- 缺口冲击强度: 0.49
- 弯曲模量 [MPa]: 1.8639
- 热变形温度 [℃]: 153.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.29 g/cc | 1.29 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.016 cm/cm | 0.016 in/in | |
| Linear Mold Shrinkage, Transverse | 0.030 cm/cm | 0.030 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength | 49.05 MPa | 7114 psi | ASTM D638 |
| Elongation at Break | >= 120 % | >= 120 % | ASTM D638 |
| Flexural Strength | 70.63 MPa | 10240 psi | ASTM D790 |
| Flexural Modulus | 1.8639 GPa | 270.34 ksi | ASTM D790 |
| Izod Impact, Notched | 0.490 J/cm | 0.918 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 153 °C | 307 °F | ASTM D648 |
| Flammability, UL94 | HB | HB | |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 230 - 250 °C | 446 - 482 °F | |
| Mold Temperature | 40.0 - 60.0 °C | 104 - 140 °F | |