- 熔体流动速率 [g/10min]: 7.0
- 密度 [g/cm3]: 1.66
- 缺口冲击强度: 0.747
- 弯曲模量 [MPa]: 10.3
- 热变形温度 [℃]: 220.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.66 g/cc | 1.66 g/cc | ASTM D792 | ||
| Density | 1.66 g/cc | 0.0600 lb/in³ | ISO 1183 | ||
| Moisture Absorption | 0.160 % | 0.160 % | 23°C/50%RH; ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.00300 - 0.00500 cm/cm | 0.00300 - 0.00500 in/in | ASTM D955 | ||
| 0.00100 - 0.00800 cm/cm | 0.00100 - 0.00800 in/in | ISO 294-4 | |||
| Linear Mold Shrinkage, Transverse | 0.00800 - 0.0130 cm/cm | 0.00800 - 0.0130 in/in | ISO 294-4 | ||
| Melt Flow | 7.00 g/10 min @Load 2.16 kg, Temperature 250 °C | 7.00 g/10 min @Load 4.76 lb, Temperature 482 °F | (MVR) cm³/10min; ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 89.0 | 89.0 | ISO 2039-2 | ||
| Tensile Strength at Break | 134 MPa | 19500 psi | ASTM D638 | ||
| 135 MPa | 19600 psi | 5mm/min; ISO 527-2/1A | |||
| Elongation at Break | 2.50 % | 2.50 % | 5mm/min; ISO 527-2/1A | ||
| 2.50 % @Temperature 22.8 °C | 2.50 % @Temperature 73.0 °F | ASTM D638 | |||
| Tensile Modulus | 10.7 GPa | 1550 ksi | 1mm/min; ISO 527-2/1A | ||
| 9.65 GPa @Temperature 22.8 °C | 1400 ksi @Temperature 73.0 °F | ASTM D638 | |||
| Flexural Strength | 200 MPa | 29000 psi | ISO 178 | ||
| 203 MPa | 29500 psi | ASTM D790 | |||
| Flexural Modulus | 10.3 GPa | 1490 ksi | ISO 178 | ||
| 9.65 GPa @Temperature 22.8 °C | 1400 ksi @Temperature 73.0 °F | ASTM D790 | |||
| Izod Impact, Notched | 0.747 J/cm | 1.40 ft-lb/in | ASTM D256 | ||
| Izod Impact, Notched (ISO) | 7.70 kJ/m² | 3.66 ft-lb/in² | ISO 180/1A | ||
| Charpy Impact Unnotched | 5.90 J/cm² | 28.1 ft-lb/in² | ISO 179/1eU | ||
| 4.20 J/cm² @Temperature -30.0 °C | 20.0 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 0.850 J/cm² | 4.04 ft-lb/in² | ISO 179/1eA | ||
| 0.850 J/cm² @Temperature -30.0 °C | 4.04 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 | ||
| 2.00e+16 ohm-cm | 2.00e+16 ohm-cm | ASTM D257 | |||
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | IEC 60093 | ||
| Dielectric Constant | 2.90 @Frequency 1.00e+6 Hz | 2.90 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| 3.50 @Frequency 1.00e+6 Hz | 3.50 @Frequency 1.00e+6 Hz | ASTM D150 | |||
| 3.60 @Frequency 100 Hz | 3.60 @Frequency 100 Hz | IEC 60250 | |||
| Dielectric Strength | 19.7 kV/mm | 500 kV/in | short term; ASTM D149 | ||
| 34.0 kV/mm | 864 kV/in | IEC 60243-1 | |||
| Dissipation Factor | 0.00330 @Frequency 100 Hz | 0.00330 @Frequency 100 Hz | IEC 60250 | ||
| 0.0145 @Frequency 1.00e+6 Hz | 0.0145 @Frequency 1.00e+6 Hz | IEC 60250 | |||
| 0.0200 @Frequency 1.00e+6 Hz | 0.0200 @Frequency 1.00e+6 Hz | ASTM D150 | |||
