- 密度 [g/cm3]: 1.31
- 缺口冲击强度: 4.0
- 拉伸强度 [MPa]: 60.0
- 弯曲模量 [MPa]: 2.55
- 热变形温度 [℃]: 150.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.31 g/cc | 1.31 g/cc | ASTM D792 | ||
| Density | 1.31 g/cc | 0.0473 lb/in³ | ISO 1183 | ||
| Moisture Absorption | 0.140 % | 0.140 % | 23°C/50%RH; ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.0180 - 0.0200 cm/cm | 0.0180 - 0.0200 in/in | ASTM D955 | ||
| 0.0180 - 0.0200 cm/cm | 0.0180 - 0.0200 in/in | ISO 294-4 | |||
| Linear Mold Shrinkage, Transverse | 0.0180 - 0.0200 cm/cm | 0.0180 - 0.0200 in/in | ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 55.0 MPa | 7980 psi | 50mm/min; ISO 527-2/1A | ||
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | 50mm/min; ISO 527-2/1A | ||
| Elongation at Break | 25.0 % | 25.0 % | 50mm/min; ISO 527-2/1A | ||
| 40.0 % | 40.0 % | 50mm/min; ISO 527-2/1A | |||
| Elongation at Yield | 4.00 % | 4.00 % | 50mm/min; ISO 527-2/1A | ||
| Tensile Modulus | 2.70 GPa | 392 ksi | 1mm/min; ISO 527-2/1A | ||
| Flexural Strength | 80.0 MPa | 11600 psi | ISO 178 | ||
| Flexural Modulus | 2.55 GPa | 370 ksi | ISO 178 | ||
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | ISO 180/1A | ||
| Izod Impact, Unnotched (ISO) | 31.0 kJ/m² | 14.8 ft-lb/in² | ISO 180/1U | ||
| 33.0 kJ/m² @Temperature -30.0 °C | 15.7 ft-lb/in² @Temperature -22.0 °F | ISO 180/1U | |||
| Charpy Impact Unnotched | 11.1 J/cm² | 52.8 ft-lb/in² | ISO 179/1eU | ||
| 3.50 J/cm² @Temperature -30.0 °C | 16.7 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 0.430 J/cm² | 2.05 ft-lb/in² | ISO 179/1eA | ||
| 0.430 J/cm² @Temperature -30.0 °C | 2.05 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 | ||
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | IEC 60093 | ||
| Dielectric Constant | 3.20 @Frequency 1.00e+6 Hz | 3.20 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| Dielectric Strength | 15.0 kV/mm | 381 kV/in | IEC 60243-1 | ||
| Dissipation Factor | 0.0200 @Frequency 1.00e+6 Hz | 0.0200 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 120 µm/m-°C | 66.7 µin/in-°F | ISO 11359-2 | ||
| CTE, linear, Transverse to Flow | 110 µm/m-°C | 61.1 µin/in-°F | ISO 11359-2 | ||
| Melting Point | 225 °C | 437 °F | 10°C/min; ISO 11357-1,-2,-3 | ||
| 225 °C | 437 °F | ASTM D3418 | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 150 °C | 302 °F | ISO 75-1, -2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | ISO 75-1, -2 | ||
| Vicat Softening Point | 190 °C | 374 °F | B50 (50°C/h 50N); ISO 306 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 20.0 - 50.0 °C | 68.0 - 122 °F | |||
| 65.0 - 93.0 °C | 149 - 199 °F | Cavity temperature | |||
| Feed Temperature | 230 - 240 °C | 446 - 464 °F | |||
| Rear Barrel Temperature | 230 - 240 °C | 446 - 464 °F | |||
| Middle Barrel Temperature | 235 - 250 °C | 455 - 482 °F | |||
| Front Barrel Temperature | 240 - 260 °C | 464 - 500 °F | |||
| Nozzle Temperature | 250 - 260 °C | 482 - 500 °F | |||
| Zone 1 | 230 - 240 °C | 446 - 464 °F | |||
| Zone 2 | 235 - 250 °C | 455 - 482 °F | |||
| Zone 3 | 235 - 250 °C | 455 - 482 °F | |||
| Zone 4 | 240 - 260 °C | 464 - 500 °F | |||
| Die Temperature | 250 - 260 °C | 482 - 500 °F | |||
| Melt Temperature | 235 - 260 °C | 455 - 500 °F | |||
| 235 - 260 °C | 455 - 500 °F | ||||
| Mold Temperature | 65.6 - 93.3 °C | 150 - 200 °F | |||
| Drying Temperature | 120 - 130 °C | 248 - 266 °F | |||
| Dry Time | 4.00 hour | 4.00 hour | |||
| Moisture Content | 0.0200 % | 0.0200 % | Necessary low maximum residual | ||
| Back Pressure | 0.000 - 0.345 MPa | 0.000 - 50.0 psi | |||
| Hot-Working Temperature | 250 - 260 °C | 482 - 500 °F | |||
| Descriptive Properties | |||||
| Injection molding | Yes | ||||
| Injection speed | medium-fast | ||||
| Longer pre-drying times/storage | lower the temperature to 100° C until processed. | <= 60 h | |||
| Processing Notes | Fast Injection Speed | ||||
| Medium Screw Speed | |||||