- 密度 [g/cm3]: 1.45
- 缺口冲击强度: 4.5
- 弯曲模量 [MPa]: 5.90
- 热变形温度 [℃]: 219.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.45 g/cc | 0.0524 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.15 % | 0.15 % | 23°C/50%RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0060 cm/cm | 0.0040 - 0.0060 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0010 cm/cm | 0.0010 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 82.0 MPa | 11900 psi | 5mm/min; ISO 527-2/1A |
| Elongation at Break | 1.6 % | 1.6 % | 5mm/min; ISO 527-2/1A |
| Tensile Modulus | 6.30 GPa | 914 ksi | 1mm/min; ISO 527-2/1A |
| Flexural Strength | 140 MPa | 20300 psi | ISO 178 |
| Flexural Modulus | 5.90 GPa | 856 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 4.50 kJ/m² | 2.14 ft-lb/in² | ISO 180/1A |
| Charpy Impact Unnotched | 1.60 J/cm² | 7.61 ft-lb/in² | ISO 179/1eU |
| 1.60 J/cm² @Temperature 30.0 °C | 7.61 ft-lb/in² @Temperature 86.0 °F | ISO 179/1eU | |
| Charpy Impact, Notched | 0.400 J/cm² | 1.90 ft-lb/in² | ISO 179/1eA |
| 0.480 J/cm² @Temperature 30.0 °C | 2.28 ft-lb/in² @Temperature 86.0 °F | ISO 179/1eA | |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 6.00e+14 ohm-cm | 6.00e+14 ohm-cm | IEC 60093 |
| Surface Resistance | 2.00e+17 ohm | 2.00e+17 ohm | IEC 60093 |
| Dielectric Constant | 3.5 @Frequency 100 Hz | 3.5 @Frequency 100 Hz | IEC 60250 |
| 3.6 @Frequency 1.00e+6 Hz | 3.6 @Frequency 1.00e+6 Hz | IEC 60250 | |
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | IEC 60243-1 |
| Dissipation Factor | 0.019 @Frequency 1.00e+6 Hz | 0.019 @Frequency 1.00e+6 Hz | IEC 60250 |
| Comparative Tracking Index | 175 V | 175 V | IEC 60112 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 38.0 µm/m-°C | 21.1 µin/in-°F | ISO 11359-2 |
| CTE, linear, Transverse to Flow | 80.0 µm/m-°C | 44.4 µin/in-°F | ISO 11359-2 |
| Melting Point | 225 °C | 437 °F | ISO 11357-1,-2,-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 219 °C | 426 °F | ISO 75-1, -2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 182 °C | 360 °F | ISO 75-1, -2 |
| Glass Transition Temp, Tg | 49.0 °C | 120 °F | ISO 11357-1,-2,-3 |
| Flammability, UL94 | HB @Thickness 0.800 mm | HB @Thickness 0.0315 in | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 20.0 - 50.0 °C | 68.0 - 122 °F | hopper |
| 65.0 - 95.0 °C | 149 - 203 °F | cavity | |
| Feed Temperature | 235 - 250 °C | 455 - 482 °F | |
| Zone 1 | 235 - 250 °C | 455 - 482 °F | |
| Zone 2 | 240 - 255 °C | 464 - 491 °F | |
| Zone 3 | 240 - 255 °C | 464 - 491 °F | |
| Zone 4 | 245 - 260 °C | 473 - 500 °F | |
| Die Temperature | 250 - 265 °C | 482 - 509 °F | |
| Melt Temperature | 250 - 265 °C | 482 - 509 °F | |
| 280 °C | 536 °F | ISO 294 | |
| Mold Temperature | 80.0 °C | 176 °F | ISO 294 |
| Hot-Working Temperature | 250 - 260 °C | 482 - 500 °F | |