- 密度 [g/cm3]: 1.44
- 缺口冲击强度: 4.5
- 拉伸强度 [MPa]: 64.0
- 弯曲模量 [MPa]: 3.00
- 热变形温度 [℃]: 134.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.44 g/cc | 0.0520 lb/in³ | ISO 1183 & ASTM D792 |
| Linear Mold Shrinkage | 0.023 - 0.025 cm/cm | 0.023 - 0.025 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 79 | 79 | ISO 2039-2 |
| Tensile Strength, Yield | 64.0 MPa | 9280 psi | 50 mm/min; ISO 527-2/1A |
| Elongation at Break | 12 % | 12 % | 50 mm/min; ISO 527-2/1A |
| Elongation at Yield | 7.0 % | 7.0 % | 50 mm/min; ISO 527-2/1A |
| Tensile Modulus | 3.00 GPa | 435 ksi | 1 mm/min; ISO 527-2/1A |
| Flexural Strength | 90.0 MPa | 13100 psi | ISO 178 |
| Flexural Modulus | 3.00 GPa | 435 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 4.50 kJ/m² | 2.14 ft-lb/in² | ISO 180/1A |
| Charpy Impact, Notched | 0.400 J/cm² | 1.90 ft-lb/in² | ISO 179/1eA |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | >= 1.00e+16 ohm-cm | >= 1.00e+16 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+17 ohm | >= 1.00e+17 ohm | IEC 60093 |
| Dielectric Constant | 3.5 @Frequency 1e+6 Hz | 3.5 @Frequency 1e+6 Hz | IEC 60250 |
| 3.6 @Frequency 100 Hz | 3.6 @Frequency 100 Hz | IEC 60250 | |
| Dielectric Strength | 37.0 kV/mm | 940 kV/in | IEC 60243-1 |
| Dissipation Factor | 0.0047 @Frequency 100 Hz | 0.0047 @Frequency 100 Hz | IEC 60250 |
| 0.0185 @Frequency 1e+6 Hz | 0.0185 @Frequency 1e+6 Hz | IEC 60250 | |
| Comparative Tracking Index | 325 V | 325 V | IEC 60112 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 139 µm/m-°C @Temperature 20.0 °C | 77.2 µin/in-°F @Temperature 68.0 °F | ISO 11359-2 |
| Melting Point | 225 °C | 437 °F | ISO 11357-1,2,3 & ASTM D3418 |
| Deflection Temperature at 0.46 MPa (66 psi) | 134 °C | 273 °F | ISO 75-1, -2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 66.0 °C | 151 °F | ISO 75-1, -2 |
| Flammability, UL94 | V-0 @Thickness 0.800 mm | V-0 @Thickness 0.0315 in | |
| Processing Properties | Metric | English | Comments |
| Rear Barrel Temperature | 230 - 240 °C | 446 - 464 °F | |
| Middle Barrel Temperature | 235 - 250 °C | 455 - 482 °F | |
| Front Barrel Temperature | 240 - 255 °C | 464 - 491 °F | |
| Nozzle Temperature | 250 - 255 °C | 482 - 491 °F | |
| Melt Temperature | 235 - 255 °C | 455 - 491 °F | |
| Mold Temperature | 65.0 - 93.0 °C | 149 - 199 °F | |
| Drying Temperature | 121 °C | 250 °F | |
| Dry Time | 4 hour | 4 hour | |
| Back Pressure | 0.000 - 0.345 MPa | 0.000 - 50.0 psi | |