- 熔体流动速率 [g/10min]: 11.72
- 密度 [g/cm3]: 1.31
- 吸水率 [%]: 0.45
- 拉伸强度 [MPa]: 55.0
- 热变形温度 [℃]: 150.0
Physical Properties | Metric | English | Comments | ||
---|---|---|---|---|---|
Density | 1.31 g/cc | 0.0473 lb/in³ | ISO 1183 | ||
Water Absorption at Saturation | 0.45 % | 0.45 % | ISO 62 | ||
Linear Mold Shrinkage | 0.017 cm/cm | 0.017 in/in | Pigmentation can change mold shrinkage. | ||
Linear Mold Shrinkage, Transverse | 0.017 cm/cm | 0.017 in/in | Pigmentation can change mold shrinkage. | ||
Melt Flow | 11.72 g/10 min @Load 2.16 kg, Temperature 250 °C | 11.72 g/10 min @Load 4.76 lb, Temperature 482 °F | ISO 1133 | ||
Mechanical Properties | Metric | English | Comments | ||
Hardness, Shore D | 77 | 77 | ISO 868 | ||
Ball Indentation Hardness | 150 MPa | 21800 psi | H30; ISO 2039-1 | ||
Tensile Strength, Yield | 55.0 MPa | 7980 psi | 50 mm/min; ISO 527-1/2 | ||
Elongation at Break | >= 50 % | >= 50 % | 50 mm/min; ISO 527-1/2 | ||
Elongation at Yield | 9.0 % | 9.0 % | 50 mm/min; ISO 527-1/2 | ||
Tensile Modulus | 2.60 GPa | 377 ksi | ISO 527-1/2 | ||
Charpy Impact Unnotched | 30.0 J/cm² @Temperature -30.0 °C | 143 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eU | ||
NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | ISO 179/1eU | |||
Charpy Impact, Notched | 0.600 J/cm² @Temperature -30.0 °C | 2.86 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eA | ||
0.700 J/cm² @Temperature 23.0 °C | 3.33 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | |||
Electrical Properties | Metric | English | Comments | ||
Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 | ||
Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 60093 | ||
Dielectric Constant | 3.3 @Frequency 100 Hz | 3.3 @Frequency 100 Hz | IEC 60250 | ||
3.5 @Frequency 1e+6 Hz | 3.5 @Frequency 1e+6 Hz | IEC 60250 | |||
Dielectric Strength | 27.0 kV/mm | 686 kV/in | K20/P50; IEC 60243-1 | ||
Dissipation Factor | 0.0020 @Frequency 100 Hz | 0.0020 @Frequency 100 Hz | IEC 60250 | ||
0.023 @Frequency 1e+6 Hz | 0.023 @Frequency 1e+6 Hz | IEC 60250 | |||
Comparative Tracking Index | 575 V | 575 V | Test Solution A, 100 drops; IEC 60112 | ||
600 V | 600 V | Test Solution A, CTI; IEC 60112 | |||
Thermal Properties | Metric | English | Comments | ||
CTE, linear | 110 µm/m-°C @Temperature 23.0 - 55.0 °C | 61.1 µin/in-°F @Temperature 73.4 - 131 °F | Longitudinal; ISO 11359 | ||
CTE, linear, Transverse to Flow | 110 µm/m-°C @Temperature 23.0 - 55.0 °C | 61.1 µin/in-°F @Temperature 73.4 - 131 °F | ISO 11359 | ||
Melting Point | 221 - 226 °C | 430 - 439 °F | DSC | ||
Deflection Temperature at 0.46 MPa (66 psi) | 150 °C | 302 °F | ISO 75-1/2 | ||
Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | ISO 75-1/2 | ||
Vicat Softening Point | 180 °C | 356 °F | 50N; ISO 306 | ||
220 °C | 428 °F | 10N; ISO 306 | |||
Flammability, UL94 | HB @Thickness 0.800 mm | HB @Thickness 0.0315 in | |||
HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | ||||
Oxygen Index | 23 % | 23 % | ISO 4589 | ||
Glow Wire Test | 850 °C @Thickness 2.00 mm | 1560 °F @Thickness 0.0787 in | IEC 60695-2-1/0-3 | ||
Descriptive Properties | |||||
Electrolytic Corrosion | A1 Step | IEC 60426 |