- 成型收缩率 [%]: 0.002
- 缺口冲击强度: 0.883
- 弯曲模量 [MPa]: 7.35
- 热变形温度 [℃]: 210.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.50 g/cc | 1.50 g/cc | ASTM D792 | ||
| Moisture Absorption | 0.0300 % @Time 86400 sec | 0.0300 % @Time 24.0 hour | ASTM D570 | ||
| Linear Mold Shrinkage | 0.0020 - 0.0050 cm/cm @Thickness 1.60 mm | 0.0020 - 0.0050 in/in @Thickness 0.0630 in | horizontal; ASTM D955 | ||
| 0.0080 - 0.014 cm/cm @Thickness 1.60 mm | 0.0080 - 0.014 in/in @Thickness 0.0630 in | vertical; ASTM D955 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength | 93.2 MPa | 13500 psi | ASTM D638 | ||
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 | ||
| Flexural Strength | 160 MPa | 23200 psi | ASTM D790 | ||
| Flexural Modulus | 7.35 GPa | 1070 ksi | ASTM D790 | ||
| Izod Impact, Notched | >= 0.883 J/cm @Thickness 6.35 mm | >= 1.65 ft-lb/in @Thickness 0.250 in | ASTM D256 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 | ||
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | ASTM D257 | ||
| Dielectric Constant | 3.5 @Frequency 60.0 Hz | 3.5 @Frequency 60.0 Hz | ASTM D150 | ||
| Dielectric Strength | 22.0 kV/mm @Thickness 2.00 mm | 559 kV/in @Thickness 0.0787 in | ASTM D149 | ||
| Dissipation Factor | 0.0010 @Frequency 60.0 Hz | 0.0010 @Frequency 60.0 Hz | ASTM D150 | ||
| Arc Resistance | 120 sec | 120 sec | ASTM D495 | ||
| Comparative Tracking Index | 400 V | 400 V | ASTM D3638 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 225 °C | 437 °F | DSC | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | ASTM D648 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | ASTM D648 | ||
| Flammability, UL94 | V-0 @Thickness 0.800 mm | V-0 @Thickness 0.0315 in | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 240 - 270 °C | 464 - 518 °F | |||
| Nozzle Temperature | 260 - 270 °C | 500 - 518 °F | |||
| Mold Temperature | 40.0 - 120 °C | 104 - 248 °F | suitable temperature 60-80°C | ||
| Injection Pressure | 50.0 - 120 MPa | 7250 - 17400 psi | |||
| Hold Pressure | 30.0 - 80.0 MPa | 4350 - 11600 psi | |||
| Back Pressure | 0.000 - 0.300 MPa | 0.000 - 43.5 psi | |||
| Screw Speed | 60 - 120 rpm | 60 - 120 rpm | to be chosen in such a way that plasticizing time is just within cooling time | ||
| Descriptive Properties | |||||
| Injection Rate | middle-fast | ||||