- 密度 [g/cm3]: 1.31
- 缺口冲击强度: 8.8
- 拉伸强度 [MPa]: 41.0
- 弯曲模量 [MPa]: 1.123
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.31 g/cc | 0.0473 lb/in³ | ISO 1183 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 32.0 MPa | 4640 psi | 50mm/min; ISO 527-2/1A |
| Tensile Strength, Yield | 41.0 MPa | 5950 psi | 50mm/min; ISO 527-2/1A |
| Elongation at Break | 50 % | 50 % | 50mm/min; ISO 527-2/1A |
| Elongation at Yield | 16.8 % | 16.8 % | 50mm/min; ISO 527-2/1A |
| Tensile Modulus | 1.257 GPa | 182.3 ksi | 1mm/min; ISO 527-2/1A |
| Flexural Modulus | 1.123 GPa | 162.9 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 8.80 kJ/m² | 4.19 ft-lb/in² | ISO 180/1A |
| Izod Impact, Unnotched (ISO) | NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | ISO 180/1U |