- 密度 [g/cm3]: 1.65
- 吸水率 [%]: 0.27
- 缺口冲击强度: 11.0
- 弯曲模量 [MPa]: 12.0
- 热变形温度 [℃]: 220.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.65 g/cc | 0.0596 lb/in³ | ISO 1183 |
| Filler Content | 45 % | 45 % | ISO 3451 |
| Moisture Absorption at Equilibrium | 0.10 % | 0.10 % | Humidity Absorption, 50% RH, 23°C; ISO 62 |
| Water Absorption at Saturation | 0.27 % | 0.27 % | 23°C; ISO 62 |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0090 cm/cm | 0.0090 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 150 MPa | 21800 psi | ISO 527 |
| Elongation at Break | 1.8 % | 1.8 % | ISO 527 |
| Tensile Modulus | 14.0 GPa | 2030 ksi | ISO 527 |
| Flexural Strength | 240 MPa | 34800 psi | 23°C, at break; ISO 178 |
| Flexural Modulus | 12.0 GPa | 1740 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 11.0 kJ/m² @Temperature -30.0 °C | 5.23 ft-lb/in² @Temperature -22.0 °F | ISO 180/1A |
| 14.0 kJ/m² @Temperature 23.0 °C | 6.66 ft-lb/in² @Temperature 73.4 °F | ISO 180/1A | |
| Charpy Impact Unnotched | 6.00 J/cm² @Temperature -30.0 °C | 28.6 ft-lb/in² @Temperature -22.0 °F | ISO 179/eU |
| 7.00 J/cm² @Temperature 23.0 °C | 33.3 ft-lb/in² @Temperature 73.4 °F | ISO 179/eU | |
| Charpy Impact, Notched | 1.20 J/cm² @Temperature -30.0 °C | 5.71 ft-lb/in² @Temperature -22.0 °F | ISO 179/eA |
| 1.50 J/cm² @Temperature 23.0 °C | 7.14 ft-lb/in² @Temperature 73.4 °F | ISO 179/eA | |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | IEC 60093 |
| Comparative Tracking Index | 500 V | 500 V | IEC 60112 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 225 °C | 437 °F | 10 K/min; ISO 3146 |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ISO 75-1/2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | ISO 75-1/2 |
| Vicat Softening Point | 215 °C | 419 °F | 50N; ISO 306 |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |
| HB @Thickness 3.20 mm | HB @Thickness 0.126 in | ||
| Glow Wire Test | 650 °C @Thickness 2.00 mm | 1200 °F @Thickness 0.0787 in | plaque; IEC 60695 |