- 熔体流动速率 [g/10min]: 14.0
- 密度 [g/cm3]: 1.52
- 吸水率 [%]: 0.05
- 缺口冲击强度: 0.908
- 弯曲模量 [MPa]: 9.11
- 热变形温度 [℃]: 217.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.52 g/cc | 1.52 g/cc | ASTM D792 | ||
| Density | 1.52 g/cc | 0.0549 lb/in³ | ISO 1183 | ||
| Water Absorption | 0.0500 % | 0.0500 % | 24hr immersion; ASTM D570 | ||
| Linear Mold Shrinkage, Flow | 0.00300 - 0.00500 cm/cm | 0.00300 - 0.00500 in/in | ASTM D955 | ||
| 0.00300 - 0.00500 cm/cm | 0.00300 - 0.00500 in/in | ISO 294-4 | |||
| Melt Flow | 14.0 g/10 min | 14.0 g/10 min | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 90.0 | 90.0 | ISO 2039-2 | ||
| Tensile Strength at Break | 124 MPa | 18000 psi | ASTM D638 | ||
| 135 MPa | 19600 psi | 5mm/min; ISO 527-2/1A | |||
| Elongation at Break | 2.60 % | 2.60 % | 5mm/min; ISO 527-2/1A | ||
| 4.00 % @Temperature 22.8 °C | 4.00 % @Temperature 73.0 °F | ASTM D638 | |||
| Flexural Strength | 197 MPa | 28500 psi | ASTM D790 | ||
| 210 MPa | 30500 psi | ISO 178 | |||
| Flexural Modulus | 9.11 GPa | 1320 ksi | ISO 178 | ||
| 8.27 GPa @Temperature 22.8 °C | 1200 ksi @Temperature 73.0 °F | ASTM D790 | |||
| Izod Impact, Notched | 0.908 J/cm | 1.70 ft-lb/in | ASTM D256 | ||
| Izod Impact, Notched (ISO) | 9.20 kJ/m² | 4.38 ft-lb/in² | ISO 180/1A | ||
| Charpy Impact, Notched | 0.720 J/cm² | 3.43 ft-lb/in² | ISO 179/1eA | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 | ||
| Dielectric Strength | 20.5 kV/mm | 520 kV/in | short term; ASTM D149 | ||
| Dissipation Factor | 0.00200 @Frequency 1000 Hz | 0.00200 @Frequency 1000 Hz | ASTM D150 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 25.0 µm/m-°C | 13.9 µin/in-°F | ISO 11359-2 | ||
| CTE, linear, Transverse to Flow | 128 µm/m-°C | 71.1 µin/in-°F | ISO 11359-2 | ||
| Melting Point | 225 °C | 437 °F | 10°C/min; ISO 11357-1,-2,-3 | ||
| 225 °C | 437 °F | ASTM D3418 | |||
| Transformation Temperature, Tg | 60.0 °C | 140 °F | 10°C/min; ISO 11357-1,-2,-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 217 °C | 422 °F | ASTM D648 | ||
| 225 °C | 437 °F | ISO 75-1, -2 | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 204 °C | 400 °F | ASTM D648 | ||
| 207 °C | 405 °F | ISO 75-1, -2 | |||
| Flammability, UL94 | HB | HB | UL94 | ||
| HB @Thickness 0.800 mm | HB @Thickness 0.0315 in | UL94 | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 20.0 - 50.0 °C | 68.0 - 122 °F | |||
| 65.0 - 93.0 °C | 149 - 199 °F | Cavity temperature | |||
| Feed Temperature | 230 - 240 °C | 446 - 464 °F | |||
| Rear Barrel Temperature | 230 - 240 °C | 446 - 464 °F | |||
| Middle Barrel Temperature | 235 - 250 °C | 455 - 482 °F | |||
| Front Barrel Temperature | 240 - 260 °C | 464 - 500 °F | |||
| Nozzle Temperature | 250 - 260 °C | 482 - 500 °F | |||
| Zone 1 | 230 - 240 °C | 446 - 464 °F | |||
| Zone 2 | 235 - 250 °C | 455 - 482 °F | |||
| Zone 3 | 235 - 250 °C | 455 - 482 °F | |||
| Zone 4 | 240 - 260 °C | 464 - 500 °F | |||
| Die Temperature | 250 - 260 °C | 482 - 500 °F | |||
| Melt Temperature | 235 - 260 °C | 455 - 500 °F | |||
| 235 - 260 °C | 455 - 500 °F | ||||
| 260 °C | 500 °F | Injection molding; ISO 294 | |||
| Mold Temperature | 65.6 - 93.3 °C | 150 - 200 °F | |||
| 82.0 °C | 180 °F | Injection molding; ISO 294 | |||
| Injection Velocity | 300 mm/sec | 11.8 in/sec | ISO 294 | ||
| Drying Temperature | 120 - 130 °C | 248 - 266 °F | |||
| Dry Time | 4.00 hour | 4.00 hour | |||
| Moisture Content | 0.0200 % | 0.0200 % | Necessary low maximum residual | ||
| Hold Pressure | 48.0 MPa | 6960 psi | ISO 294 | ||
| Back Pressure | 0.000 - 0.345 MPa | 0.000 - 50.0 psi | |||
| Hot-Working Temperature | 250 - 260 °C | 482 - 500 °F | |||
| Descriptive Properties | |||||
| Injection molding | Yes | ||||
| Injection speed | medium-fast | ||||
| Longer pre-drying times/storage | lower the temperature to 100° C until processed. | <= 60 h | |||
| Processing conditions | ISO 7792-2 | ||||
| Processing Notes | Fast Injection Speed | ||||
| Medium Screw Speed | |||||