| Arc Resistance | 106 sec | 106 sec | ASTM D495 | ||
| Comparative Tracking Index | 250 V | 250 V | IEC 60112 | ||
| 250 V | 250 V | ASTM D3638 | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 25.0 µm/m-°C | 13.9 µin/in-°F | ISO 11359-2 | ||
| CTE, linear, Transverse to Flow | 77.0 µm/m-°C | 42.8 µin/in-°F | ISO 11359-2 | ||
| Melting Point | 225 °C | 437 °F | 10°C/min; ISO 11357-1,-2,-3 | ||
| 225 °C | 437 °F | ASTM D3418 | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ISO 75-1, -2 | ||
| 221 °C | 430 °F | ASTM D648 | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 206 °C | 403 °F | ASTM D648 | ||
| 208 °C | 406 °F | ISO 75-1, -2 | |||
| Deflection Temperature at 8.0 MPa | 165 °C | 329 °F | ISO 75-1, -2 | ||
| Vicat Softening Point | 225 °C | 437 °F | B50 (50°C/h 50N); ISO 306 | ||
| Flammability, UL94 | V-0 | V-0 | UL94 | ||
| V-0 @Thickness 0.380 mm | V-0 @Thickness 0.0150 in | UL94 | |||
| 5VA @Thickness 1.50 mm | 5VA @Thickness 0.0591 in | UL94 | |||
| Oxygen Index | 30.0 % | 30.0 % | ISO 4589 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 20.0 - 50.0 °C | 68.0 - 122 °F | |||
| 65.0 - 93.0 °C | 149 - 199 °F | Cavity temperature | |||
| Feed Temperature | 230 - 240 °C | 446 - 464 °F | |||
| Rear Barrel Temperature | 230 - 240 °C | 446 - 464 °F | |||
| Middle Barrel Temperature | 235 - 250 °C | 455 - 482 °F | |||
| Front Barrel Temperature | 240 - 255 °C | 464 - 491 °F | |||
| Nozzle Temperature | 250 - 255 °C | 482 - 491 °F | |||
| Zone 1 | 230 - 240 °C | 446 - 464 °F | |||
| Zone 2 | 235 - 250 °C | 455 - 482 °F | |||
| Zone 3 | 235 - 250 °C | 455 - 482 °F | |||
| Zone 4 | 240 - 255 °C | 464 - 491 °F | |||
| Die Temperature | 250 - 255 °C | 482 - 491 °F | |||
| Melt Temperature | 235 - 255 °C | 455 - 491 °F | |||
| 235 - 255 °C | 455 - 491 °F | ||||
| 260 °C | 500 °F | Injection molding; ISO 294 | |||
| Mold Temperature | 65.6 - 93.3 °C | 150 - 200 °F | |||
| 82.0 °C | 180 °F | Injection molding; ISO 294 | |||
| Injection Velocity | 300 mm/sec | 11.8 in/sec | ISO 294 | ||
| Drying Temperature | 120 - 130 °C | 248 - 266 °F | |||
| Dry Time | 4.00 hour | 4.00 hour | |||
| Moisture Content | 0.0200 % | 0.0200 % | Necessary low maximum residual | ||
| Hold Pressure | 48.0 MPa | 6960 psi | ISO 294 | ||
| Back Pressure | 0.000 - 0.345 MPa | 0.000 - 50.0 psi | |||
| Hot-Working Temperature | 250 - 260 °C | 482 - 500 °F | |||
| Descriptive Properties | |||||
| Injection molding | Yes | ||||
| Injection speed | medium-fast | ||||
| Longer pre-drying times/storage | lower the temperature to 100° C until processed. | <= 60 h | |||
| Processing conditions | ISO 7792-2 | ||||
| Processing Notes | Fast Injection Speed | ||||
| Medium Screw Speed | |||||