness 0.236 in		UL 746B
 115 °C
@Thickness 3.00 mm		239 °F
@Thickness 0.118 in		UL 746B
 115 °C
@Thickness 1.50 mm		239 °F
@Thickness 0.0591 in		UL 746B
 115 °C
@Thickness 0.750 mm		239 °F
@Thickness 0.0295 in		UL 746B
UL RTI, Mechanical without Impact  120 °C
@Thickness 3.00 mm		248 °F
@Thickness 0.118 in		UL 746B
 120 °C
@Thickness 6.00 mm		248 °F
@Thickness 0.236 in		UL 746B
 120 °C
@Thickness 0.750 mm		248 °F
@Thickness 0.0295 in		UL 746B
 120 °C
@Thickness 1.50 mm		248 °F
@Thickness 0.0591 in		UL 746B
Flammability, UL94  HB
@Thickness 6.00 mm		HB
@Thickness 0.236 in		IEC 60695-11-10
 HB
@Thickness 1.50 mm		HB
@Thickness 0.0591 in		IEC 60695-11-10
 HB
@Thickness 3.00 mm		HB
@Thickness 0.118 in		IEC 60695-11-10
 HB
@Thickness 1.50 mm		HB
@Thickness 0.0591 in		UL94
 HB
@Thickness 3.00 mm		HB
@Thickness 0.118 in		UL94
 HB
@Thickness 6.00 mm		HB
@Thickness 0.236 in		UL94
Oxygen Index 20 %20 %ISO 4589-1/-2
 
Processing PropertiesMetricEnglishComments
Melt Temperature 225 °C437 °F10°C/min; ISO 11357-1/-3
 250 °C482 °FOptimum
 240 - 260 °C464 - 500 °F
Mold Temperature 80.0 °C176 °Foptimum
 30.0 - 130 °C86.0 - 266 °F
Drying Temperature 110 - 130 °C230 - 266 °F
Dry Time 2.00 - 4.00 hour2.00 - 4.00 hour
Moisture Content <= 0.040 %<= 0.040 %
 
Descriptive Properties
AdditiveLubricant
AppearanceNatural Color
Drying RecommendedYes
FeaturesChemical Resistance, Good
 Dimensional Stability, Good
 Moisture Absorption, Low
 Processability, Good
 Stiffness, Good
 Strength, Good
FillerGlass fiber reinforcement
FormsPellets
GenericPBT
Material StatusCurrent
Part Marking Code>PBT-GF10<ISO 11469
Polymer FamilyPolyester
Polymer TypePBT
Processing MethodInjection Molding
Product CategoryGlass Reinforced Resins
Region Available - GlobalYes
Resin IdentificationPBT-GF10ISO 1043
RoHS ComplianceContact Manufacturer
Ultrasonic WeldableYes
UsesAutomotive Applications
 General Purpose
 Industrial Applications
 Parts, Engineering
 Parts, Machine/Mechanical
 Structural Parts

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-38084.html

免责声明: 本文 DuPont Performance Polymers Crastin® SK601 NC010 PBT 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他物性信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4