- 熔体流动速率 [g/10min]: 15.0
- 密度 [g/cm3]: 1.55
- 热变形温度 [℃]: 220.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.55 g/cc | 0.0560 lb/in³ | ISO 1183 | ||
| Density of Compound | 1.32 g/cc | 0.0477 lb/in³ | melt; Internal | ||
| Moisture Absorption | 0.150 % | 0.150 % | 23°C/50%RH; ISO 62 | ||
| Viscosity Test | 70.0 cm³/g | 70.0 cm³/g | ISO 307, 1157, 1628 | ||
| Melt Flow | 15.0 g/10 min @Load 2.16 kg, Temperature 265 °C | 15.0 g/10 min @Load 4.76 lb, Temperature 509 °F | (MVR) cm³/10min; ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 150 MPa | 21800 psi | 5mm/min; ISO 527-2/1A | ||
| Elongation at Break | 2.50 % | 2.50 % | 5mm/min; ISO 527-2/1A | ||
| Tensile Modulus | 10.5 GPa | 1520 ksi | 1mm/min; ISO 527-2/1A | ||
| Flexural Strength | 210 MPa | 30500 psi | ISO 178 | ||
| Charpy Impact Unnotched | 5.60 J/cm² | 26.6 ft-lb/in² | ISO 179/1eU | ||
| 5.80 J/cm² @Temperature -30.0 °C | 27.6 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 1.00 J/cm² | 4.76 ft-lb/in² | ISO 179/1eA | ||
| 1.00 J/cm² @Temperature -30.0 °C | 4.76 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 | ||
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | IEC 60093 | ||
| Dielectric Constant | 4.10 @Frequency 1.00e+6 Hz | 4.10 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| 4.40 @Frequency 100 Hz | 4.40 @Frequency 100 Hz | IEC 60250 | |||
| Dielectric Strength | 31.0 kV/mm | 787 kV/in | IEC 60243-1 | ||
| Dissipation Factor | 0.00140 @Frequency 100 Hz | 0.00140 @Frequency 100 Hz | IEC 60250 | ||
| 0.0170 @Frequency 1.00e+6 Hz | 0.0170 @Frequency 1.00e+6 Hz | IEC 60250 | |||
| Comparative Tracking Index | 250 V | 250 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 20.0 µm/m-°C | 11.1 µin/in-°F | ISO 11359-2 | ||
| Specific Heat Capacity | 1.73 J/g-°C | 0.413 BTU/lb-°F | Internal | ||
| Thermal Conductivity | 0.171 W/m-K | 1.19 BTU-in/hr-ft²-°F | Internal | ||
| Melting Point | 255 °C | 491 °F | 10°C/min; ISO 11357-1,-2,-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ISO 75-1, -2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | ISO 75-1, -2 | ||
| Deflection Temperature at 8.0 MPa | 125 °C | 257 °F | ISO 75-1, -2 | ||
| Vicat Softening Point | 225 °C | 437 °F | B50 (50°C/h 50N); ISO 306 | ||
| Flammability, UL94 | HB @Thickness 0.820 mm | HB @Thickness 0.0323 in | UL94 | ||
| HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | UL94 | |||
| Oxygen Index | 20.0 % | 20.0 % | ISO 4589 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 20.0 - 50.0 °C | 68.0 - 122 °F | |||
| 90.0 - 100 °C | 194 - 212 °F | Cavity temperature | |||
| 220 °C | 428 °F | Ejection temperature; Internal | |||
| Feed Temperature | 190 - 200 °C | 374 - 392 °F | |||
| Zone 1 | 250 - 260 °C | 482 - 500 °F | |||
| Zone 2 | 250 - 260 °C | 482 - 500 °F | |||
| Zone 3 | 260 - 270 °C | 500 - 518 °F | |||
| Zone 4 | 260 - 270 °C | 500 - 518 °F | |||
| Die Temperature | 265 - 275 °C | 509 - 527 °F | |||
| Melt Temperature | 265 - 275 °C | 509 - 527 °F | |||
| 265 - 275 °C | 509 - 527 °F | ||||
| 270 °C | 518 °F | Injection molding; ISO 294 | |||
| Mold Temperature | 90.0 °C | 194 °F | Injection molding; ISO 294 | ||
| 90.0 - 100 °C | 194 - 212 °F | ||||
| Injection Velocity | 200 mm/sec | 7.87 in/sec | ISO 294 | ||
| Drying Temperature | 120 - 140 °C | 248 - 284 °F | |||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | |||
| Moisture Content | 0.0200 % | 0.0200 % | Necessary low maximum residual | ||
| Dew Point | <= -30.0 °C | <= -22.0 °F | Pre-drying | ||
| Hold Pressure | 40.0 - 80.0 MPa | 5800 - 11600 psi | |||
| 70.0 MPa | 10200 psi | ISO 294 | |||
| 60.0 - 100 MPa | 8700 - 14500 psi | ||||
| Back Pressure | 1.00 - 3.00 MPa | 145 - 435 psi | |||
| Screw Speed | 60.0 rpm @Diameter 55.0 mm | 60.0 rpm @Diameter 2.17 in | |||
| 75.0 rpm @Diameter 40.0 mm | 75.0 rpm @Diameter 1.57 in | ||||
| 90.0 rpm @Diameter 25.0 mm | 90.0 rpm @Diameter 0.984 in | ||||
| Hot-Working Temperature | 265 - 275 °C | 509 - 527 °F | |||
| Descriptive Properties | |||||
| Injection molding | Yes | ||||
| Injection speed | fast | ||||
| Longer pre-drying times/storage | lower the temperature to 100° C until processed. | <= 60 h | |||
| Processing conditions | 7792 | ||||
| Processing Notes | Fast Injection Speed | ||||
| Maximum Barrel Residence Time 5-10 min | |||||
| Open Nozzle Design Preferred | |||||
| Peripheral screw speed max. 0.3 m/sec | |||||