Celanese Celanex® 3209HR PBT, Glass Reinforced 物性表: Celanese Celanex® 3209HR PBT, Glass Reinforced物性表及特性介绍,Celanese Celanex® 3209HR PBT, Glass Reinforced注塑参数详情,如需Celanese Celanex® 3209HR PBT, Glass Reinforced下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.41
  • 缺口冲击强度: 5.3
  • 弯曲模量 [MPa]: 5.30
  • 热变形温度 [℃]: 220.0
 
Physical PropertiesMetricEnglishComments
Specific Gravity 1.41 g/cc1.41 g/ccASTM D792
Density 1.41 g/cc0.0509 lb/in³ISO 1183
Moisture Absorption at Equilibrium 0.17 %0.17 %23°C/50%RH; ISO 62
Linear Mold Shrinkage, Flow 0.0010 cm/cm0.0010 in/inISO 294-4
Linear Mold Shrinkage, Transverse 0.0090 cm/cm0.0090 in/inISO 294-4
 
Mechanical PropertiesMetricEnglishComments
Tensile Strength at Break 100 MPa14500 psi5mm/min; ISO 527-2/1A
Elongation at Break 3.5 %3.5 %5mm/min; ISO 527-2/1A
Tensile Modulus 5.80 GPa841 ksi1mm/min; ISO 527-2/1A
Flexural Strength 150 MPa21800 psiISO 178
Flexural Modulus 5.30 GPa769 ksiISO 178
Izod Impact, Notched (ISO) 5.30 kJ/m²2.52 ft-lb/in²ISO 180/1A
Izod Impact, Unnotched (ISO) 17.0 kJ/m²
@Temperature 23.0 °C
8.09 ft-lb/in²
@Temperature 73.4 °F
ISO 180/1U
Charpy Impact Unnotched 2.20 J/cm²10.5 ft-lb/in²ISO 179/1eU
 2.20 J/cm²
@Temperature 30.0 °C
10.5 ft-lb/in²
@Temperature 86.0 °F
ISO 179/1eU
Charpy Impact, Notched 0.550 J/cm²2.62 ft-lb/in²ISO 179/1eA
 0.400 J/cm²
@Temperature 30.0 °C
1.90 ft-lb/in²
@Temperature 86.0 °F
ISO 179/1eA
 
Electrical PropertiesMetricEnglishComments
Volume Resistivity 4.00e+14 ohm-cm4.00e+14 ohm-cmIEC 60093
Surface Resistance 2.00e+16 ohm2.00e+16 ohmIEC 60093
Dielectric Constant  2.9
@Frequency 1.00e+6 Hz
2.9
@Frequency 1.00e+6 Hz
IEC 60250
 3.7
@Frequency 100 Hz
3.7
@Frequency 100 Hz
IEC 60250
Dielectric Strength 17.0 kV/mm432 kV/inIEC 60243-1
Dissipation Factor 0.024
@Frequency 1.00e+6 Hz
0.024
@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index 325 V325 VIEC 60112
 
Thermal PropertiesMetricEnglishComments
CTE, linear, Parallel to Flow 38.0 µm/m-°C21.1 µin/in-°FISO 11359-2
CTE, linear, Transverse to Flow 100 µm/m-°C55.6 µin/in-°FISO 11359-2
Melting Point 225 °C437 °FISO 11357-1,-2,-3
Deflection Temperature at 0.46 MPa (66 psi) 220 °C428 °FISO 75-1, -2
Deflection Temperature at 1.8 MPa (264 psi) 180 °C356 °FISO 75-1, -2
Glass Transition Temp, Tg 60.0 °C140 °FISO 11357-1,-2,-3
 
Processing PropertiesMetricEnglishComments
Processing Temperature 20.0 - 50.0 °C68.0 - 122 °Fhopper
 65.0 - 93.0 °C149 - 199 °Fcavity
Feed Temperature 230 - 240 °C446 - 464 °F
Zone 1 230 - 240 °C446 - 464 °F
Zone 2 235 - 250 °C455 - 482 °F
Zone 3 235 - 250 °C455 - 482 °F
Zone 4 240 - 260 °C464 - 500 °F
Die Temperature 250 - 260 °C482 - 500 °F
Melt Temperature 235 - 260 °C455 - 500 °F
Hot-Working Temperature 250 - 260 °C482 - 500 °F

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-38400.html

免责声明: 本文 Celanese Celanex® 3209HR PBT, Glass Reinforced 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4