- 密度 [g/cm3]: 1.6
- 弯曲模量 [MPa]: 7.20
- 热变形温度 [℃]: 220.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.60 g/cc | 0.0578 lb/in³ | ISO 1183 | ||
| Moisture Absorption at Equilibrium | 0.15 % | 0.15 % | 23°C/50%RH; ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0050 cm/cm | 0.0020 - 0.0050 in/in | ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0080 cm/cm | 0.0050 - 0.0080 in/in | ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 115 MPa | 16700 psi | 5mm/min; ISO 527-2/1A | ||
| Elongation at Break | 2.5 % | 2.5 % | 5mm/min; ISO 527-2/1A | ||
| Tensile Modulus | 7.20 GPa | 1040 ksi | 1mm/min; ISO 527-2/1A | ||
| Flexural Strength | 185 MPa | 26800 psi | ISO 178 | ||
| Flexural Modulus | 7.20 GPa | 1040 ksi | ISO 178 | ||
| Charpy Impact Unnotched | 3.50 J/cm² | 16.7 ft-lb/in² | ISO 179/1eU | ||
| 3.50 J/cm² @Temperature 30.0 °C | 16.7 ft-lb/in² @Temperature 86.0 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 0.700 J/cm² | 3.33 ft-lb/in² | ISO 179/1eA | ||
| 0.650 J/cm² @Temperature 30.0 °C | 3.09 ft-lb/in² @Temperature 86.0 °F | ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+13 ohm-cm | >= 1.00e+13 ohm-cm | IEC 60093 | ||
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | IEC 60093 | ||
| Dielectric Constant | 3.5 @Frequency 1.00e+6 Hz | 3.5 @Frequency 1.00e+6 Hz | ASTM D150 | ||
| 3.9 @Frequency 1.00e+6 Hz | 3.9 @Frequency 1.00e+6 Hz | IEC 60250 | |||
| 4.3 @Frequency 50.0 Hz | 4.3 @Frequency 50.0 Hz | IEC 60250 | |||
| Dielectric Strength | 18.9 kV/mm | 480 kV/in | short term; ASTM D149 | ||
| 32.0 kV/mm | 813 kV/in | IEC 60243-1 | |||
| Dissipation Factor | 0.0033 @Frequency 50.0 Hz | 0.0033 @Frequency 50.0 Hz | IEC 60250 | ||
| 0.016 @Frequency 1.00e+6 Hz | 0.016 @Frequency 1.00e+6 Hz | IEC 60250 | |||
| 0.020 @Frequency 1.00e+6 Hz | 0.020 @Frequency 1.00e+6 Hz | ASTM D150 | |||
| Arc Resistance | 87 sec | 87 sec | ASTM D495 | ||
| Comparative Tracking Index | 175 V | 175 V | ASTM D3638 | ||
| 225 V | 225 V | IEC 60112 | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 35.0 µm/m-°C | 19.4 µin/in-°F | ISO 11359-2 | ||
| CTE, linear, Transverse to Flow | 35.0 µm/m-°C | 19.4 µin/in-°F | ISO 11359-2 | ||
| Melting Point | 225 °C | 437 °F | ISO 11357-1,-2,-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ISO 75-1, -2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 203 °C | 397 °F | ISO 75-1, -2 | ||
| Deflection Temperature at 8.0 MPa | 135 °C | 275 °F | ISO 75-1, -2 | ||
| Vicat Softening Point | 220 °C | 428 °F | B50 (50°C/h 50N); ISO 306 | ||
| Flammability, UL94 | V-0 | V-0 | |||
| V-0 @Thickness 0.380 mm | V-0 @Thickness 0.0150 in | ||||
| V-0 @Thickness 1.60 mm | V-0 @Thickness 0.0630 in | ||||
| Oxygen Index | 30 % | 30 % | ISO 4589 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 20.0 - 50.0 °C | 68.0 - 122 °F | hopper | ||
| 65.0 - 93.0 °C | 149 - 199 °F | cavity | |||
| Feed Temperature | 230 - 240 °C | 446 - 464 °F | |||
| Zone 1 | 230 - 240 °C | 446 - 464 °F | |||
| Zone 2 | 235 - 250 °C | 455 - 482 °F | |||
| Zone 3 | 235 - 250 °C | 455 - 482 °F | |||
| Zone 4 | 240 - 260 °C | 464 - 500 °F | |||
| Die Temperature | 250 - 260 °C | 482 - 500 °F | |||
| Melt Temperature | 235 - 260 °C | 455 - 500 °F | |||
| 260 °C | 500 °F | ISO 294 | |||
| Mold Temperature | 80.0 °C | 176 °F | ISO 294 | ||
| Injection Velocity | 200 mm/sec | 7.87 in/sec | ISO 294 | ||
| Drying Temperature | 120 - 130 °C | 248 - 266 °F | |||
| Dry Time | 4 hour | 4 hour | |||
| Moisture Content | 0.020 % | 0.020 % | Necessary low maximum | ||
| Injection Pressure | 70.0 MPa | 10200 psi | ISO 294 | ||
| Hot-Working Temperature | 250 - 260 °C | 482 - 500 °F | |||
| Descriptive Properties | |||||
| Injection molding | Yes | ||||
| Injection speed | medium-fast | ||||
| Melt volume rate (MVR), cm³/10min | 9 | ||||
| MVR test load, kg | 2.16 | ||||
| MVR test temperature, °C | 250 | ||||
| Processing conditions acc. ISO | 7792 | ||||