- 熔体流动速率 [g/10min]: 30.0
- 密度 [g/cm3]: 1.42
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.42 g/cc @Temperature 23.0 °C | 0.0513 lb/in³ @Temperature 73.4 °F | ±0.02; ISO 1183 | ||
| Melt Flow | 30 g/10 min @Load 2.16 kg, Temperature 250 °C | 30 g/10 min @Load 4.76 lb, Temperature 482 °F | ±5; ISO 1133 | ||
| Melt Index of Compound | 25 g/10 min @Load 2.16 kg, Temperature 250 °C | 25 g/10 min @Load 4.76 lb, Temperature 482 °F | ±5; cm³/10min; ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 105 MPa @Thickness 4.00 mm, Temperature 23.0 °C | 15200 psi @Thickness 0.157 in, Temperature 73.4 °F | Injection Molded; ISO 527-2 | ||
| Elongation at Break | >= 3.0 % @Thickness 4.00 mm, Temperature 23.0 °C | >= 3.0 % @Thickness 0.157 in, Temperature 73.4 °F | Injection Molded; ISO 527-2 | ||
| Tensile Modulus | 6.50 GPa @Thickness 4.00 mm, Temperature 23.0 °C | 943 ksi @Thickness 0.157 in, Temperature 73.4 °F | ISO 527-2 | ||
| Charpy Impact Unnotched | 3.10 J/cm² @Temperature 23.0 °C | 14.8 ft-lb/in² @Temperature 73.4 °F | Injection Molded; ISO 179 | ||
| Charpy Impact, Notched | 0.370 J/cm² @Temperature 23.0 °C | 1.76 ft-lb/in² @Temperature 73.4 °F | Injection Molded; ISO 179 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 | ||
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | ASTM D257 | ||
| Thermal Properties | Metric | English | Comments | ||
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | Internal Method | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 240 - 260 °C | 464 - 500 °F | |||
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |||
| Drying Temperature | 80.0 - 120 °C | 176 - 248 °F | |||
| Dry Time | 4.00 hour | 4.00 hour | |||
| Descriptive Properties | |||||
| Appearance | Blue | ||||
| Features | Good Chemical Resistance | ||||
| Good Impact Resistance | |||||
| Filler / Reinforcement | Glass Fiber Reinforcement, 15% Filler by Weight | ||||
| Forms | Pellets | ||||
| Generic Material | PBT | ||||
| Generic Name | Polybutylene Terephthalate (PBT) | ||||
| Processing Method | Injection Molding | ||||
| Regional Availability | Europe | ||||
| RoHS Compliance | RoHS Compliant | ||||