- 密度 [g/cm3]: 1.55
- 缺口冲击强度: 0.747
- 弯曲模量 [MPa]: 9.50
- 热变形温度 [℃]: 220.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.55 g/cc | 1.55 g/cc | ASTM D792 |
| Density | 1.55 g/cc | 0.0560 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.19 % | 0.19 % | 23°C/50%RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.00 - 0.0050 cm/cm | 0.00 - 0.0050 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0080 cm/cm | 0.0050 - 0.0080 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 91 | 91 | ISO 2039-2 |
| Tensile Strength at Break | 125 MPa | 18100 psi | 5mm/min; ISO 527-2/1A |
| 110 MPa @Temperature 22.8 °C | 16000 psi @Temperature 73.0 °F | ASTM D638 | |
| Elongation at Break | 2.2 % | 2.2 % | 5mm/min; ISO 527-2/1A |
| 3.0 % @Temperature 22.8 °C | 3.0 % @Temperature 73.0 °F | ASTM D638 | |
| Tensile Modulus | 9.70 GPa | 1410 ksi | 1mm/min; ISO 527-2/1A |
| Flexural Strength | 180 MPa | 26100 psi | ISO 178 |
| Flexural Modulus | 9.50 GPa | 1380 ksi | ISO 178 |
| 9.31 GPa @Temperature 22.8 °C | 1350 ksi @Temperature 73.0 °F | ASTM D790 | |
| Izod Impact, Notched | 0.747 J/cm @Temperature 22.8 °C | 1.40 ft-lb/in @Temperature 73.0 °F | ASTM D256 |
| Izod Impact, Notched (ISO) | 5.30 kJ/m² | 2.52 ft-lb/in² | ISO 180/1A |
| Charpy Impact Unnotched | 2.70 J/cm² | 12.8 ft-lb/in² | ISO 179/1eU |
| 2.40 J/cm² @Temperature 30.0 °C | 11.4 ft-lb/in² @Temperature 86.0 °F | ISO 179/1eU | |
| Charpy Impact, Notched | 0.670 J/cm² | 3.19 ft-lb/in² | ISO 179/1eA |
| 0.720 J/cm² @Temperature 30.0 °C | 3.43 ft-lb/in² @Temperature 86.0 °F | ISO 179/1eA | |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | IEC 60093 |
| 1.00e+17 ohm-cm | 1.00e+17 ohm-cm | ASTM D257 | |
| Surface Resistance | 6.00e+16 ohm | 6.00e+16 ohm | IEC 60093 |
| Dielectric Constant | 3.1 @Frequency 1.00e+6 Hz | 3.1 @Frequency 1.00e+6 Hz | IEC 60250 |
| 3.3 @Frequency 100 Hz | 3.3 @Frequency 100 Hz | IEC 60250 | |
| Dielectric Strength | 23.6 kV/mm | 600 kV/in | short term; ASTM D149 |
| 31.0 kV/mm | 787 kV/in | IEC 60243-1 | |
| Dissipation Factor | 0.012 @Frequency 1.00e+6 Hz | 0.012 @Frequency 1.00e+6 Hz | IEC 60250 |
| Comparative Tracking Index | 325 V | 325 V | IEC 60112 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 28.0 µm/m-°C | 15.6 µin/in-°F | ISO 11359-2 |
| CTE, linear, Transverse to Flow | 85.0 µm/m-°C | 47.2 µin/in-°F | ISO 11359-2 |
| Melting Point | 225 °C | 437 °F | ISO 11357-1,-2,-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ASTM D648 |
| 223 °C | 433 °F | ISO 75-1, -2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 202 °C | 396 °F | ISO 75-1, -2 |
| 204 °C | 400 °F | ASTM D648 | |
| Glass Transition Temp, Tg | 54.0 °C | 129 °F | ISO 11357-1,-2,-3 |