- 熔体流动速率 [g/10min]: 25.0
- 缺口冲击强度: 0.392
- 弯曲强度 [MPa]: 60.8
- 弯曲模量 [MPa]: 2.75
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.30 g/cc @Temperature 23.0 °C | 1.30 g/cc @Temperature 73.4 °F | ASTM D792 |
| Filler Content | 0.00 % | 0.00 % | |
| Linear Mold Shrinkage | 0.011 - 0.018 cm/cm | 0.011 - 0.018 in/in | ASTM D955 |
| Melt Flow | 25 g/10 min @Load 2.16 kg, Temperature 250 °C | 25 g/10 min @Load 4.76 lb, Temperature 482 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 60.8 MPa | 8820 psi | 5mm/min; ASTM D638 |
| Elongation at Break | 20 % | 20 % | 5mm/min; ASTM D638 |
| Flexural Strength | 98.1 MPa | 14200 psi | 2.8mm/min; ASTM D790 |
| Flexural Modulus | 2.75 GPa | 398 ksi | 2.8mm/min; ASTM D790 |
| Izod Impact, Notched | 0.392 J/cm @Thickness 3.17 mm, Temperature 23.0 °C | 0.735 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 80.0 °C | 176 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 1.50 mm | V-0 @Thickness 0.0591 in | |
| Processing Properties | Metric | English | Comments |
| Middle Barrel Temperature | 225 - 245 °C | 437 - 473 °F | Cylinder Temperature |
| Mold Temperature | 40.0 - 80.0 °C | 104 - 176 °F | |
| Drying Temperature | 100 - 120 °C | 212 - 248 °F | |
| Dry Time | 3 - 5 hour | 3 - 5 hour | |