- 密度 [g/cm3]: 1.55
- 缺口冲击强度: 0.801
- 弯曲模量 [MPa]: 9.10
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.55 g/cc | 0.0560 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 109 MPa | 15800 psi | 5mm/min; ISO 527-2/1A |
| 110 MPa @Temperature 22.8 °C | 16000 psi @Temperature 73.0 °F | ASTM D638 | |
| Elongation at Break | 1.8 % | 1.8 % | 5mm/min; ISO 527-2/1A |
| 5.0 % @Temperature 22.8 °C | 5.0 % @Temperature 73.0 °F | ASTM D638 | |
| Flexural Strength | 168 MPa | 24400 psi | ISO 178 |
| 172 MPa @Temperature 22.8 °C | 25000 psi @Temperature 73.0 °F | ASTM D790 | |
| Flexural Modulus | 9.10 GPa | 1320 ksi | ISO 178 |
| Izod Impact, Notched | 0.801 J/cm @Temperature 22.8 °C | 1.50 ft-lb/in @Temperature 73.0 °F | ASTM D256 |
| Izod Impact, Notched (ISO) | 5.10 kJ/m² | 2.43 ft-lb/in² | ISO 180/1A |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 2.00e+15 ohm-cm | 2.00e+15 ohm-cm | ASTM D257 |
| Dielectric Strength | 23.6 kV/mm | 600 kV/in | short term; ASTM D149 |
| Arc Resistance | 124 sec | 124 sec | ASTM D495 |
| Thermal Properties | Metric | English | Comments |
| Flammability, UL94 | HB | HB | |