- 缺口冲击强度: 5.8
- 弯曲模量 [MPa]: 3.775
- 热变形温度 [℃]: 200.0
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 69.0 MPa | 10000 psi | 50mm/min; ISO 527-2/1A |
| Elongation at Break | 3.0 % | 3.0 % | 50mm/min; ISO 527-2/1A |
| Tensile Modulus | 3.882 GPa | 563.0 ksi | 1mm/min; ISO 527-2/1A |
| Flexural Strength | 100.6 MPa | 14590 psi | ISO 178 |
| Flexural Modulus | 3.775 GPa | 547.5 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 5.80 kJ/m² | 2.76 ft-lb/in² | ISO 180/1A |
| 5.70 kJ/m² @Temperature 30.0 °C | 2.71 ft-lb/in² @Temperature 86.0 °F | ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 10.5 kJ/m² @Temperature 30.0 °C | 5.00 ft-lb/in² @Temperature 86.0 °F | ISO 180/1U |
| 12.2 kJ/m² @Temperature 23.0 °C | 5.81 ft-lb/in² @Temperature 73.4 °F | ISO 180/1U | |
| Charpy Impact Unnotched | 1.45 J/cm² | 6.90 ft-lb/in² | ISO 179/1eU |
| 1.39 J/cm² @Temperature 30.0 °C | 6.61 ft-lb/in² @Temperature 86.0 °F | ISO 179/1eU | |
| Charpy Impact, Notched | 0.570 J/cm² | 2.71 ft-lb/in² | ISO 179/1eA |
| 0.620 J/cm² @Temperature 30.0 °C | 2.95 ft-lb/in² @Temperature 86.0 °F | ISO 179/1eA | |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 200 °C | 392 °F | ISO 75-1, -2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 182 °C | 360 °F | ISO 75-1, -2 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 20.0 - 50.0 °C | 68.0 - 122 °F | hopper |
| 65.0 - 93.0 °C | 149 - 199 °F | cavity | |
| Feed Temperature | 230 - 240 °C | 446 - 464 °F | |
| Zone 1 | 230 - 240 °C | 446 - 464 °F | |
| Zone 2 | 235 - 250 °C | 455 - 482 °F | |
| Zone 3 | 235 - 250 °C | 455 - 482 °F | |
| Zone 4 | 240 - 260 °C | 464 - 500 °F | |
| Die Temperature | 250 - 260 °C | 482 - 500 °F | |
| Melt Temperature | 235 - 260 °C | 455 - 500 °F | |
| Hot-Working Temperature | 250 - 260 °C | 482 - 500 °F | |